Citation: Du Mengfan, Chen Qirong, Zou Yu, Yang Kaimeng, Hu Jianxin, Meng Xiangfu. Molten Salt Synthesis of TiO₂ Nanosheet with Rich Oxygen Vacancies and Its Photocatalytic Activity[J]. Chemistry, ;2020, 83(3): 232-239. shu

Molten Salt Synthesis of TiO₂ Nanosheet with Rich Oxygen Vacancies and Its Photocatalytic Activity

1.
Department of Chemistry, Capital Normal University, Beijing, 100048
2.
Beijing Academy of Science and Technology, Beijing Center for Physical and Chemical Analysis, Beijing, 100089

Corresponding author: Meng Xiangfu, xfmeng@cnu.edu.cn
Received Date: 25 November 2019
Accepted Date: 28 December 2019

Figures(10)

The positive effects of oxygen vacancy defects on the performance of semiconductor materials are attracting increasing attention. Herein, blue TiO₂ nanosheet with rich oxygen vacancies was successfully synthesized via a one-step molten salt method using the hydrolysis product of TiCl₄ in trifluoroacetic acid as a precursor. Due to the low oxygen partial pressure of the molten salt, the lattice oxygen of TiO₂ was consumed during calcination, leading to a large amount of oxygen vacancies and Ti³⁺. UV-Visible diffuse reflectance spectroscopy showed that the band gap of blue TiO₂ nanosheets was reduced to 2.69 eV, and the light adsorption range was extended from the ultraviolet region to the visible region. The as-prepared blue TiO₂ nanosheets exhibits excellent photocatalytic activity, and the photodegradation rate of rhodamine B is 47.3 times that of pure TiO₂ under full-spectrum light irradiation. At the same time, the formed lattice fluorine doping can effectively stabilize the oxygen vacancies and greatly improve the separation efficiency of the photogenerated carriers. This work provides a new insight for constructing oxygen vacancies in semiconductor oxide materials.
- Titanium dioxide,
- Molten salt,
- Oxygen vacancies,
- Defects,
- Photocatalytic activity
1. [1]
  Fang W Z, Dappozze F, Guillard C, et al. J. Phys. Chem. C, 2017, 121(32):17068~17076.
2. [2]
  Peper J, Vinyard D, Brudvig G, et al. J. Am. Chem. Soc., 2017, 139(8):2868~2871.
3. [3]
  Fang W Z, Khrouz L, Zhou Y, et al. Phys. Chem. Chem. Phys., 2017, 19(21):13875~13881.
4. [4]
  Wang G M, Wang H Y, Ling Y C, et al. Nano Lett., 2011, 11(7):3026~3033.
5. [5]
  Xing M Y, Zhang J L, Chen F, et al. Chem. Commun., 2011, 47(17):4947~4949.
6. [6]
  Grabstanowicz L R, Gao S M, Li T, et al. Inorg. Chem., 2013, 52(7):3884~3890.
7. [7]
  Jiang W Y, Bai S, Wang L M, et al. Small, 2016, 12(12):1640~1648.
8. [8]
  Kong L N, Jiang Z Q, Wang C H, et al. Appl. Mater. Interf., 2015, 7(14):7752~7758.
9. [9]
  Zhang H, Cai J M, Wang Y T, et al. Appl. Catal. B, 2018, 220:126~136.
10. [10]
  Yang Y R, Gao P, Ren X C, et al. Appl. Catal. B, 2017, 218:751~757.
11. [11]
  Zhang X C, Hu W Y, Zhang K F, et al. ACS Sustain. Chem. Eng., 2017, 5(8):6894~6901.
12. [12]
  Yu C L, Wu Z, Liu R Y, et al. Appl. Catal. B, 2017, 209:1~11.
13. [13]
  Shannon R D, Pask J A. J. Am. Ceram. Soc., 1965, 48(8):391~198.
14. [14]
  Liu L J, Jiang Y Q, Zhao H L, et al. ACS Catal., 2016, 6(2):1097~1108.
15. [15]
  Pei Z X, Weng S X, Liu P. Appl. Catal. B, 2016, 180:463~470.
16. [16]
  Wang Y, Zhang H M, Han Y H, et al. Chem. Commun., 2011, 47(10):2829~2831.
17. [17]
  Eder D, Motta M S, Windle A H. Acta Mater., 2010, 58(13):4406~4413.
18. [18]
  Sarkar D, Ishchuk S, Taffa D H, et al. J. Phys. Chem. C, 2016, 120(7):3853~3862.
19. [19]
  Xu L M, Ming L F, Chen F. ChemCatChem, 2015, 7(12):1797~1800.
20. [20]
  Xing M Y, Zhang J L, Chen F, et al. Chem. Commun., 2011, 47(17):4947~4949.
