Two-dimensional mesoporous sensing materials

Yu Wen Facai Wei Wenqian Zhang Anyang Cui Jing Cui Chengbin Jing Zhigao Hu Qingguo He Jianwei Fu Shaohua Liu Jiangong Cheng

Citation:  Wen Yu, Wei Facai, Zhang Wenqian, Cui Anyang, Cui Jing, Jing Chengbin, Hu Zhigao, He Qingguo, Fu Jianwei, Liu Shaohua, Cheng Jiangong. Two-dimensional mesoporous sensing materials[J]. Chinese Chemical Letters, 2020, 31(2): 521-524. doi: 10.1016/j.cclet.2019.04.071 shu

Two-dimensional mesoporous sensing materials

English

  • Owing to the unique two-dimensional (2D) morphology, ultrathin thickness and high surface area, 2D materials have been intensively researched in recent years, which present the tremendous potential for diverse applications, such as chemical gas sensors, energy storage, electronic devices, electrocatalysts [1-8]. Besides, 2D materials can provide multiple active sites, high flexibility and good processability, which are particularly important for construction of high-performance gas sensors [9]. For example, graphene has been exploited as sensor to detect single NO2 gas molecule at room temperature, exhibiting an ultrahigh sensitivity [10]. Addtionally, the working temperature of gas sensors can even decrease to room temperature for the participation of some 2D materials, which greatly facilitated their practical application [11-13].

    Mesoporous materials with uniform pore size (2–50 nm), high surface area, large pore volume and modifiable surface, have been widely employed as supports for catalysis, separation, selective adsorption, even as hosts to include guest molecules over the past few years. Creating abundant mesopores along in-plane direction in nanosheets, can provide for 2D materials with higher surface area and additional active sites, thereby rendering them with enhanced electrochemical storage capacity, catalytic activity and filtration capability [14-26]. For the most of gas sensors, the sensing mechanisms are depended on the interaction of gas molecules with the surface of solid materials, therefore, it is highly desired to develop 2D mesoporous materials for gas sensing with defined porous structure, large surface area and well-defined surface properties [27-32]. However, up to now, exploring 2D mesoporous materials for gas sensor still remains unresolved, maybe due to the lack of suitable materials [33].

    Here, we synthesized 2D mesoporous polypyrrole (2D mPPy) nanosheets with hierarchical nanopores (mesopores of about 18 nm and micropores of about 1 nm) via a soft-template directing co-assembly route. The resultant materials featured uniform pore size, ultrathin thickness and high surface area. Serving as electrochemical sensor, the 2D mPPy nanosheets exhibited a fast response and high sensitivity for ammonia gas (NH3). As known, NH3 is widely used in manufacturing and agricultural production, but, as a highly toxic gas, it can irritate the skin, eyes and respiratory tract, and cause lung disease by reacting with the other air pollutants (nitrogen or sulfur) to form particles smaller than 2.5 μm (PM2.5) [34, 35]. Therefore, it was expected that 2D mPPy would offer a new choice for the high-performance NH3 sensor.

    The previous study demonstrated that amphiphilic surfactants of perfluorinated carboxylic acid (PFCA) can self-assemble into bilayerstructured micelles in a mixed solvent of EtOH/H2O, which can serve as an exquisite whilst robust platform for the guest moieties to be self-assembled on both of their surfaces [36]. Compared with the common surfactants (such as aliphatic amine, etc.), PFCA possesses smaller surface energy and could form more stable assembling structures. In addition, the abundant carboxyl functional groups of PFCA bilayers would be more favorable to guide the polymerization of pyrrole monomers, because of the electrostatic interaction between carboxyl groups of PFCA and imino groups of pyrroles [36, 37]. On the other hand, PS-b-PEO block co-polymer (BCP) can self-assemble into spherical micelles in a mixed solvent of THF/H2O at room temperature, rearranging into close-packed monolayers around the surfaces of PFCA bilayer throughH-bondingbetween the PEO chains and PFCA. Subsequently, after adding pyrrolemonomers and ammonium persulfate (APS), the above hierarchical supermolecule assemblies of BCP@PFCA can guide the polymerization of pyrrole monomers under triggering of APS. Upon the complete removal of the BCP and PFCA templates, the 2D mPPy nanosheets were obtained. The abovemechanism is similar to the growth of PPy directed by aliphatic amine, but here an improved method was adopted, and the detailed experimental procedure can be seen from Supporting information.

