Citation: WANG Hui, ZHANG Jun-feng, BAI Yun-xing, WANG Wen-feng, TAN Yi-sheng, HAN Yi-zhuo. NiO@SiO₂ core-shell catalyst for low-temperature methanation of syngas in slurry reactor[J]. Journal of Fuel Chemistry and Technology, ;2016, 44(5): 548-556. shu

NiO@SiO₂ core-shell catalyst for low-temperature methanation of syngas in slurry reactor

WANG Hui ^1,2 ,
ZHANG Jun-feng ^1,*,, ,
BAI Yun-xing ^1,2 ,
WANG Wen-feng ^1,2 ,
TAN Yi-sheng ¹ ,
HAN Yi-zhuo ¹

1.
State Key Laboratory of Coal Conversion, Institute of Coal Chemistry, Chinese Academy of Sciences, Taiyuan 030001, China
2.
University of Chinese Academy of Sciences, Beijing 100049, China

Corresponding author: ZHANG Jun-feng, zhangjf@sxicc.ac.cn
Received Date: 25 December 2015
Revised Date: 29 February 2016

Figures(6)

A series of NiO@SiO₂ core-shell catalysts were prepared using modified Stöber-method. Their catalytic performances in methanation of syngas were investigated in slurry reactor at 320 ℃. The catalysts before and after reaction were characterized by XRD, TEM, XPS, N₂-physisorption, etc. It was found that the NiO@SiO₂ core-shell samples had well-shape morphologies and relatively uniform scale. The catalyst test revealed that the methanation activity of these catalysts decreased dramatically with increase of core particle size. The three catalysts with distinct size of core and shell showed remarkably rapid deactivation in the initial period of 20 h and then deactivated slowly during the following reaction, while their CH₄ selectivity maintained at about 80%. Void-shell was formed during the reaction probably because easy-migrated Ni (CO)_x species were generated. Apparently, it was concluded that increase of core particle size, decrease of BET surface area and pore volume, and abatement of mesopores within 3-5 nm in the shell were responsible for the deactivation of these core-shell catalysts based on the characterization of catalysts.
- core-shell,
- nickel-based catalyst,
- slurry reactor,
- low-temperature methanation
1. [1]
  ZHANG Jun-feng, BAI Yun-xing, ZHANG Qing-de, XIE Hong-juan, TAN Yi-sheng, HAN Yi-zhuo. Low temperature methanation of syngas in a slurry reactor over Zr-doped Ni/γ-Al₂O₃ catalyst[J]. J Fuel Chem Technol, 2013,41(8):966-971.
2. [2]
  MENG Fan-hui, CHANG Hui-rong, LI Zhong. Catalytic performance of Ni-Mn/Al₂O₃ catalyst for CO methanation in slurry-bed reactor[J]. CIESC J, 2014,65(8):2997-3003.
3. [3]
  MENG Fan-hui, LIU Jun, LI Zhong, ZHONG Peng-zhan, ZHENG Hua-yan. Effect of Ce content of Ni-Ce/Al₂O₃ catalyst constructure and CO methanation in slurry-bed reactor[J]. J Fuel Chem Technol, 2014,42(2):231-237.
4. [4]
  ZHANG J F, BAI Y X, ZHANG Q D, WANG X X, ZHANG T, TAN Y S, HAN Y Z. Low-temperature methanation of syngas in slurry phase over Zr-doped Ni/γ-Al₂O₃ catalysts prepared using different methods[J]. Fuel, 2014,132:211-218. doi: 10.1016/j.fuel.2014.04.085
5. [5]
  HUANG Guo-bao, WANG Zhi-qing, LI Qing-feng, HUANG Jie-jie, FANG Yi-tian. Syngas methanation over nickel catalyst in liquid-phase[J]. J Fuel Chem Technol, 2014,42(8):952-957.
6. [6]
  HE Long. Research of nickel based catalyst for methanation of synthetic gas in slurry bed reactor[D]. Beijing: China University of Mining and Technology (Beijing), 2012.
