Citation: Zou Ying, Wang Hongtao, Sheng Liangquan. Intermediate Temperature Fuel Cell Performance of the Composite Electrolyte Ce_0.8Gd_0.2O_2-α-(Li/K)₂CO₃[J]. Chemistry, ;2017, 80(6): 558-562. shu

Intermediate Temperature Fuel Cell Performance of the Composite Electrolyte Ce_0.8Gd_0.2O_2-α-(Li/K)₂CO₃

Anhui Provincial Key Laboratory for Degradation and Monitoring of Pollution of the Environment, School of Chemical and Material Engineering, Fuyang Teachers College, Fuyang 236037

Corresponding author: Wang Hongtao, hongtaoking3@163.com
Received Date: 19 December 2016
Accepted Date: 6 February 2017

Figures(7)

Ce_0.8Gd_0.2O_2-α was synthesized by sol-gel method at 900℃, which is much lower than the conventional sintering temperature (1400℃), and was further compounded with (Li/K)₂CO₃. The XRD pattern showed that there is no chemical reaction between Ce_0.8Gd_0.2O_2-α and (Li/K)₂CO₃. The SEM images demonstrated that the composite electrolyte is sufficiently dense and does not have holes. The conductivities of the composite electrolyte in dry nitrogen atmosphere were measured using electrochemical analyzer. The highest conductivity was observed to be 6.4×10^-2 S·cm^-1 at 600℃, which is higher than that of single CeO₂ material. The H₂/O₂ fuel cell performance test showed that the electrolyte impedance and polarization impedance under open-circuit condition are 2.7Ω and 0.8Ω, respectively, and the maximum output power density is 267mW·cm^-2 at 600℃.
- CeO₂,
- Composite,
- Electrolyte,
- Fuel cell,
- Conductivity
1. [1]
  Y Chen, N Orlovskaya, E A Payzant et al. J. Eur. Ceram. Soc., 2015, 35:951~958.
2. [2]
3. [3]
  J Kondoh. J. Alloy. Compd., 2004, 375:270~282.
4. [4]
5. [5]
  T Ueno, Y Hirata, T Shimonosono. Ceram. Int., 2016, 42:1926~1932.
6. [6]
7. [7]
  T V Gestel, D Sebold, H P Buchkremer. J. Eur. Ceram. Soc., 2015, 35:1505~1515.
8. [8]
  J H Joo, G M Choi. Solid State Ionics, 2007, 178:1602~1607.
9. [9]
  T Kobayashi, S R Wang, M Dokiya. Solid State Ionics, 1999, 126:349~357.
10. [10]
  L Zhang, R Lan, X X Xu et al. J. Power Sources, 2009, 194:967~971.
11. [11]
12. [12]
13. [13]
  R Dziembaj, M Molenda, M M Zaitz et al. Solid State Ionics, 2013, 251:18~22.
14. [14]
  A Gondolini, E Mercadelli, A Sanson et al. J. Eur. Ceram. Soc., 2013, 33:67~77.
15. [15]
  M Prekajski, M Stojmenovic, A Radojkovic et al. J. Alloy. Compd., 2014, 617:563~568.
16. [16]
  Y Zhao, Z Xu, C Xia et al. Int. J. Hydrogen Energ., 2013, 38:1553~1559.
17. [17]
18. [18]
  S Shawuti, M A Gulgun. J. Power Sources, 2014, 267:128~135.
19. [19]
  B Zhu, S Li, B E Mellander. Electrochem. Commun., 2008,10:302~305.
20. [20]
  S Rajesh, D A Macedo, R M Nascimento et al. Int. J. Hydrogen Energ., 38(2013) 16539~16545.
21. [21]
  J T Kim, T H Lee, K Y Park et al. J. Power Sources, 2015, 275:563~572.
22. [22]
  J Huang, Z Mao, Z Liu et al. J. Power Sources, 2008,175:238~243.
23. [23]
  J Huang, Z Gao, Z Mao. Int. J. Hydrogen Energ., 2010, 35:4270~4275.
24. [24]
  N S Ferreira, R S Angélica, V B Marques et al. Mater. Lett., 2016, 165:139~142.
25. [25]
  M O Mazan, J Marrero-Jerez, A Soldati et al. Int. J. Hydrogen Energ., 2015, 40:3981~3989.
26. [26]
  A I B Rondao, S G Patricio, F M L Figueiredo et al. Int. J. Hydrogen Energ., 2014, 39:5460~5469.