    We performed a serial of characterizations to testify the synthesized 2D mPPy nanosheets. As seen from the Fouriertransform infrared (FT-IR) spectra (Fig. S1 in Supporting information), the obtained 2D mPPy nanosheets showed the typical symmetric stretching vibration of the pyrrole rings at 1541 cm-1 and 1458 cm-1, and asymmetric stretching vibration of the pyrrole rings at 1277 cm-1 and 1024 cm-1, as well as stretching vibration of =C-N and twisting vibration of =C-H of polymeric pyrrole, indicating the formation of PPy [38-40]. Moreover, the synthesized 2D mPPy nanosheets and the control samples (noted as PPy-blank, synthesized without any templates) exhibited the almost same infrared signals in the wavenumber range of 500-4000 cm-1, which can prove the complete removal of BCP and PFCA templates. Moreover, the characteristic peaks of BCP and PFCA, including ArH, -CH2/-CH3, C=C of aromatic benzene rings, and carboxyl and alkyl signals of PFCA, cannot be found in the IR spectra of the 2D mPPy nanosheets, which also versified the removal of templates.

    The UV–vis spectroscopy showed that the 2D mPPy nanosheets possessed the similar signals with the PPy-blank materials (Fig. S2 in Supporting information). Among them, the signal of ~330 nm corresponds to the ππ* electronic transition of pyrrole ring, while the signal of ~420 nm is attributed to the polarization peak of PPy [41, 42].

    The morphology of the obtained PPy can be observed by the scanning electron microscopy (SEM, Fig. 1), which revealed that the resultant PPy samples possessed 2D ultrathin nanosheet architecture, and uniformly distributed mesopores with pore diameter of approximately 15–20 nm. In contrast, we only obtained the irregular PPy nanoparticles if without any templates (PPy-blank), as shown Fig. S2. This result indicated that BCP and PFCA templates play a very important role in the synthesis of mPPy materials with unique morphology and structure.

    Figure 1

    Figure 1.  Morphology and structure of the 2D mPPy nanosheets. (a) Schematic illustration of the 2D mPPy nanosheets. (b) AFM survey of the 2D mPPy nanosheets (Vertical scale: 114.2 nm). (c, d) SEM images of the 2D mPPy nanosheets.

    The results of atomic force microscopy (AFM, Fig. 1b) also revealed that the prepared 2D mPPy nanosheets had a smooth surface with a total thickness of about 24 nm. As previously reported, the diameter of PS90-b-PEO114 spherical micelles here used is about 12–15 nm [37]. Therefore, the thickness of the 2D mPPy nanosheets corresponds to the height of the two layers of BCP spherical micelles, indicating that the spherical BCP micelles would close pack on the both surfaces of PFCA into sandwich structure. In addition, some smaller PPy nanosheets can be also found in AFM images, which may be caused by the constant stirring, polymerization and removal of the template during the preparation of PPy.

    Transmission electron microscopy characterization (Fig. 2) further demonstrated that 2D mPPy nanosheets obtained by this soft template-oriented strategy possessed uniform mesopores with a pore size of approximately 18 nm, consistent with the above SEM results. At the same time, the high-resolution TEM (HRTEM) also revealed the overlap of mesopores in vertical, which may be formed by the packing of different PPy layers. Therefore, we speculated that the formation of bilayer-structured PPy nanosheets may result from the simultaneous absorption, assembly and growth of PPy on the both of surfaces of PFCA bilayer templates. Interestingly, besides mesopores, some micropores of about 1 nm can be also found in the 2D mPPy nanosheets (Fig. 2d), may owing to the contribution of PEO chains by spreading and occupying space in PPy frameworks, their removal would lead to the formation of micropores. The Nitrogen adsorption analysis below would provide more evidences for the presence of micropores.

    Figure 2

    Figure 2.  TEM images of the 2D mPPy nanosheets at different magnifications.

