Citation: SUN Meng-Meng, CAO Yi, LAN Li, ZOU Sha, FANG Zhi-Tao, CHEN Yao-Qiang. Selective Catalytic Oxidation of Ammonia to Nitrogen over Iron and Copper Bimetallic Catalysts[J]. Acta Physico-Chimica Sinica, ;2014, 30(12): 2300-2306. doi: 10.3866/PKU.WHXB201409291 shu

Selective Catalytic Oxidation of Ammonia to Nitrogen over Iron and Copper Bimetallic Catalysts

1.
Key Laboratory of Green Chemistry & Technology of the Ministry of Education, College of Chemistry, Sichuan University, Chengdu 610064, P. R. China

Received Date: 16 June 2014
Available Online: 29 September 2014
Fund Project: 国家自然科学基金(21173153) (21173153) 国家高技术研究发展计划项目(863) (2013AA065304) (863) (2013AA065304)四川省科技厅科技支撑项目(2011GZ0035, 2012FZ0008)资助 (2011GZ0035, 2012FZ0008)

Iron and copper bimetallic catalysts with fixed total contents of copper and iron were prepared by a co-impregnation method, and then used for selective catalytic oxidation of ammonia to nitrogen. The properties of the catalysts were characterized by N₂ adsorption-desorption, H₂ temperature-programmed reduction (H₂- TPR), NH₃ temperature-programmed desorption (NH₃-TPD), X-ray diffraction (XRD), and X-ray photoelectron spectroscopy (XPS). The iron and copper bimetallic catalysts exhibited od activity and high selectivity of N₂ at the gas hourly space velocity (GHSV) of 100000 h^-1. The activity and N₂ selectivity in the low temperature range increased with increasing Cu loading, whereas in the high temperature range (above 400 ℃) the selectivity of N₂ was directly related to the content of iron. The highest NH₃ conversion was achieved at about 350℃ for Fe_0.25Cu_0.75/ZSM-5, and the N₂ selectivity was up to 97% at 300 ℃. On the other hand, the extremely high N₂ selectivity about 98% was obtained over Fe_0.75Cu_0.25/ZSM-5 at 500 ℃. In addition, N₂O as the by-product and greenhouse gas was obtained in very low amounts for all the catalysts. The characterization results showed that the activity was influenced by the acid content and the amounts of copper species. Moreover, the highly reducing capacity could improve the N₂ selectivity.
- Iron,
- Copper,
- Molecular sieve,
- Ammonia oxidation reaction,
- N₂ selectivity,
- Catalyst
1. [1]
  
