Zhi Hui Zhou, Jian Hua Yang, Li Feng Chang, Yan Zhang, Wei Guo Sun, Jin Qu Wang. Novel preparation of NaA/carbon nanocomposite thin films with high permeance for CO2/CH4 separation[J]. Chinese Chemical Letters,
2007, 18(4): 455-457.
doi:
10.1016/j.cclet.2007.01.039
Citation: Zhi Hui Zhou, Jian Hua Yang, Li Feng Chang, Yan Zhang, Wei Guo Sun, Jin Qu Wang. Novel preparation of NaA/carbon nanocomposite thin films with high permeance for CO2/CH4 separation[J]. Chinese Chemical Letters, 2007, 18(4): 455-457. doi: 10.1016/j.cclet.2007.01.039
Citation: Zhi Hui Zhou, Jian Hua Yang, Li Feng Chang, Yan Zhang, Wei Guo Sun, Jin Qu Wang. Novel preparation of NaA/carbon nanocomposite thin films with high permeance for CO2/CH4 separation[J]. Chinese Chemical Letters, 2007, 18(4): 455-457. doi: 10.1016/j.cclet.2007.01.039
Novel preparation of NaA/carbon nanocomposite thin films with high permeance for CO2/CH4 separation
摘要:
Novel NaA/carbon nanocomposite thin films were successfully prepared on a porous α-Al2O3 substrate by incorporating nanosized NaA zeolite into novolak-type phenolic resin. The prepared films were characterized by XRD, SEM and single gas permeation tests. The NaA zeolite/carbon nanocomposite thin films exhibited that the ideal separation factor of CO2/CH4 was 28.4and the carbon dioxide flux was 3.39×10-7 mol/(Pa m2 s) at room temperature and under a pressure difference of 100 kPa, which was two orders of magnitude higher than that of pure carbon membrane prepared at the same procedures and conditions as those of composite films. From the SEM images, the films were continuous and highly intergrown. Compared with carbon membranes, the thickness of nanocomposite films was drastically decreased, which was helpful to reduce the diffusion resistance and increase the flux of gas permeance.
-
关键词:
- Nanocomposite
- / Thin films
- / High performance
- / Gas separation
English
Novel preparation of NaA/carbon nanocomposite thin films with high permeance for CO2/CH4 separation
Abstract:
Novel NaA/carbon nanocomposite thin films were successfully prepared on a porous α-Al2O3 substrate by incorporating nanosized NaA zeolite into novolak-type phenolic resin. The prepared films were characterized by XRD, SEM and single gas permeation tests. The NaA zeolite/carbon nanocomposite thin films exhibited that the ideal separation factor of CO2/CH4 was 28.4and the carbon dioxide flux was 3.39×10-7 mol/(Pa m2 s) at room temperature and under a pressure difference of 100 kPa, which was two orders of magnitude higher than that of pure carbon membrane prepared at the same procedures and conditions as those of composite films. From the SEM images, the films were continuous and highly intergrown. Compared with carbon membranes, the thickness of nanocomposite films was drastically decreased, which was helpful to reduce the diffusion resistance and increase the flux of gas permeance.
-
Key words: