Citation: Bingyu Huang, Jipeng Fu, Tianyi Sun, Yuqi Li, Jinru Liu, Kaina Wang, Qian Xu, Wengui Yu, Hongqi Chen, Huajie Luo, Mathieu Allix, Mingxue Tang, Shiqing Xu. Nanothermometry and luminescence modulation via separated activators in core-shell-shell fluoride nanoparticles[J]. Chinese Chemical Letters, ;2026, 37(7): 111159. doi: 10.1016/j.cclet.2025.111159 shu

Nanothermometry and luminescence modulation via separated activators in core-shell-shell fluoride nanoparticles

Bingyu Huang ^a ,
Jipeng Fu ^{a, *,} ,
Tianyi Sun ^b ,
Yuqi Li ^b ,
Jinru Liu ^a ,
Kaina Wang ^b ,
Qian Xu ^a ,
Wengui Yu ^a ,
Hongqi Chen ^a ,
Huajie Luo ^b ,
Mathieu Allix ^c ,
Mingxue Tang ^{b, *,} ,
Shiqing Xu ^{a, *,}

a.
College of Optical and Electronic Technology, China Jiliang University, Hangzhou 310018, China
b.
School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China
c.
CNRS, CEMHTI UPR3079, Univ. Orléans, Orléans F-45071, France

fujipeng@cjlu.edu.cn

mingxue.tang@hpstar.ac.cn

shiqingxu@cjlu.edu.cn

Received Date: 19 January 2025
Revised Date: 19 March 2025
Accepted Date: 27 March 2025
Available Online: 27 March 2025

Figures(4)