7. [7]
  MA Sheng-li. Study on low temperature methanation for coal-derived syngas over Ni-based catalyst[D]. Taiyuan: Institute of Coal Chemistry, Chinese Academy of Sciences, 2011.
8. [8]
  GRAF C, VOSSEN D L J, IMHOF A, VAN BLAADEREN A. A general method to coat colloidal particles with silica[J]. Langmuir, 2003,19(17):6693-6700. doi: 10.1021/la0347859
9. [9]
  YAO L H, LI Y X, ZHAO J, JI W J, AU C T. Core-shell structured nanoparticles (M@SiO₂, Al₂O₃, MgO; M=Fe, Co, Ni, Ru) and their application in CO_x-free H₂ production via NH₃ decomposition[J]. Catal Today, 2010,158(3/4):401-408.
10. [10]
  LI Z W, MO L Y, KATHIRASER Y, KAWI S. Yolk-Satellite-Shell Structured Ni-Yolk@Ni@SiO₂ Nanocomposite: Superb Catalyst toward Methane CO₂ Reforming Reaction[J]. ACS Catal, 2015,4(5):1526-1536.
11. [11]
  LI Z W, KATHIRASER Y, KAWI S. Facile synthesis of high surface area yolk-shell Ni@Ni embedded SiO₂ via Ni phyllosilicate with enhanced performance for CO₂ reforming of CH₄[J]. ChemCatChem, 2014,7:160-168.
12. [12]
  LI L, YAO Y, SUN B, FEI Z Y, XIA H, ZHAO J, JI W J, AU C T. Highly active and stable lanthanum-doped core-shell-structured Ni@SiO₂ catalysts for the partial oxidation of methane to syngas[J]. ChemCatChem, 2013,5(12):3781-3787. doi: 10.1002/cctc.201300537
13. [13]
  LI L, HE S C, SONG Y Y, ZHAO J, JI W J, AU C T. Fine-tunable Ni@porous silica core-shell nanocatalysts: Synthesis, characterization, and catalytic properties in partial oxidation of methane to syngas[J]. J Catal, 2012,288:54-64. doi: 10.1016/j.jcat.2012.01.004
14. [14]
  LI Lei. Core-shell structured nanocatalysts: design, synthesize and their application in partial oxidation of methane to syngas[D]. Nanjing: Nanjing University, 2012.
15. [15]
  TAKENAKA S, UMEBAYASHI H, TANABE E, MATSUNE H, KISHIDA M. Specific performance of silica-coated Ni catalysts for the partial oxidation of methane to synthesis gas[J]. J Catal, 2007,245(2):392-400. doi: 10.1016/j.jcat.2006.11.005
16. [16]
  ZHANG L F, LI M, REN T Z, LIU X Y, YUAN Z Y. Ce-modified Ni nanoparticles encapsulated in SiO₂ for CO_x-free hydrogen production via ammonia decomposition[J]. Int J Hydrogen Energ, 2015,40(6):2648-2656. doi: 10.1016/j.ijhydene.2014.12.079
17. [17]
  ZHANG Ming-wei. Preparation of core-shell iron-based catalysts and their application for CO hydrogenation[D]. Taiyuan: Institute of Coal Chemistry, Chinese Academy of Sciences, 2011.
18. [18]
  ZHANG M W, FANG K G, LIN M G, HOU B, ZHONG L S, ZHU Y, WEI W, SUN Y H. Controlled Fabrication of Iron Oxide/Mesoporous Silica Core-Shell Nanostructures[J]. J Phys Chem C, 2013,117:21529-21538. doi: 10.1021/jp4049583
19. [19]
  XIE R Y, LI D B, HOU B, WANG J G, JIA L T, SUN Y H. Solvothermally derived Co₃O₄@m-SiO₂ nanocomposites for Fischer-Tropschsynthesis[J]. Catal Commun, 2011,12(5):380-383. doi: 10.1016/j.catcom.2010.10.010
20. [20]
  XIE R Y, WANG H, GAO P, XIA L, ZHANG Z Z, ZHAO T J, SUN Y H. Core@shell Co₃O₄@C-m-SiO₂ catalysts with inert C modified mesoporous channel for desired middle distillate[J]. Appl Catal A: Gen, 2015,492:93-99. doi: 10.1016/j.apcata.2014.12.023
21. [21]