27. [27]
  N C T Martins, S Rajesh, F M B Marques et al. Mater. Res. Bull., 2015, 70:449~455.
28. [28]
  S Kobi, N Jaiswal, D Kumar et al. J. Alloy. Compd., 2016, 658:513~519.
29. [29]
  X Liu, N Fechler, M Antonietti et al. Chem. Soc. Rev., 2013, 42:8237~8265.
30. [30]
  N Sammes, R Phillips, A Smirnova et al. J. Power Sources, 2004, 134:153~159.
31. [31]
  C Xia, Y Li, Y Tian et al. J. Power Sources, 2009, 188:156~162.
32. [32]
  M Chen, H Zhang, L Fan et al. Int. J. Hydrogen Energ., 2014, 39:12309~12316.
33. [33]
  H Wang, J Liu. Ceram. Int., 2016, 42:18136~18140.
34. [34]
  M Afzal, R Raza, S Du et al. Electrochim. Acta, 2015, 178:385~391.
1. [1]
  Ronghui LI . Photocatalysis performance of nitrogen-doped CeO₂ thin films via ion beam-assisted deposition. Chinese Journal of Inorganic Chemistry, 2025, 41(6): 1123-1130. doi: 10.11862/CJIC.20240440
2. [2]
  Xiutao Xu , Chunfeng Shao , Jinfeng Zhang , Zhongliao Wang , Kai Dai . Rational Design of S-Scheme CeO₂/Bi₂MoO₆ Microsphere Heterojunction for Efficient Photocatalytic CO₂ Reduction. Acta Physico-Chimica Sinica, 2024, 40(10): 2309031-0. doi: 10.3866/PKU.WHXB202309031
3. [3]
  Peng Li , Yuanying Cui , Zhongliao Wang , Graham Dawson , Chunfeng Shao , Kai Dai . Efficient interfacial charge transfer of CeO₂/Bi₁₉Br₃S₂₇ S-scheme heterojunction for boosted photocatalytic CO₂ reduction. Acta Physico-Chimica Sinica, 2025, 41(6): 100065-0. doi: 10.1016/j.actphy.2025.100065
4. [4]
  Ke Qiu , Fengmei Wang , Mochou Liao , Kerun Zhu , Jiawei Chen , Wei Zhang , Yongyao Xia , Xiaoli Dong , Fei Wang . A Fumed SiO₂-based Composite Hydrogel Polymer Electrolyte for Near-Neutral Zinc-Air Batteries. Acta Physico-Chimica Sinica, 2024, 40(3): 2304036-0. doi: 10.3866/PKU.WHXB202304036
5. [5]
  Shiqi Zhang , Heng Zhang , Aiwen Lei . 从物理化学的角度看化学能的利用. University Chemistry, 2025, 40(6): 310-315. doi: 10.12461/PKU.DXHX202408124
6. [6]
  Xichen YAO , Shuxian WANG , Yun WANG , Cheng WANG , Chuang ZHANG . Oxygen reduction performance of self?supported Fe/N/C three-dimensional aerogel catalyst layers. Chinese Journal of Inorganic Chemistry, 2025, 41(7): 1387-1396. doi: 10.11862/CJIC.20240384
7. [7]
  Jiayu Tang , Jichuan Pang , Shaohua Xiao , Xinhua Xu , Meifen Wu . Improvement for Measuring Transference Numbers of Ions by Moving-Boundary Method. University Chemistry, 2024, 39(5): 193-200. doi: 10.3866/PKU.DXHX202311021
8. [8]
  Ran HUO , Zhaohui ZHANG , Xi SU , Long CHEN . Research progress on multivariate two dimensional conjugated metal organic frameworks. Chinese Journal of Inorganic Chemistry, 2024, 40(11): 2063-2074. doi: 10.11862/CJIC.20240195
9. [9]
  Ru SONG , Biao WANG , Chunling LU , Bingbing NIU , Dongchao QIU . Electrochemical properties of stable and highly active PrBa_0.5Sr_0.5Fe_1.6Ni_0.4O_5+δ cathode material. Chinese Journal of Inorganic Chemistry, 2025, 41(4): 639-649. doi: 10.11862/CJIC.20240397
10. [10]
  Tao Jiang , Yuting Wang , Lüjin Gao , Yi Zou , Bowen Zhu , Li Chen , Xianzeng Li . Experimental Design for the Preparation of Composite Solid Electrolytes for Application in All-Solid-State Batteries: Exploration of Comprehensive Chemistry Laboratory Teaching. University Chemistry, 2024, 39(2): 371-378. doi: 10.3866/PKU.DXHX202308057