    Powder X-ray diffraction (XRD, Fig. S3 in Supporting information) displayed a weak peak of 23.8° (2θ), corresponding to the ππ interaction of the aromatic ring between the PPy chains [39, 40]. It indicated that the resultant materials consisted primarily of amorphous polymeric frameworks.

    Nitrogen adsorption test manifested (Fig. 3) that the 2D mPPy nanosheets had uniform mesopore with a pore size of about 18 nm. This result is agreed to the above SEM and TEM characterizations. As shown in nitrogen adsorption analysis, besides mesopores, the 2D PPy nanosheets have some micropores and macropores. The mesopores are derived from the removal of BCP templates and the macropores may be made from the stacked ultrathin PPy nanosheets, while the micropores may be attributed to the occupation of the PEO chains in the PPy polymer frameworks, because the interaction of the PEO chains and the pyrrole monomers would lead to the assembly and growth of pyrrole around the PEO chains, then the PEO chains interspersed into the PPy polymer networks and generated microporous channels after BCP removal. Similar phenomena were often found in mesoporous silica and carbon systems [43-45]. Additionally, the BET surface area and pore volume of the 2D mPPy nanosheets were 56 m2/g and 0.64 cm3/g, respectively, which were close to the previously reported 2D mesoporous PPy [37]. In contrast, the PPy-blank sample has a BET surface area of only 25 m2/g. This result indicates that BCP and PFCA templates are of great importance to the formation of 2D mesoporous materials with high specific surface area.

    Figure 3

    Figure 3.  Nitrogen adsorption–desorption isotherm and pore size distributions of the 2D mPPy nanosheets.

    Given their unique structure, including high specific surface area, regular mesoporous array and ultra-thin nanosheet structure, etc., the 2D mPPy nanosheets would be a suitable candidate for gas sensing. Therefore, we further evaluated their sensing performance for NH3 detecting.

    The response and recovery properties of the 2D mPPy nanosheets for NH3 are tested at 22 ℃ and relative humidity of 21%. Fig. 4a showed that the 2D mPPy nanosheets had an excellent sensitivity to NH3, which can reach 42% even at very low concentration of 20 ppm. Further, the sensitivity increased with the increase of NH3 concentration. The detecting limitation and sensitivity of the 2D mPPy nanosheets for NH3 was very close to, or even exceeded those of the conventional PPy with the different morphologies of nanowires, nanotubes or films [46-50], although which are still needed to be improved. As a p-type conductor, the excellent conductivity of polypyrrole is mainly attributed to their hole migration. When NH3 gas spread into polypyrrole frameworks, they can donate electrons to the holes of PPy and thus reduce the numbersofholes, resultingin anincreaseof the resistivity of PPy.The resistivity changes of PPy can be converted into the detectable signals for sensing device. Therefore, conducting polymer of PPy as a sensitive material can be used for NH3 detecting [51]. Fig. 3 also demonstratedthat, when escaping from NH3, the resistanceof the2D mPPy nanosheets immediately dropped. The recovery time of resistance became gradually longer with the increase of cycle numbers, perhaps due to the inevitable entrapment of the residual NH3 molecules in the mesoporous materials.

    Figure 4

    Figure 4.  The sensing performance of the 2D mPPy nanosheets. (a) The sensitivity of the 2D mPPy nanosheets for NH3 with different concentrations. (b) The sensitivity of the 2D mPPy nanosheets and PPy-blank for NH3 detecting. (c) The sensitivity for NH3 detecting of the 2D mPPy nanosheets with different acids at 1 mol/L. (d) The detecting sensitivity of the 2D mPPy nanosheets for different gases.

    Furthermore, we compared the NH3 sensing performance of the 2D mPPy nanosheets with PPy-blank samples. As shown in Fig. 4b, when the NH3 concentration was 200 ppm, the 2D mPPy nanosheets exhibited a higher sensitivity than PPy-blank samples, because the higher specific surface area was favorable to the contact with gas molecules and thus improved their sensitivity. However, it would also result in a longer recovery time for the 2D mPPy nanosheets.