  (1) Krupa, S. V. Environ. Pollut. 2003, 124, 179. doi: 10.1016/S0269-7491(02)00434-7
2. [2]
  (2) Hung, C. M. Powder Technol. 2009, 196, 56. doi: 10.1016/j.powtec.2009.07.001
3. [3]
  (3) Akah, A.; Cundy, C.; Garforth, A. Appl. Catal. B: Environ. 2005, 59, 221. doi: 10.1016/j.apcatb.2004.10.020
4. [4]
  (4) Sobczyk, D. P.; Hensen, E. J. M.; Jong, A. M. D.; Santen, R. A. V. Top. Catal. 2003, 23, 1. doi: 10.1023/A:1024834800948
5. [5]
  (5) Hung, C. M. Powder Technol. 2010, 200, 78. doi: 10.1016/j.powtec.2010.02.014
6. [6]
  (6) Broek, A. C. M. V. D.; Grondelle, J. V.; Santen, R. A. V. J. Catal.1999, 185, 297. doi: 10.1006/jcat.1999.2506
7. [7]
  (7) Gang, L.; Anderson, B. G.; Grondelle, J. V.; Santen, R. A. V. Appl. Catal. B: Environ. 2003, 40, 101. doi: 10.1016/S0926-3373(02)00129-7
8. [8]
  (8) Zhang, L.; Zhang, C. B.; He, H. J. Catal. 2009, 261, 101. doi: 10.1016/j.jcat.2008.11.004
9. [9]
  (9) Zhang, L.; He, H. J. Catal. 2009, 268, 18. doi: 10.1016/j.jcat.2009.08.011
10. [10]
  (10) Long, R. Q.; Yang, R. T. J. Catal. 2002, 207, 158. doi: 10.1006/jcat.2002.3545
11. [11]
  (11) Cui, X. Z.; Zhou, J.; Ye, Z. Q.; Chen, H. R.; Li, L.; Ruan, M. L.; Shi, J. L. J. Catal. 2010, 270, 310. doi: 10.1016/j.jcat.2010.01.005
12. [12]
  (12) Qi, G. S.; Yang, R. T. Appl. Catal. A: Gen. 2005, 287, 25. doi: 10.1016/j.apcata.2005.03.006
13. [13]
  (13) Qi, G. S.; Gatt, J. E.; Yang, R. T. J. Catal. 2004, 226, 120. doi: 10.1016/j.jcat.2004.05.023
14. [14]
  (14) Long, R. Q.; Yang, R. T. J. Catal. 2001, 201, 145. doi: 10.1006/jcat.2001.3234
15. [15]
  (15) Gang, L.; Grondelle, J. V.; Anderson, B. G.; Santen, R. A. V. J. Catal. 1999, 186, 100. doi: 10.1006/jcat.1999.2524
16. [16]
  (16) Metkar, P. S.; Harold, M. P.; Balakotaiah, V. Appl. Catal. B: Environ. 2012, 111, 67.
17. [17]
  (17) Song, S. Q.; Jiang, S. J. Appl. Catal. B: Environ. 2012, 117, 346.
18. [18]
  (18) Liang, C. X.; Li, X. Y.; Qu, Z. P.; Tade, M.; Liu, S. M. Appl. Surf. Sci. 2012, 258, 3738. doi: 10.1016/j.apsusc.2011.12.017
19. [19]
  (19) Shi, L.; Yu, T.;Wang, X. Q.;Wang, J.; Shen, M. Q. Acta Phys. -Chim. Sin. 2013, 29, 1550. [石琳, 于铁, 王欣全, 王军, 沈美庆. 物理化学学报, 2013, 29, 1550.] doi: 10.3866/PKU.WHXB201304283
20. [20]
  (20) Rauscher, M.; Kesore, K.; Mönnig, R.; Schwieger,W.; Tißler, A.; Turek, T. Appl. Catal. A: Gen. 1999, 184, 249. doi: 10.1016/S0926-860X(99)00088-5
21. [21]
  (21) Zhang, T.; Liu, J.;Wang, D. X.; Zhao, Z.;Wei, Y. C.; Cheng, K.; Jiang, G. Y.; Duan, A. J. Appl. Catal. B: Environ. 2014, 148, 520.
22. [22]
  (22) Wang, J.; Huang, Y.; Yu, T.; Zhu, S. C.; Shen, M. Q.; Li,W.; Wang, J. Q. Catal. Sci. Technol. 2014, 4, 3004. doi: 10.1039/c4cy00451e
23. [23]
  (23) Brüggemann, T. C.; Keil, F. J. J. Phys. Chem. C 2009, 113, 13860.
24. [24]
  (24) Wagner, C. D.; Riggs,W. M.; Davis, L. E.; Moulder, J. F. Handbook of X-ray Photoelectron Spectroscopy, 1st ed.; Muilenberg, G. E. Ed. Perkin-Elmer Corporation: Eden Prairie, Minnesota, USA, 1979.
25. [25]
  (25) Gurgul, J.; ??tka, K.; Hnat, I.; Rynkowski, J.; Dzwigaj, S. Microporous Mesoporous Mat. 2013, 168, 1. doi: 10.1016/j.micromeso.2012.09.015