21. [21]
  Zhou Y, Chen C H, Wang N N, et al. J. Phys. Chem. C, 2016, 120(11):6116~6124.
22. [22]
  Fang W Z, Xing M Y, Zhang J L. Appl. Catal. B, 2014, 160~161:240~246.
23. [23]
  Samsudin E M, Hamid S B A, Juan J C, et al. Appl. Surf. Sci., 2016, 365:57~68.
24. [24]
  Zou Y, Yang K M, Chen Q R, et al. RSC Adv., 2018, 8(64):36819~36825.
25. [25]
  Dai K, Lu L H, Liu Q, et al. Dalton Transac., 2014, 43(5):2202~2210.
26. [26]
  Yu J C, Yu J G, Ho W K, et al. Chem. Mater., 2002, 14(9):3808~3816.
27. [27]
  Zhu Q, Wang X J, Jiang J, et al. J. Phys. Chem. C, 2017, 121(41):22806~22814.
28. [28]
  Zhang N, Li X Y, Ye H C, et al. J. Am. Chem. Soc., 2016, 138(28):8928~8935.
29. [29]
  Kim W, Tachikawa T, Moon G H, et al. Angew. Chem. Int. Ed., 2014, 53(51):14036~14041.
30. [30]
  Liu B S, Cheng K, Nie S C, et al. J. Phys. Chem. C., 2017, 121(36):19836~19848
31. [31]
  Cushing S K, Meng F, Zhang J, et al. ACS Catal., 2017, 7(3):1742~1748.
32. [32]
  Lan Y P, Sohn H Y, Mohassab Y, et al. J. Am. Ceram. Soc., 2017, 100:1863~1875.
1. [1]
  Chunchun Wang , Changjun You , Ke Rong , Chuqi Shen , Fang Yang , Shijie Li . An S-Scheme MIL-101(Fe)-on-BiOCl Heterostructure with Oxygen Vacancies for Boosting Photocatalytic Removal of Cr(Ⅵ). Acta Physico-Chimica Sinica, 2024, 40(7): 2307045-0. doi: 10.3866/PKU.WHXB202307045
2. [2]
  Weicheng Feng , Jingcheng Yu , Yilan Yang , Yige Guo , Geng Zou , Xiaoju Liu , Zhou Chen , Kun Dong , Yuefeng Song , Guoxiong Wang , Xinhe Bao . Regulating the High Entropy Component of Double Perovskite for High-Temperature Oxygen Evolution Reaction. Acta Physico-Chimica Sinica, 2024, 40(6): 2306013-0. doi: 10.3866/PKU.WHXB202306013
3. [3]
  Wenlong LI , Xinyu JIA , Jie LING , Mengdan MA , Anning ZHOU . Photothermal catalytic CO₂ hydrogenation over a Mg-doped In₂O_3-x catalyst. Chinese Journal of Inorganic Chemistry, 2024, 40(5): 919-929. doi: 10.11862/CJIC.20230421
4. [4]
  Bing LIU , Huang ZHANG , Hongliang HAN , Changwen HU , Yinglei ZHANG . Visible light degradation of methylene blue from water by triangle Au@TiO₂ mesoporous catalyst. Chinese Journal of Inorganic Chemistry, 2024, 40(5): 941-952. doi: 10.11862/CJIC.20230398
5. [5]
  Shengjuan Huo , Xiaoyan Zhang , Xiangheng Li , Xiangning Li , Tianfang Chen , Yuting Shen . Unveiling the Marvels of Titanium: Popularizing Multifunctional Colored Titanium Product Films. University Chemistry, 2024, 39(5): 184-192. doi: 10.3866/PKU.DXHX202310127
6. [6]
  Ruiqing LIU , Wenxiu LIU , Kun XIE , Yiran LIU , Hui CHENG , Xiaoyu WANG , Chenxu TIAN , Xiujing LIN , Xiaomiao FENG . Three-dimensional porous titanium nitride as a highly efficient sulfur host. Chinese Journal of Inorganic Chemistry, 2024, 40(5): 867-876. doi: 10.11862/CJIC.20230441
7. [7]
  Qiang Zhang , Yuanbiao Huang , Rong Cao . Imidazolium-Based Materials for CO₂ Electroreduction. Acta Physico-Chimica Sinica, 2024, 40(4): 2306040-0. doi: 10.3866/PKU.WHXB202306040
8. [8]
  Hailang JIA , Pengcheng JI , Hongcheng LI . Preparation and performance of nickel doped ruthenium dioxide electrocatalyst for oxygen evolution. Chinese Journal of Inorganic Chemistry, 2025, 41(8): 1632-1640. doi: 10.11862/CJIC.20240398
9. [9]
  Xiaoning TANG , Shu XIA , Jie LEI , Xingfu YANG , Qiuyang LUO , Junnan LIU , An XUE . Fluorine-doped MnO₂ with oxygen vacancy for stabilizing Zn-ion batteries. Chinese Journal of Inorganic Chemistry, 2024, 40(9): 1671-1678. doi: 10.11862/CJIC.20240149
10. [10]
  Zhiquan Zhang , Baker Rhimi , Zheyang Liu , Min Zhou , Guowei Deng , Wei Wei , Liang Mao , Huaming Li , Zhifeng Jiang . Insights into the Development of Copper-Based Photocatalysts for CO₂ Conversion. Acta Physico-Chimica Sinica, 2024, 40(12): 2406029-0. doi: 10.3866/PKU.WHXB202406029
11. [11]
  Jianan Hong , Chenyu Xu , Yan Liu , Changqi Li , Menglin Wang , Yanwei Zhang . Decoding the interfacial competition between hydrogen evolution and CO₂ reduction via edge-active-site modulation in photothermal catalysis. Acta Physico-Chimica Sinica, 2025, 41(9): 100099-0. doi: 10.1016/j.actphy.2025.100099
12. [12]
  Runhua Chen , Qiong Wu , Jingchen Luo , Xiaolong Zu , Shan Zhu , Yongfu Sun . Defective Ultrathin Two-Dimensional Materials for Photo-/Electrocatalytic CO₂ Reduction: Fundamentals and Perspectives. Acta Physico-Chimica Sinica, 2025, 41(3): 2308052-0. doi: 10.3866/PKU.WHXB202308052
13. [13]
  Zhangyong LIU , Lihui XU , Yue YANG , Liming WANG , Hong PAN , Xinzhe HUANG , Xueqiang FU , Yingxiu ZHANG , Meiran DOU , Meng WANG , Yi TENG . Preparation and photocatalytic performance of Cs_xWO₃/TiO₂ based on full spectral response. Chinese Journal of Inorganic Chemistry, 2025, 41(7): 1445-1464. doi: 10.11862/CJIC.20240345
14. [14]
  Yanhui XUE , Shaofei CHAO , Man XU , Qiong WU , Fufa WU , Sufyan Javed Muhammad . Construction of high energy density hexagonal hole MXene aqueous supercapacitor by vacancy defect control strategy. Chinese Journal of Inorganic Chemistry, 2024, 40(9): 1640-1652. doi: 10.11862/CJIC.20240183
15. [15]
  Bing WEI , Jianfan ZHANG , Zhe CHEN . Research progress in fine tuning of bimetallic nanocatalysts for electrocatalytic carbon dioxide reduction. Chinese Journal of Inorganic Chemistry, 2025, 41(3): 425-439. doi: 10.11862/CJIC.20240201
16. [16]
  Wenjuan Tan , Yong Ye , Xiujuan Sun , Bei Liu , Jiajia Zhou , Hailong Liao , Xiulin Wu , Rui Ding , Enhui Liu , Ping Gao . Building P-Poor Ni₂P and P-Rich CoP₃ Heterojunction Structure with Cation Vacancy for Enhanced Electrocatalytic Hydrazine and Urea Oxidation. Acta Physico-Chimica Sinica, 2024, 40(6): 2306054-0. doi: 10.3866/PKU.WHXB202306054
17. [17]
  Bizhu Shao , Huijun Dong , Yunnan Gong , Jianhua Mei , Fengshi Cai , Jinbiao Liu , Dichang Zhong , Tongbu Lu . Metal-Organic Framework-Derived Nickel Nanoparticles for Efficient CO₂ Electroreduction in Wide Potential Windows. Acta Physico-Chimica Sinica, 2024, 40(4): 2305026-0. doi: 10.3866/PKU.WHXB202305026
18. [18]
  Yan Kong , Wei Wei , Lekai Xu , Chen Chen . Electrochemical Synthesis of Organonitrogen Compounds from N-integrated CO₂ Reduction Reaction. Acta Physico-Chimica Sinica, 2024, 40(8): 2307049-0. doi: 10.3866/PKU.WHXB202307049
19. [19]
  Hui-Ying Chen , Hao-Lin Zhu , Pei-Qin Liao , Xiao-Ming Chen . Integration of Ru(Ⅱ)-Bipyridyl and Zinc(Ⅱ)-Porphyrin Moieties in a Metal-Organic Framework for Efficient Overall CO₂ Photoreduction. Acta Physico-Chimica Sinica, 2024, 40(4): 2306046-0. doi: 10.3866/PKU.WHXB202306046
20. [20]
  Jingyi Xie , Qianxi Lü , Weizhen Qiao , Chenyu Bu , Yusheng Zhang , Xuejun Zhai , Renqing Lü , Yongming Chai , Bin Dong . Enhancing Cobalt―Oxygen Bond to Stabilize Defective Co₂MnO₄ in Acidic Oxygen Evolution. Acta Physico-Chimica Sinica, 2024, 40(3): 2305021-0. doi: 10.3866/PKU.WHXB202305021

Get Citation

PDF

XML

Metrics

PDF Downloads(24)
Abstract views(3239)
HTML views(1098)

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

Molten Salt Synthesis of TiO2 Nanosheet with Rich Oxygen Vacancies and Its Photocatalytic Activity

Metrics

通讯作者: 陈斌, bchen63@163.com

Molten Salt Synthesis of TiO₂ Nanosheet with Rich Oxygen Vacancies and Its Photocatalytic Activity