Upconversion nanoparticles (UCNPs) have been naturally entangled with surface phonons since their discovery due to their high specific surface area. However, in addition to quenching luminescence at ambient temperatures, surface phonons play a crucial role in activating the dark layer between the sensitizer and the activator to enhance luminescence in thermal environments. Considering that the positive effect of surface phonons may be eliminated under inert cladding, a β-NaGdF₄:Yb,Tm@NaYF₄@NaGdF₄:Yb,Er core-shell-shell upconversion luminescence (UCL) system with two opposite thermo-responsive luminescence behaviors is designed here. The imposition of an inert intermediate shell layer causes the weakening of the blue luminescence of the core Tm ions in the thermal environment, while on the contrary the outermost Er ions realize an effective enhancement of luminescence with the help of surface phonons. In addition, the photoluminescence results show that effective modulation of luminescence color can be achieved by changing the thickness of the inert shell layer, the concentration of Er ions in the activation layer, and the excitation power. Finally, the distinct thermally responsive luminescence behaviors and temperature-dependent color variations enabled moderate temperature sensing and information encryption applications. The maximum relative and absolute sensitivities can be up to 1.62%/K and 0.64%/K from 298 K to 573 K, respectively. These findings provided new insights into optimizing the luminescent properties of fluorides and provided a new platform for the application of multiple properties in a material.
- Core/shell/shell upconversion nanoparticles,
- Surface phonons,
- Inert cladding,
- Nanothermometry,
- Luminescence modulation
1. [1]
  S.K. Ling, Y.X. Wang, X.Y. Qin, et al., Inorg. Chem. 63 (2024) 6660–6673. doi: 10.1021/acs.inorgchem.3c04524
2. [2]
  J.S. Liao, M.H. Wang, F.L. Lin, et al., Nat. Commun. 13 (2022) 2090. doi: 10.1038/s41467-022-29784-6
3. [3]
  B.Z. Zheng, D.N. Zhong, T.T. Xie, et al., Chem 7 (2021) 1615–1625. doi: 10.1016/j.chempr.2021.03.008
4. [4]
  K.N. Wang, J.P. Fu, H.L. Dong, et al., Small Struct. 5 (2024) 2400092. doi: 10.1002/sstr.202400092
5. [5]
  D. Li, M.C. Jia, T. Jia, G.Y. Chen, Adv. Mater. 36 (2024) 2309452. doi: 10.1002/adma.202309452
6. [6]
  Y. Hong, Y.Q. Jiang, C.H. Yuan, et al., Chin. Chem. Lett. 35 (2024) 109909. doi: 10.1016/j.cclet.2024.109909
7. [7]
  Z.Q. Ge, Z.X. Pan, Yan S, et al., Chin. Chem. Lett. 35 (2024) 109850. doi: 10.1016/j.cclet.2024.109850
8. [8]
  J.J. Zhou, B.D. Rosal, D. Jaque, S. Uchiyama, D.Y. Jin, Nat. Methods 17 (2020) 967–980. doi: 10.1038/s41592-020-0957-y
9. [9]
  S.Y. Han, R.R. Deng, Q.F. Gu, et al., Nature 587 (2020) 594–599. doi: 10.1038/s41586-020-2932-2
10. [10]
  K. Malhotra, D. Hrovat, B. Kumar, et al., ACS Appl. Mater. Interfaces 15 (2023) 2499–2528. doi: 10.1021/acsami.2c12370
11. [11]
  Y.L. Chang, H.R. Chen, X.Y. Xie, et al., Nat. Commun. 14 (2023) 1079. doi: 10.1038/s41467-023-36813-5
12. [12]
  J.P. Fu, R. Pang, L.H. Jiang, et al., Dalton Trans. 45 (2016) 13317–13323. doi: 10.1039/C6DT01552B
13. [13]
  C.D.S. Brites, R. Marin, M. Suta, et al., Adv. Mater. 35 (2023) 2302749. doi: 10.1002/adma.202302749
14. [14]
  M. Yang, H.J. Gong, D. Yang, et al., Chin. Chem. Lett. 35 (2024) 108468. doi: 10.1016/j.cclet.2023.108468
15. [15]
  Q.Q. Li, X.Y. Xie, H. Wu, et al., Nano Lett. 23 (2023) 3444–3450. doi: 10.1021/acs.nanolett.3c00495