  LI Y R, LU G X, MA J T. Highly active and stable nano NiO-MgO catalyst encapsulated by silica with a core-shell structurefor CO₂ methanation[J]. RSC Adv, 2014,4:17420-17428. doi: 10.1039/c3ra46569a
22. [22]
  MUNNIK P, VELTHOEN M E Z, DE JONGH P E, DE JONG K P, GOMMES C J. Nanoparticle growth in supported nickel catalysts during methanation reaction-larger is better[J]. Angew Chem, Int Ed, 2014,53(36):9493-9497. doi: 10.1002/anie.201404103
23. [23]
  ENGBAEK J, LYTKEN O, NIELSEN J H, CHORKENDORFF L. CO dissociation on Ni: The effect of steps and of nickel carbonyl[J]. Surf Sci, 2008,602(3):733-743. doi: 10.1016/j.susc.2007.12.008
24. [24]
  ZENG Bo. Synthesis of middle distillates via cobalt-based catalysts with core-shell structures[D]. Taiyuan: Institute of Coal Chemistry, Chinese Academy of Sciences, 2014.
25. [25]
  CHOU K, CHEN C. Fabrication and characterization of silver core and porous silica shell nanocomposite particles[J]. Microporous Mesoporous Mater, 2007,98:208-213. doi: 10.1016/j.micromeso.2006.09.006
1. [1]
  Dan Li , Hui Xin , Xiaofeng Yi . Comprehensive Experimental Design on Ni-based Catalyst for Biofuel Production. University Chemistry, 2024, 39(8): 204-211. doi: 10.3866/PKU.DXHX202312046
2. [2]
  Yu Wang , Haiyang Shi , Zihan Chen , Feng Chen , Ping Wang , Xuefei Wang . 具有富电子Pt^δ^-壳层的空心AgPt@Pt核壳催化剂：提升光催化H₂O₂生成选择性与活性. Acta Physico-Chimica Sinica, 2025, 41(7): 100081-. doi: 10.1016/j.actphy.2025.100081
3. [3]
  Lina Guo , Ruizhe Li , Chuang Sun , Xiaoli Luo , Yiqiu Shi , Hong Yuan , Shuxin Ouyang , Tierui Zhang . 层状双金属氢氧化物的层间阴离子对衍生的Ni-Al₂O₃催化剂光热催化CO₂甲烷化反应的影响. Acta Physico-Chimica Sinica, 2025, 41(1): 2309002-. doi: 10.3866/PKU.WHXB202309002
4. [4]
  Wen YANG , Didi WANG , Ziyi HUANG , Yaping ZHOU , Yanyan FENG . La promoted hydrotalcite derived Ni-based catalysts: In situ preparation and CO₂ methanation performance. Chinese Journal of Inorganic Chemistry, 2024, 40(3): 561-570. doi: 10.11862/CJIC.20230276
5. [5]
  Siming Bian , Sijie Luo , Junjie Ou . Application of van Deemter Equation in Instrumental Analysis Teaching: A New Type of Core-Shell Stationary Phase. University Chemistry, 2025, 40(3): 381-386. doi: 10.12461/PKU.DXHX202406087
6. [6]
  Xuejie Wang , Guoqing Cui , Congkai Wang , Yang Yang , Guiyuan Jiang , Chunming Xu . 碳基催化剂催化有机液体氢载体脱氢研究进展. Acta Physico-Chimica Sinica, 2025, 41(5): 100044-. doi: 10.1016/j.actphy.2024.100044
7. [7]
  Yuanyin Cui , Jinfeng Zhang , Hailiang Chu , Lixian Sun , Kai Dai . Rational Design of Bismuth Based Photocatalysts for Solar Energy Conversion. Acta Physico-Chimica Sinica, 2024, 40(12): 2405016-. doi: 10.3866/PKU.WHXB202405016
8. [8]
  Xue Liu , Lipeng Wang , Luling Li , Kai Wang , Wenju Liu , Biao Hu , Daofan Cao , Fenghao Jiang , Junguo Li , Ke Liu . Cu基和Pt基甲醇水蒸气重整制氢催化剂研究进展. Acta Physico-Chimica Sinica, 2025, 41(5): 100049-. doi: 10.1016/j.actphy.2025.100049
9. [9]
  Jiaxuan Zuo , Kun Zhang , Jing Wang , Xifei Li . 锂离子电池Ni-Co-Mn基正极材料前驱体的形核调控及机制. Acta Physico-Chimica Sinica, 2025, 41(1): 2404042-. doi: 10.3866/PKU.WHXB202404042
10. [10]
  Endong YANG , Haoze TIAN , Ke ZHANG , Yongbing LOU . Efficient oxygen evolution reaction of CuCo₂O₄/NiFe-layered bimetallic hydroxide core-shell nanoflower sphere arrays. Chinese Journal of Inorganic Chemistry, 2024, 40(5): 930-940. doi: 10.11862/CJIC.20230369