26. [26]
  (26) Lisi, L.; Pirone, R.; Russo, G.; Stanzione, V. Chem. Eng. J. 2009, 154, 341. doi: 10.1016/j.cej.2009.04.025
27. [27]
  (27) Long, R. Q.; Yang, R. T. J. Catal. 2001, 198, 20. doi: 10.1006/jcat.2000.3118
1. [1]
  Xudong Lv , Tao Shao , Junyan Liu , Meng Ye , Shengwei Liu . Paired Electrochemical CO₂ Reduction and HCHO Oxidation for the Cost-Effective Production of Value-Added Chemicals. Acta Physico-Chimica Sinica, 2024, 40(5): 2305028-0. doi: 10.3866/PKU.WHXB202305028
2. [2]
  Pei Li , Yuenan Zheng , Zhankai Liu , An-Hui Lu . Boron-Containing MFI Zeolite: Microstructure Control and Its Performance of Propane Oxidative Dehydrogenation. Acta Physico-Chimica Sinica, 2025, 41(4): 2406012-0. doi: 10.3866/PKU.WHXB202406012
3. [3]
  Peng YUE , Liyao SHI , Jinglei CUI , Huirong ZHANG , Yanxia GUO . Effects of Ce and Mn promoters on the selective oxidation of ammonia over V₂O₅/TiO₂ catalyst. Chinese Journal of Inorganic Chemistry, 2025, 41(2): 293-307. doi: 10.11862/CJIC.20240210
4. [4]
  Bing WEI , Jianfan ZHANG , Zhe CHEN . Research progress in fine tuning of bimetallic nanocatalysts for electrocatalytic carbon dioxide reduction. Chinese Journal of Inorganic Chemistry, 2025, 41(3): 425-439. doi: 10.11862/CJIC.20240201
5. [5]
  Wentao Xu , Xuyan Mo , Yang Zhou , Zuxian Weng , Kunling Mo , Yanhua Wu , Xinlin Jiang , Dan Li , Tangqi Lan , Huan Wen , Fuqin Zheng , Youjun Fan , Wei Chen . Bimetal Leaching Induced Reconstruction of Water Oxidation Electrocatalyst for Enhanced Activity and Stability. Acta Physico-Chimica Sinica, 2024, 40(8): 2308003-0. doi: 10.3866/PKU.WHXB202308003
6. [6]
  Wenke ZHENG , Ce LIU , Wei CHEN , Hongshan KE , Fanlong ZENG , Yibo LEI , Anyang LI , Wenyuan WANG . Synthesis and bonding analysis of low-coordinate Fe and Cr complexes with ultra-bulky silylamino groups. Chinese Journal of Inorganic Chemistry, 2025, 41(7): 1285-1293. doi: 10.11862/CJIC.20250095
7. [7]
  Zhanggui DUAN , Yi PEI , Shanshan ZHENG , Zhaoyang WANG , Yongguang WANG , Junjie WANG , Yang HU , Chunxin LÜ , Wei ZHONG . Preparation of UiO-66-NH₂ supported copper catalyst and its catalytic activity on alcohol oxidation. Chinese Journal of Inorganic Chemistry, 2024, 40(3): 496-506. doi: 10.11862/CJIC.20230317
8. [8]
  Jingkun Yu , Xue Yong , Ang Cao , Siyu Lu . Bi-Layer Single Atom Catalysts Boosted Nitrate-to-Ammonia Electroreduction with High Activity and Selectivity. Acta Physico-Chimica Sinica, 2024, 40(6): 2307015-0. doi: 10.3866/PKU.WHXB202307015
9. [9]
  Zhiquan Zhang , Baker Rhimi , Zheyang Liu , Min Zhou , Guowei Deng , Wei Wei , Liang Mao , Huaming Li , Zhifeng Jiang . Insights into the Development of Copper-Based Photocatalysts for CO₂ Conversion. Acta Physico-Chimica Sinica, 2024, 40(12): 2406029-0. doi: 10.3866/PKU.WHXB202406029
10. [10]
  Jiapei Zou , Junyang Zhang , Xuming Wu , Cong Wei , Simin Fang , Yuxi Wang . A Comprehensive Experiment Based on Electrocatalytic Nitrate Reduction into Ammonia: Synthesis, Characterization, Performance Exploration, and Applicable Design of Copper-based Catalysts. University Chemistry, 2024, 39(6): 373-382. doi: 10.3866/PKU.DXHX202312081
11. [11]
  Wang Wang , Yucheng Liu , Shengli Chen . Use of NiFe Layered Double Hydroxide as Electrocatalyst in Oxygen Evolution Reaction: Catalytic Mechanisms, Electrode Design, and Durability. Acta Physico-Chimica Sinica, 2024, 40(2): 2303059-0. doi: 10.3866/PKU.WHXB202303059
12. [12]
  .
  CCS Chemistry | 超分子活化底物为自由基促进高效选择性光催化氧化
  . CCS Chemistry, 2025, 7(10.31635/ccschem.025.202405229): -.
13. [13]
  Feifei Yang , Wei Zhou , Chaoran Yang , Tianyu Zhang , Yanqiang Huang . Enhanced Methanol Selectivity in CO₂ Hydrogenation by Decoration of K on MoS₂ Catalyst. Acta Physico-Chimica Sinica, 2024, 40(7): 2308017-0. doi: 10.3866/PKU.WHXB202308017
14. [14]
  Zhaoyu Wen , Na Han , Yanguang Li . Recent Progress towards the Production of H₂O₂ by Electrochemical Two-Electron Oxygen Reduction Reaction. Acta Physico-Chimica Sinica, 2024, 40(2): 2304001-0. doi: 10.3866/PKU.WHXB202304001
15. [15]
  Haoyu Sun , Dun Li , Yuanyuan Min , Yingying Wang , Yanyun Ma , Yiqun Zheng , Hongwen Huang . Hierarchical Palladium-Copper-Silver Porous Nanoflowers as Efficient Electrocatalysts for CO₂ Reduction to C₂₊ Products. Acta Physico-Chimica Sinica, 2024, 40(6): 2307007-0. doi: 10.3866/PKU.WHXB202307007
16. [16]
  Xue Dong , Xiaofu Sun , Shuaiqiang Jia , Shitao Han , Dawei Zhou , Ting Yao , Min Wang , Minghui Fang , Haihong Wu , Buxing Han . Electrochemical CO₂ Reduction to C₂₊ Products with Ampere-Level Current on Carbon-Modified Copper Catalysts. Acta Physico-Chimica Sinica, 2025, 41(3): 2404012-0. doi: 10.3866/PKU.WHXB202404012
17. [17]
  Yufang GAO , Nan HOU , Yaning LIANG , Ning LI , Yanting ZHANG , Zelong LI , Xiaofeng LI . Nano-thin layer MCM-22 zeolite: Synthesis and catalytic properties of trimethylbenzene isomerization reaction. Chinese Journal of Inorganic Chemistry, 2024, 40(6): 1079-1087. doi: 10.11862/CJIC.20240036
18. [18]
  Dong Xiang , Kunzhen Li , Kanghua Miao , Ran Long , Yujie Xiong , Xiongwu Kang . Amine-Functionalized Copper Catalysts: Hydrogen Bonding Mediated Electrochemical CO₂ Reduction to C₂ Products and Superior Rechargeable Zn-CO₂ Battery Performance. Acta Physico-Chimica Sinica, 2024, 40(8): 2308027-0. doi: 10.3866/PKU.WHXB202308027
19. [19]
  Lina Guo , Ruizhe Li , Chuang Sun , Xiaoli Luo , Yiqiu Shi , Hong Yuan , Shuxin Ouyang , Tierui Zhang . Effect of Interlayer Anions in Layered Double Hydroxides on the Photothermocatalytic CO₂ Methanation of Derived Ni-Al₂O₃ Catalysts. Acta Physico-Chimica Sinica, 2025, 41(1): 100002-0. doi: 10.3866/PKU.WHXB202309002
20. [20]
  Qing Li , Guangxun Zhang , Yuxia Xu , Yangyang Sun , Huan Pang . P-Regulated Hierarchical Structure Ni₂P Assemblies toward Efficient Electrochemical Urea Oxidation. Acta Physico-Chimica Sinica, 2024, 40(9): 2308045-0. doi: 10.3866/PKU.WHXB202308045

Get Citation

PDF

XML

Metrics

PDF Downloads(424)
Abstract views(775)
HTML views(18)

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142