16. [16]
  K. Trejgis, K. Ledwa, K. Maciejewska, L. Li, L. Marciniak, Sci. Rep. 12 (2022) 5847.
17. [17]
  Y. Xue, Y.Q. Chen, G.X. Li, et al., Chin. Chem. Lett. 35 (2024) 108447.
18. [18]
  M. Liu, J.Y. Liang, F. Vetrone, Acc. Chem. Res. 57 (2024) 2653–2664. doi: 10.1021/acs.accounts.4c00342
19. [19]
  X. Qu, P.Z. Wu, K.X. Duan, et al., Chin. Chem. Lett. 35 (2024) 109681. doi: 10.1016/j.cclet.2024.109681
20. [20]
  Y.B. Wang, L. Lei, G.Ye R, et al., ACS Appl. Mater. Interfaces 13 (2021) 23951–23959. doi: 10.1021/acsami.1c05611
21. [21]
  C. Mi, J.J. Zhou, F. Wang, G.G. Lin, D.Y. Jin, Chem. Mater. 31 (2019) 9480–9487. doi: 10.1021/acs.chemmater.9b03466
22. [22]
  S.Y. Han, Z.G. Yi, J.B. Zhang, et al., Nat. Commun. 12 (2021) 3704. doi: 10.1038/s41467-021-23967-3
23. [23]
  H. Xu, S.Y. Han, R.R. Deng, et al., Nat. Photon. 15 (2021) 732–737. doi: 10.1038/s41566-021-00862-3
24. [24]
  B.Z. Zheng, J.Y. Fan, B. Chen, et al., Chem. Rev. 122 (2022) 5519–5603. doi: 10.1021/acs.chemrev.1c00644
25. [25]
  S.Q. Chang, J.P. Fu, X. Sun, et al., Inorg. Chem. 61 (2022) 3746–3753. doi: 10.1021/acs.inorgchem.1c04016
26. [26]
  F. Li, L.P. Tu, Y.Q. Zhang, et al., Nat. Photonics 18 (2024) 440–449. doi: 10.1038/s41566-024-01393-3
27. [27]
  K.N. Wang, J.P. Fu, S.B. Zhan, et al., Chem 11 (2025) 102325. doi: 10.1016/j.chempr.2024.09.024
28. [28]
  K.N. Wang, J.P. Fu, S.Q. Chang, et al., Adv. Powder Mater. 2 (2023) 100112.
29. [29]
  Y.H. Wang, Z.C. An, Z.R. Tao, et al., J. Phys. Chem. Lett. 13 (2022) 12032–12040. doi: 10.1021/acs.jpclett.2c03449
30. [30]
  Y.L. Wang, J.H. Rui, H. Song, et al., J. Am. Chem. Soc. 146 (2024) 6530–6535. doi: 10.1021/jacs.3c10886
31. [31]
  H.M. Liu, L. Yan, J.S. Huang, et al., J. Phys. Chem. Lett. 13 (2022) 2306–2312. doi: 10.1021/acs.jpclett.2c00005
32. [32]
  L. Marciniak, W. Piotrowski, M. Szalkowski, et al., Chem. Eng. J. 427 (2022) 131941. doi: 10.1016/j.cej.2021.131941
33. [33]
  X.F. Wu, S.P. Zhan, J.B. Han, Y.X. Liu, Nano Lett. 21 (2021) 272–278.
34. [34]
  W.Q. Cao, Z.L. Liao, H.X. Chen, et al., ACS Appl. Mater. Interfaces 16 (2024) 58920–58930. doi: 10.1021/acsami.4c15171
35. [35]
  Z.H. Chen, Y.K. Cun, S.L. Yan, et al., Sci. China Mater. 66 (2023) 4742–4748. doi: 10.1007/s40843-023-2647-1
36. [36]
  Y.Z. Zi, Z.W. Yang, Z. Xu, et al., J. Alloys Compd. 880 (2021) 160156.
37. [37]
  E.D. Martínez, C.D.S. Brites, L.D. Carlos, et al., Adv. Funct. Mater. 29 (2019) 1807758.
38. [38]
  J.J. Zhou, S.H. Wen, J.Y. Liao, et al., Nat. Photonics 12 (2018) 154–158. doi: 10.1038/s41566-018-0108-5
39. [39]
  J.S. Huang, L. Yan, C.An Z, et al., Adv. Mater. 36 (2024) 2310524.
40. [40]
  X. Sun, W. Dong, C.J. Lou, et al., J. Solid State Chem. 316 (2022) 123640.
41. [41]
  Z.C. An, Q.Q. Li, J.S. Huang, L.L. Tao, B. Zhou, Nano Lett. 23 (2023) 6241–6248. doi: 10.1021/acs.nanolett.3c00747
42. [42]
  H.H. Fu, C.H. Hu, J. Liu, et al., CrystEngComm 24 (2022) 7698–7717. doi: 10.1039/d2ce01206e
43. [43]
  J.Y. Chen, L.L. Liang, S.D. Tan, et al., Nano Lett. 23 (2023) 7221–7227. doi: 10.1021/acs.nanolett.3c01621
44. [44]
  R. Shi, C.D.S. Brites, L.D. Carlos, Small Struct. 3 (2022) 2100194.
45. [45]
  Y. Wang, J.X. Low, Y.F. Bi, et al., Chin. Chem. Lett. 33 (2022) 1087–1090.
46. [46]
  H.Y. Xu, M.C. Jia, Z.Y. Wang, Y.L. Wei, Z. L. Fu, ACS Appl. Mater. Interfaces 13 (2021) 61506–61517. doi: 10.1021/acsami.1c17900
47. [47]
  L. Yan, J.S. Huang, Z.C. An, Q.Y. Zhang, B. Zhou, Nano Lett. 22 (2022) 7042–7048. doi: 10.1021/acs.nanolett.2c01931
48. [48]
  Q.L. Zou, C. Marcelot, N. Ratel-Ramond, et al., ACS Nano 16 (2022) 12107–12117. doi: 10.1021/acsnano.2c02423
49. [49]
  Y. Zhang, P.P. Lei, X.H. Zhu, Y. Zhang, Nat. Commun. 12 (2021) 6178.
50. [50]
  Y.H. Wei, S. Yang, K.H. Zhu, et al., Laser Photon. Rev. 18 (2024) 2400612.
51. [51]
  J.W. Jin, J. Lin, Y.P. Huang, et al., Chin. Chem. Lett. 33 (2022) 4798–4802.
1. [1]
  Linke Zhang , Tao Pang , Lingwei Zeng , Feng Huang , Daqin Chen . Recent progress of fluoride core-shell nanocrystals: Manipulating the non-steady-state of upconversion luminescence. Chinese Journal of Structural Chemistry, 2025, 44(11): 100713-100713. doi: 10.1016/j.cjsc.2025.100713
2. [2]
  Min Song , Qian Zhang , Tao Shen , Guanyu Luo , Deli Wang . Surface reconstruction enabled o-PdTe@Pd core-shell electrocatalyst for efficient oxygen reduction reaction. Chinese Chemical Letters, 2024, 35(8): 109083-. doi: 10.1016/j.cclet.2023.109083
3. [3]
  Shaonan Tian , Yu Zhang , Qing Zeng , Junyu Zhong , Hui Liu , Lin Xu , Jun Yang . Core-shell gold-copper nanoparticles: Evolution of copper shells on gold cores at different gold/copper precursor ratios. Chinese Journal of Structural Chemistry, 2023, 42(11): 100160-100160. doi: 10.1016/j.cjsc.2023.100160
4. [4]
  Guoliang Liu , Zhiqiang Liu , Anmin Zheng . Modulation of zeolite surface realizes dynamic copper species redispersion. Chinese Journal of Structural Chemistry, 2024, 43(6): 100308-100308. doi: 10.1016/j.cjsc.2024.100308
5. [5]
  Tao He , Chunxue Wang , Yifei Liang , Tingjie Fu , Kunlin Li , Xin Sun , Kai Li , Ping Ning , Fei Wang . Research progress of core-shell catalysts in the deNO_x field. Chinese Chemical Letters, 2026, 37(6): 112113-. doi: 10.1016/j.cclet.2025.112113
6. [6]
  Hengying Xiang , Nanping Deng , Lu Gao , Wen Yu , Bowen Cheng , Weimin Kang . 3D core-shell nanofibers framework and functional ceramic nanoparticles synergistically reinforced composite polymer electrolytes for high-performance all-solid-state lithium metal battery. Chinese Chemical Letters, 2024, 35(8): 109182-. doi: 10.1016/j.cclet.2023.109182
7. [7]
  Lei Zhang , Kaimin Chen , Luchang Li , Xiu Wei , Xianxin Cai , Yaohui Yu , Yixian Yang , Renping Cao , Fenghua Wei , Bang Lan , Yanhua Li , Xiaohu Luo , Hui Liang , Deshuai Zhen . One-pot synthesis of Ni–Co nanoparticles@Ni_0.19Co_0.26P nanowires core/shell arrays on Ni foam for efficient hydrogen evolution reaction at all pH values. Chinese Chemical Letters, 2026, 37(6): 111002-. doi: 10.1016/j.cclet.2025.111002
8. [8]
  Guo-Hong Gao , Run-Ze Zhao , Ya-Jun Wang , Xiao Ma , Yan Li , Jian Zhang , Ji-Sen Li . Core–shell heterostructure engineering of CoP nanowires coupled NiFe LDH nanosheets for highly efficient water/seawater oxidation. Chinese Chemical Letters, 2024, 35(8): 109181-. doi: 10.1016/j.cclet.2023.109181
9. [9]
  Shudi Yu , Jie Li , Jiongting Yin , Wanyu Liang , Yangping Zhang , Tianpeng Liu , Mengyun Hu , Yong Wang , Zhengying Wu , Yuefan Zhang , Yukou Du . Built-in electric field and core-shell structure of the reconstructed sulfide heterojunction accelerated water splitting. Chinese Chemical Letters, 2024, 35(12): 110068-. doi: 10.1016/j.cclet.2024.110068
10. [10]
  Yaoyin Lou , Xiaoyang Jerry Huang , Kuang-Min Zhao , Mark J. Douthwaite , Tingting Fan , Fa Lu , Ouardia Akdim , Na Tian , Shigang Sun , Graham J. Hutchings . Stable core-shell Janus BiAg bimetallic catalyst for CO₂ electrolysis into formate. Chinese Chemical Letters, 2025, 36(3): 110300-. doi: 10.1016/j.cclet.2024.110300