11. [11]
  Fan Wu , Wenchang Tian , Jin Liu , Qiuting Zhang , YanHui Zhong , Zian Lin . Core-Shell Structured Covalent Organic Framework-Coated Silica Microspheres as Mixed-Mode Stationary Phase for High Performance Liquid Chromatography. University Chemistry, 2024, 39(11): 319-326. doi: 10.12461/PKU.DXHX202403031
12. [12]
  Zhiquan Zhang , Baker Rhimi , Zheyang Liu , Min Zhou , Guowei Deng , Wei Wei , Liang Mao , Huaming Li , Zhifeng Jiang . Insights into the Development of Copper-based Photocatalysts for CO₂ Conversion. Acta Physico-Chimica Sinica, 2024, 40(12): 2406029-. doi: 10.3866/PKU.WHXB202406029
13. [13]
  Fangxuan Liu , Ziyan Liu , Guowei Zhou , Tingting Gao , Wenyu Liu , Bin Sun . Hollow structured photocatalysts. Acta Physico-Chimica Sinica, 2025, 41(7): 100071-. doi: 10.1016/j.actphy.2025.100071
14. [14]
  Jiapei Zou , Junyang Zhang , Xuming Wu , Cong Wei , Simin Fang , Yuxi Wang . A Comprehensive Experiment Based on Electrocatalytic Nitrate Reduction into Ammonia: Synthesis, Characterization, Performance Exploration, and Applicable Design of Copper-based Catalysts. University Chemistry, 2024, 39(6): 373-382. doi: 10.3866/PKU.DXHX202312081
15. [15]
  Xi YANG , Chunxiang CHANG , Yingpeng XIE , Yang LI , Yuhui CHEN , Borao WANG , Ludong YI , Zhonghao HAN . Co-catalyst Ni₃N supported Al-doped SrTiO₃: Synthesis and application to hydrogen evolution from photocatalytic water splitting. Chinese Journal of Inorganic Chemistry, 2025, 41(3): 440-452. doi: 10.11862/CJIC.20240371
16. [16]
  Lei Shi . Nucleophilicity and Electrophilicity of Radicals. University Chemistry, 2024, 39(11): 131-135. doi: 10.3866/PKU.DXHX202402018
17. [17]
  Jiahe LIU , Gan TANG , Kai CHEN , Mingda ZHANG . Effect of low-temperature electrolyte additives on low-temperature performance of lithium cobaltate batteries. Chinese Journal of Inorganic Chemistry, 2025, 41(4): 719-728. doi: 10.11862/CJIC.20250023
18. [18]
  Qiangqiang SUN , Pengcheng ZHAO , Ruoyu WU , Baoyue CAO . Multistage microporous bifunctional catalyst constructed by P-doped nickel-based sulfide ultra-thin nanosheets for energy-efficient hydrogen production from water electrolysis. Chinese Journal of Inorganic Chemistry, 2024, 40(6): 1151-1161. doi: 10.11862/CJIC.20230454
19. [19]
  Yanan Liu , Yufei He , Dianqing Li . Preparation of Highly Dispersed LDHs-based Catalysts and Testing of Nitro Compound Reduction Performance: A Comprehensive Chemical Experiment for Research Transformation. University Chemistry, 2024, 39(8): 306-313. doi: 10.3866/PKU.DXHX202401081
20. [20]
  Hong RAO , Yang HU , Yicong MA , Chunxin LÜ , Wei ZHONG , Lihua DU . Synthesis and in vitro anticancer activity of phenanthroline-functionalized nitrogen heterocyclic carbene homo- and heterobimetallic silver/gold complexes. Chinese Journal of Inorganic Chemistry, 2024, 40(12): 2429-2437. doi: 10.11862/CJIC.20240275

Get Citation

PDF

XML

Metrics

PDF Downloads(0)
Abstract views(1658)
HTML views(155)

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

NiO@SiO2 core-shell catalyst for low-temperature methanation of syngas in slurry reactor

Metrics

通讯作者: 陈斌, bchen63@163.com

NiO@SiO₂ core-shell catalyst for low-temperature methanation of syngas in slurry reactor