11. [11]
  Chenye An , Sikandaier Abiduweili , Xue Guo , Yukun Zhu , Hua Tang , Dongjiang Yang . Hierarchical S-scheme Heterojunction of Red Phosphorus Nanoparticles Embedded Flower-like CeO₂ Triggering Efficient Photocatalytic Hydrogen Production. Acta Physico-Chimica Sinica, 2024, 40(11): 2405019-0. doi: 10.3866/PKU.WHXB202405019
12. [12]
  Zhuo WANG , Junshan ZHANG , Shaoyan YANG , Lingyan ZHOU , Yedi LI , Yuanpei LAN . Preparation and photocatalytic performance of CeO₂-reduced graphene oxide by thermal decomposition. Chinese Journal of Inorganic Chemistry, 2024, 40(9): 1708-1718. doi: 10.11862/CJIC.20240067
13. [13]
  Jiandong Liu , Zhijia Zhang , Kamenskii Mikhail , Volkov Filipp , Eliseeva Svetlana , Jianmin Ma . Research Progress on Cathode Electrolyte Interphase in High-Voltage Lithium Batteries. Acta Physico-Chimica Sinica, 2025, 41(2): 2308048-0. doi: 10.3866/PKU.WHXB202308048
14. [14]
  Zhaoxuan ZHU , Lixin WANG , Xiaoning TANG , Long LI , Yan SHI , Jiaojing SHAO . Application of poly(vinyl alcohol) conductive hydrogel electrolytes in zinc ion batteries. Chinese Journal of Inorganic Chemistry, 2025, 41(5): 893-902. doi: 10.11862/CJIC.20240368
15. [15]
  Mingyang Men , Jinghua Wu , Gaozhan Liu , Jing Zhang , Nini Zhang , Xiayin Yao . Sulfide Solid Electrolyte Synthesized by Liquid Phase Approach and Application in All-Solid-State Lithium Batteries. Acta Physico-Chimica Sinica, 2025, 41(1): 100004-0. doi: 10.3866/PKU.WHXB202309019
16. [16]
  Da Wang , Xiaobin Yin , Jianfang Wu , Yaqiao Luo , Siqi Shi . All-Solid-State Lithium Cathode/Electrolyte Interfacial Resistance: From Space-Charge Layer Model to Characterization and Simulation. Acta Physico-Chimica Sinica, 2024, 40(7): 2307029-0. doi: 10.3866/PKU.WHXB202307029
17. [17]
  Hanmei Lü , Xin Chen , Qifu Sun , Ning Zhao , Xiangxin Guo . Uniform Garnet Nanoparticle Dispersion in Composite Polymer Electrolytes. Acta Physico-Chimica Sinica, 2024, 40(3): 2305016-0. doi: 10.3866/PKU.WHXB202305016
18. [18]
  Fengqiao Bi , Jun Wang , Dongmei Yang . Specialized Experimental Design for Chemistry Majors in the Context of “Dual Carbon”: Taking the Assembly and Performance Evaluation of Zinc-Air Fuel Batteries as an Example. University Chemistry, 2024, 39(4): 198-205. doi: 10.3866/PKU.DXHX202311069
19. [19]
  Xinran Zhang , Siqi Liu , Yichi Chen , Qingli Zou , Qinghong Xu , Yaqin Huang . From Protein to Energy Storage Materials: Edible Gelatin Jelly Electrolyte. University Chemistry, 2025, 40(7): 255-266. doi: 10.12461/PKU.DXHX202408104
20. [20]
  Bowen Yang , Rui Wang , Benjian Xin , Lili Liu , Zhiqiang Niu . C-SnO₂/MWCNTs Composite with Stable Conductive Network for Lithium-based Semi-Solid Flow Batteries. Acta Physico-Chimica Sinica, 2025, 41(2): 2310024-0. doi: 10.3866/PKU.WHXB202310024

Get Citation

PDF

XML

Metrics

PDF Downloads(3)
Abstract views(457)
HTML views(63)

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

Intermediate Temperature Fuel Cell Performance of the Composite Electrolyte Ce0.8Gd0.2O2-α-(Li/K)2CO3

Metrics

通讯作者: 陈斌, bchen63@163.com

Intermediate Temperature Fuel Cell Performance of the Composite Electrolyte Ce_0.8Gd_0.2O_2-α-(Li/K)₂CO₃