Citation: Zhen Xi Wang, Qing Hua Zhang, Yi Tao Yu, Xiao Li Zhan, Feng Qiu Chen, Ji Hai Xiong. Synthesis of polystyrene-styrene/butadiene diblock copolymers via reversible addition-fragmentation chain transfer miniemulsion polymerization[J]. Chinese Chemical Letters, 2010, 21(12): 1497-1500. doi: 10.1016/j.cclet.2010.06.001
Citation: Zhen Xi Wang, Qing Hua Zhang, Yi Tao Yu, Xiao Li Zhan, Feng Qiu Chen, Ji Hai Xiong. Synthesis of polystyrene-styrene/butadiene diblock copolymers via reversible addition-fragmentation chain transfer miniemulsion polymerization[J]. Chinese Chemical Letters, 2010, 21(12): 1497-1500. doi: 10.1016/j.cclet.2010.06.001
Synthesis of polystyrene-styrene/butadiene diblock copolymers via reversible addition-fragmentation chain transfer miniemulsion polymerization
摘要:
Polystyrene-styrene/butadiene diblock copolymers were synthesized via reversible addition-fragmentation chain transfer (RAFT) miniemulsion polymerization. During the polymerization process, the molecular weight distribution was narrow and the numerical molecular weight of the copolymers increased with increasing conversion of monomers, which was close to the theoretical. FT-IR and 1H NMR results indicated that the microstructure of the polymer was mainly 1, 4-trans-butadiene with small amount of 1, 2-units, and composition in the copolymers was obtained.
English
Synthesis of polystyrene-styrene/butadiene diblock copolymers via reversible addition-fragmentation chain transfer miniemulsion polymerization
Abstract:
Polystyrene-styrene/butadiene diblock copolymers were synthesized via reversible addition-fragmentation chain transfer (RAFT) miniemulsion polymerization. During the polymerization process, the molecular weight distribution was narrow and the numerical molecular weight of the copolymers increased with increasing conversion of monomers, which was close to the theoretical. FT-IR and 1H NMR results indicated that the microstructure of the polymer was mainly 1, 4-trans-butadiene with small amount of 1, 2-units, and composition in the copolymers was obtained.