    The sensing performance of the 2D mPPy nanosheets doped with different acids, such as hydrochloric acid (HCl) and ptoluenesulfonic acid (TsOH), were also investigated (Fig. 4c). At the same concentration (1 mol/L), the doping of HCl for the 2D mPPy nanosheets offered a higher sensitivity for NH3 detecting, it may be because that HCl, as a smaller molecule, is relatively easier to dope into the compactly intertwined PPy chains.

    We also investigated the response ability of the 2D mPPy nanosheets for different gases (200 ppm of NH3, HCl, acetone and ethanol) (Fig. 4d). The results revealed the 2D mPPy nanosheets had the best response ability to NH3, but a less response to HCl gas. Meanwhile, with regard to HCl detecting, they need longer response (119 s to 22 s) and recovery times (476 s to 173 s). In addition, the 2D mPPy nanosheets have almost no obvious response to acetone and ethanol. Compared to the other gases, such as HCl gas, acetone and EtOH, etc., NH3 possesses the stronger abilityof giving electrons and are easier form NH4+, therefore, the device would have stronger adsorption and higher sensitivity for NH3.

    In conclusion, we synthesized the 2D mPPy nanosheets by a modified co-assembly strategy based on dual templates of PFCA and BCP, which featured a hierarchical nanopores (including mesopores and micropores), ultrathin thickness and high surface area. When serving for electrochemical sensor, the resultant 2D mPPy nanosheets exhibited a fast response and detection for NH3. Therefore, we expect that this study would inspire more promising nanostructured materials for gas sensors.

    This work was supported by the research programs from the National Natural Science Foundation of China (Nos. 51773062 and 61831021).

    Supplementary material related to this article canbefound, in the online version, at doi:https://doi.org/10.1016/j.cclet.2019.04.071.


    1. [1]

      F. Bonaccorso, L. Colombo, G. Yu, et al., Science 347(2015) 1246501. doi: 10.1126/science.1246501

    2. [2]

      M. Chhowalla, H.S. Shin, G. Eda, et al., Nat. Chem. 5(2013) 263-275. doi: 10.1038/nchem.1589

    3. [3]

      Y. Guo, K. Xu, C. Wu, J. Zhao, Y. Xie, Chem. Soc. Rev. (2015) 637-646.

    4. [4]

      Y. Shi, H. Li, L.J. Li, Chem. Soc. Rev. 44(2015) 2744-2756. doi: 10.1039/C4CS00256C

    5. [5]

      Z. Pei, H. Hu, G. Liang, C. Ye, Nano-micro Lett. 9(2017) 19. doi: 10.1007/s40820-016-0119-z

    6. [6]

      M. Xu, T. Liang, M. Shi, H. Chen, Chem. Rev. 113(2013) 3766-3798. doi: 10.1021/cr300263a

    7. [7]

      X. Peng, L. Peng, C. Wu, Y. Xie, Chem. Soc. Rev. 43(2014) 3303-3323. doi: 10.1039/c3cs60407a

    8. [8]

      C. Chen, J. Xi, E. Zhou, et al., Nano-micro Lett. 10(2018) 26. doi: 10.1007/s40820-017-0179-8

    9. [9]

      X. Liu, T. Ma, N. Pinna, J. Zhang, Adv. Funct. Mater. 27(2017) 1702168. doi: 10.1002/adfm.201702168

    10. [10]

      F. Schedin, A. Geim, S. Morozov, et al., Nat. Mater. 6(2007) 652-665. doi: 10.1038/nmat1967

    11. [11]

      P.A. Russo, N. Donato, S.G. Leonardi, et al., Angew. Chem. Int. Ed. 51(2012) 11053-11057. doi: 10.1002/anie.201204373

    12. [12]

      S.Y. Cho, Y. Lee, H.J. Koh, et al., Adv. Mater. 28(2016) 7020-7028. doi: 10.1002/adma.201601167

    13. [13]

      S. Cui, H. Pu, S.A. Wells, et al., Nat. Commun. 6(2015) 8632. doi: 10.1038/ncomms9632

    14. [14]

      T. Lin, I.W. Chen, F. Liu, et al., Science 350(2015) 1508-1513. doi: 10.1126/science.aab3798

    15. [15]