11. [11]
  Yangping Zhang , Tianpeng Liu , Jun Yu , Zhengying Wu , Dongqiong Wang , Yukou Du . Amorphous/crystalline AgS@CoS core@shell catalysts for efficient oxygen evolution reaction. Chinese Chemical Letters, 2025, 36(8): 110275-. doi: 10.1016/j.cclet.2024.110275
12. [12]
  Jiarong Li , Shude Liu , Yuanzhao Xie , Yue Sun , Zhuyu Liu , Meihua Chen , Yaobang Li , Yonghui Deng . Nanoemulsion-assisted assembly and polymerization towards core-shell magnetic mesoporous melamine-formaldehyde resin microspheres. Chinese Chemical Letters, 2026, 37(4): 111433-. doi: 10.1016/j.cclet.2025.111433
13. [13]
  Canghai Luo , Chao Wu , Baoling Guo , Yuan Zheng , Ze Yang , Xiaoying Ji , Jianpeng Sheng , Jian Ruan , Peng Zhao , Dongliang Li , Dong Chen . Controlled encapsulation of solid particles in core-shell capsules by millifluidics and assisted by vibrations. Chinese Chemical Letters, 2026, 37(7): 111749-. doi: 10.1016/j.cclet.2025.111749
14. [14]
  Jianning Zhang , Yihuai Zhang , Guoxin Ma , Jingchen Zhao , Tao Zhang , Jian Liu . Enhancing hydrothermal stability in Cu/SSZ-13 catalyst for diesel SCR applications through a novel core-shell structure. Chinese Chemical Letters, 2025, 36(7): 110516-. doi: 10.1016/j.cclet.2024.110516
15. [15]
  Min Jie Wang , Jiao Yang , Lishan Peng , Yongjie Bai , Zehui Liu , Xiaoliang Yang , Huijuan Lu , Bingjie Zhou , Ningtao Jiang , Guoxu He , Han-Ming Zhang , Liwei Mi , Yonghui Deng . Optimizing the size and electronic effects of core-shell heterostructures via well-constructed Ru clusters encapsulated in N-doped carbon layers. Chinese Chemical Letters, 2025, 36(12): 110573-. doi: 10.1016/j.cclet.2024.110573
16. [16]
  Yuqing Zhang , Xiao Song , Yongsheng Liu , Maochun Hong . Innovative optothermal-stimulated persistent luminescence nanoparticles for advanced tumor theranostics. Chinese Journal of Structural Chemistry, 2025, 44(7): 100624-100624. doi: 10.1016/j.cjsc.2025.100624
17. [17]
  Yuan Zhang , Shenghao Gong , A.R. Mahammed Shaheer , Rong Cao , Tianfu Liu . Plasmon-enhanced photocatalytic oxidative coupling of amines in the air using a delicate Ag nanowire@NH₂-UiO-66 core-shell nanostructures. Chinese Chemical Letters, 2024, 35(4): 108587-. doi: 10.1016/j.cclet.2023.108587
18. [18]
  Cuiping Lin , Chenchen Wang , Shaoqi Li , Qi Shen , Xiaodong Yang , Zengsheng Guo , Haiming Feng , Cuncheng Li , Yiqing Sun , Lifeng Hang . Pd@PtNiCoRuIr core-shell high-entropy alloys mesoporous nanospheres for temporally decoupled ammonia splitting by a Zn-NH₃ battery. Chinese Chemical Letters, 2026, 37(1): 111826-. doi: 10.1016/j.cclet.2025.111826
19. [19]
  Jun Yu , Yangping Zhang , Nannan Zhang , Jie Li , Huiyu Sun , Xinyu Gu , Changqing Ye , Tianpeng Liu , Yukou Du . The interface engineering strategy assists the 3D core-shell structure Co₃S₄/CuS@NiFe LDH nanocoral spheres to achieve significant overall water splitting. Chinese Chemical Letters, 2026, 37(2): 110830-. doi: 10.1016/j.cclet.2025.110830
20. [20]
  Ting Wang , Xin Yu , Yaqiang Xie . Unlocking stability: Preserving activity of biomimetic catalysts with covalent organic framework cladding. Chinese Chemical Letters, 2024, 35(6): 109320-. doi: 10.1016/j.cclet.2023.109320

Get Citation

PDF

XML

Metrics

PDF Downloads(0)
Abstract views(13)
HTML views(0)

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142