      Y. Xu, Z. Lin, X. Zhong, et al., Nat. Commun. 5(2014) 4554. doi: 10.1038/ncomms5554

    16. [16]

      D. Zhou, Y. Cui, P.W. Xiao, et al., Nat. Commun. 5(2014) 4716. doi: 10.1038/ncomms5716

    17. [17]

      K. Celebi, J. Buchheim, R.M. Wyss, et al., Science 344(2014) 289-292. doi: 10.1126/science.1249097

    18. [18]

      J. Liang, Y. Jiao, M. Jaroniec, S.Z. Qiao, Angew. Chem. Int. Ed. 51(2012) 11496-11500. doi: 10.1002/anie.201206720

    19. [19]

      S.P. Koenig, L. Wang, J. Pellegrino, J.S. Bunch, Nat Nanotech. 7(2012) 728-732. doi: 10.1038/nnano.2012.162

    20. [20]

      J. Bai, X. Zhong, S. Jiang, Y. Huang, X. Duan, Nat. Nanotech. 5(2010) 190-194. doi: 10.1038/nnano.2010.8

    21. [21]

      Y. Fang, Y. Lv, J. Tang, et al., Angew. Chem. Int. Ed. 127(2015) 8545-8549. doi: 10.1002/ange.201502845

    22. [22]

      D. Feng, Y. Lv, Z. Wu, et al., J. Am. Chem. Soc. 133(2011) 15148-15156. doi: 10.1021/ja2056227

    23. [23]

      J. Tang, J. Liu, C. Li, et al., Angew. Chem. Int. Ed. 54(2015) 588-593.

    24. [24]

      J. Liu, T. Yang, D.W. Wang, et al., Nat. Commun. 4(2013) 2987.

    25. [25]

      J. Liu, N.P. Wickramaratne, S.Z. Qiao, M. Jaroniec, Nat. Mater.14(2015) 763-774. doi: 10.1038/nmat4317

    26. [26]

      Z. Cui, C. Zu, W. Zhou, A. Manthiram, J.B. Goodenough, Adv. Mater. (2016) 6926-6931. doi: 10.1002/adma.201601382

    27. [27]

      T. Wagner, S. Haffer, C. Weinberger, D. Klaus, M. Tiemann, Chem. Soc. Rev. 42(2013) 4036-4053. doi: 10.1039/C2CS35379B

    28. [28]

      Y. Li, W. Luo, N. Qin, et al., Angew. Chem. Int. Ed. 53(2014) 9035-9040. doi: 10.1002/anie.201403817

    29. [29]

      J. Ma, Y. Ren, X. Zhou, et al., Adv. Funct. Mater. 28(2018) 1705268. doi: 10.1002/adfm.201705268

    30. [30]

      W. Luo, T. Zhao, Y. Li, et al., J. Am. Chem. Soc. 138(2016) 12586-12595. doi: 10.1021/jacs.6b07355

    31. [31]

      G. Wang, J. Qin, X. Zhou, et al., Adv. Funct. Mater. 28(2018) 1870364. doi: 10.1002/adfm.201870364

    32. [32]

      Y. Zou, X. Zhou, Y. Zhu, et al., Acc. Chem. Res. 52(2019) 714-725. doi: 10.1021/acs.accounts.8b00598

    33. [33]

      Z. Wen, Q. Shen, X. Sun, Nano-micro Lett. 9(2017) 45. doi: 10.1007/s40820-017-0146-4

    34. [34]

      E. Stokstad, Science 343(2014) 238. doi: 10.1126/science.343.6168.238

    35. [35]

      X. Zhou, S. Lee, Z. Xu, J. Yoon, Chem. Rev. 115(2015) 7944-8000. doi: 10.1021/cr500567r

    36. [36]

      S. Liu, J. Zhang, R. Dong, et al., Angew. Chem. Int. Ed. 55(2016) 12516-12521. doi: 10.1002/anie.201606988

    37. [37]

      S. Liu, F. Wang, R. Dong, et al., Adv. Mater. 28(2016) 8365-8370. doi: 10.1002/adma.201603036

    38. [38]

      G. Cho, B.M. Fung, D.T. Glatzhofer, J.S. Lee, Y.G. Shul, Langmuir 17(2001) 456-461. doi: 10.1021/la0012485

    39. [39]

      X. Zhang, J. Zhang, W. Song, Z. Liu, J. Phys. Chem. B 110(2006) 1158-1165. doi: 10.1021/jp054335k

    40. [40]

      Y. Ma, S. Jiang, G. Jian, et al., Energ. Environ. Sci. 2(2009) 224-229. doi: 10.1039/B807213M

    41. [41]

      S.E. Mavundla, G.F. Malgas, D.E. Motaung, E.I. Iwuoha, J. Mater. Sci. 45(2010) 3325-3330. doi: 10.1007/s10853-010-4351-5

    42. [42]

      C.T. Kuo, S.A. Chen, G.W. Hwang, H.H. Kuo, Synth. Met. 93(1998) 155-160. doi: 10.1016/S0379-6779(97)04072-1

    43. [43]

      M. Kruk, M. Jaroniec, C.H. Ko, R. Ryoo, Chem. Mater. 12(2000) 1961-1968. doi: 10.1021/cm000164e

    44. [44]

      M. Imperor-Clerc, P. Davidson, A. Davidson, J. Am. Chem. Soc. 122(2000) 11925-11933. doi: 10.1021/ja002245h

    45. [45]

      R. Ryoo, S.H. Joo, M. Kruk, M. Jaroniec, Adv. Mater. 13(2001) 677-681. doi: 10.1002/1521-4095(200105)13:9<677::AID-ADMA677>3.0.CO;2-C

    46. [46]

      S.C. Hernandez, D. Chaudhuri, W. Chen, N.V. Myung, A. Mulchandani, Electroanalysis 19(2007) 2125-2130. doi: 10.1002/elan.200703933

    47. [47]

      H. Yoon, M. Chang, J. Jang, J. Phys. Chem. B 110(2006) 14074-14077. doi: 10.1021/jp061423b

    48. [48]

      X. Yang, L. Li, Synth. Met. 160(2010) 1365-1367. doi: 10.1016/j.synthmet.2010.04.015

    49. [49]

      J.J. Lee, D. Yoo, C. Park, J.H. Kim, H.H. Choi, Macromol. Symp. 354(2015) 280-286. doi: 10.1002/masy.201400131

    50. [50]

      H.J. Kharat, K.P. Kakde, P.A. Savale, et al., Polym. Adv. Technol. 18(2007) 397-402. doi: 10.1002/pat.903

    51. [51]

      Y. Jiang, T. Wang, Z. Wu, et al., Sens. Actuators B -Chem. 66(2000) 280-282. doi: 10.1016/S0925-4005(00)00342-7

  • Figure 1  Morphology and structure of the 2D mPPy nanosheets. (a) Schematic illustration of the 2D mPPy nanosheets. (b) AFM survey of the 2D mPPy nanosheets (Vertical scale: 114.2 nm). (c, d) SEM images of the 2D mPPy nanosheets.

    Figure 2  TEM images of the 2D mPPy nanosheets at different magnifications.

    Figure 3  Nitrogen adsorption–desorption isotherm and pore size distributions of the 2D mPPy nanosheets.

    Figure 4  The sensing performance of the 2D mPPy nanosheets. (a) The sensitivity of the 2D mPPy nanosheets for NH3 with different concentrations. (b) The sensitivity of the 2D mPPy nanosheets and PPy-blank for NH3 detecting. (c) The sensitivity for NH3 detecting of the 2D mPPy nanosheets with different acids at 1 mol/L. (d) The detecting sensitivity of the 2D mPPy nanosheets for different gases.

  • 加载中
计量
  • PDF下载量:  2
  • 文章访问数:  221
  • HTML全文浏览量:  1
文章相关
  • 发布日期:  2020-02-01
  • 收稿日期:  2019-03-25
  • 接受日期:  2019-04-29
  • 修回日期:  2019-04-26
  • 网络出版日期:  2019-04-30
通讯作者: 陈斌, bchen63@163.com
  • 1. 

    沈阳化工大学材料科学与工程学院 沈阳 110142

  1. 本站搜索
  2. 百度学术搜索
  3. 万方数据库搜索
  4. CNKI搜索

/

返回文章