Citation: LI Qiang, DOU Tao, HUO Quan, XU Qing-Hu, NG Yan-Jun, PAN Hui-Fang. Physicochemical Properties and Activities of Hydrocarbon Catalytic Cracking of β-Zeolite with Different Silica-Alumina Ratios[J]. Acta Physico-Chimica Sinica, ;2008, 24(07): 1192-1198. doi: 10.3866/PKU.WHXB20080713 shu

Physicochemical Properties and Activities of Hydrocarbon Catalytic Cracking of β-Zeolite with Different Silica-Alumina Ratios

1.
CNPC Key Laboratory of Catalysis, China University of Petroleum, Beijing 102249, P. R. China; Institute of Special Chemical, Taiyuan University of Technology, Taiyuan 030042, P. R. China

Received Date: 3 January 2008
Available Online: 9 April 2008

High-crystallized β-zeolites with different silica-alumina molar ratios were successfully synthesized in extremely dense aqueous system using tetraethylammonium hydroxide (TEAOH) as template and solid silica gel as silica source, respectively. The silica-alumina molar ratios in the initial gels were 30, 60, 150, 300, 500, and pure silica, respectively, which were consistent with those in so-prepared samples determined by chemical method and XRF analysis. Subsequently, the physicochemical properties of samples were characterized by XRD, FT-IR, SEM, NH3-TPD, and N2-adsorption analysis. The results showed that the extent of dealumination was changed obviously and the acid content was decreased significantly in the low silica β-zeolite with highest aluminium content after hydrothermal treatment. The high silica or pure silica β-zeolites could not display higher hydrothermal stability partly due to their small grain sizes. After hydrothermal treatment, the medium silica-alumina ratio zeolite beta could remain higher acid amount and showed better hydrothermal stability. The effect of β-zeolites with different n(SiO2)/n(Al2O3) ratios as an active additive on cracking performance has been investigated. It was found that β-zeolite could increase the activity of cracking catalyst and improve the performance of resistance to carbon deposition. As β-zeolite with n(SiO2)/n(Al2O3) molar ratio of 150 was added, the cracking catalyst exhibited the higher cracking gasoline yield and lower carbon deposition.
- Silica-alumina ratio; β-Zeolite; Physicochemical property; Catalytic cracking
1. [1]
  Xingyang LI , Tianju LIU , Yang GAO , Dandan ZHANG , Yong ZHOU , Meng PAN . A superior methanol-to-propylene catalyst: Construction via synergistic regulation of pore structure and acidic property of high-silica ZSM-5 zeolite. Chinese Journal of Inorganic Chemistry, 2024, 40(7): 1279-1289. doi: 10.11862/CJIC.20240026
2. [2]
  Ping ZHANG , Chenchen ZHAO , Xiaoyun CUI , Bing XIE , Yihan LIU , Haiyu LIN , Jiale ZHANG , Yu'nan CHEN . Preparation and adsorption-photocatalytic performance of ZnAl@layered double oxides. Chinese Journal of Inorganic Chemistry, 2024, 40(10): 1965-1974. doi: 10.11862/CJIC.20240014
3. [3]
  Meng Lin , Hanrui Chen , Congcong Xu . Preparation and Study of Photo-Enhanced Electrocatalytic Oxygen Evolution Performance of ZIF-67/Copper(I) Oxide Composite: A Recommended Comprehensive Physical Chemistry Experiment. University Chemistry, 2024, 39(4): 163-168. doi: 10.3866/PKU.DXHX202308117
4. [4]
  Jiao CHEN , Yi LI , Yi XIE , Dandan DIAO , Qiang XIAO . Vapor-phase transport of MFI nanosheets for the fabrication of ultrathin b-axis oriented zeolite membranes. Chinese Journal of Inorganic Chemistry, 2024, 40(3): 507-514. doi: 10.11862/CJIC.20230403
5. [5]
  Jiali CHEN , Guoxiang ZHAO , Yayu YAN , Wanting XIA , Qiaohong LI , Jian ZHANG . Machine learning exploring the adsorption of electronic gases on zeolite molecular sieves. Chinese Journal of Inorganic Chemistry, 2025, 41(1): 155-164. doi: 10.11862/CJIC.20240408
6. [6]
  Shu'e Song , Xiaokui Wang , Yongmei Liu , Wanchun Zhu , Hong Yuan , Fuping Tian , Yunshan Bai , Yunchao Li , Li Wang , Zhongyun Wu , Yuan Chun , Jianrong Zhang , Shuyong Zhang . Suggestions on Operating Specifications of Physical Chemistry Experiment: Measurement of Viscosity, Density and Optical Properties. University Chemistry, 2025, 40(5): 148-156. doi: 10.12461/PKU.DXHX202503026
7. [7]
  Fuping Tian , Yunshan Bai , Wanchun Zhu , Yufeng Li , Yongmei Liu , Shu'e Song , Hong Yuan , Zhongyun Wu , Li Wang , Xiaokui Wang , Yuan Chun , Jianrong Zhang , Shuyong Zhang . Suggestions on Operating Specifications of Physical Chemistry Experiment: Measurement of Thermal Properties. University Chemistry, 2025, 40(5): 157-164. doi: 10.12461/PKU.DXHX202503054
8. [8]
  Yunchao Li , Hong Yuan , Yuan Chun , Xiaokui Wang , Fuping Tian , Yunshan Bai , Yongmei Liu , Wanchun Zhu , Shu'e Song , Zhongyun Wu , Li Wang , Yufeng Li , Jianrong Zhang , Shuyong Zhang . Suggestions on Operating Specifications of Physical Chemistry Experiment: Measurement of Electrical Properties. University Chemistry, 2025, 40(5): 165-177. doi: 10.12461/PKU.DXHX202503055
9. [9]
  Jun Huang , Pengfei Nie , Yongchao Lu , Jiayang Li , Yiwen Wang , Jianyun Liu . Efficient adsorption of hardness ions by a mordenite-loaded, nitrogen-doped porous carbon nanofiber cathode in capacitive deionization. Acta Physico-Chimica Sinica, 2025, 41(7): 100066-. doi: 10.1016/j.actphy.2025.100066
10. [10]
  Yuan Chun , Yongmei Liu , Fuping Tian , Hong Yuan , Shu'e Song , Wanchun Zhu , Yunchao Li , Zhongyun Wu , Xiaokui Wang , Yunshan Bai , Li Wang , Jianrong Zhang , Shuyong Zhang . Suggestions on Operating Specifications of Physical Chemistry Experiment: Measurement of Colloidal and Surface Chemical Properties, Molecular Structure and Properties. University Chemistry, 2025, 40(5): 178-188. doi: 10.12461/PKU.DXHX202503053
11. [11]
  Zhiwen HU , Weixia DONG , Qifu BAO , Ping LI . Low-temperature synthesis of tetragonal BaTiO₃ for piezocatalysis. Chinese Journal of Inorganic Chemistry, 2024, 40(5): 857-866. doi: 10.11862/CJIC.20230462
12. [12]
  Guimin ZHANG , Wenjuan MA , Wenqiang DING , Zhengyi FU . Synthesis and catalytic properties of hollow AgPd bimetallic nanospheres. Chinese Journal of Inorganic Chemistry, 2024, 40(5): 963-971. doi: 10.11862/CJIC.20230293
13. [13]
  Zhuo WANG , Junshan ZHANG , Shaoyan YANG , Lingyan ZHOU , Yedi LI , Yuanpei LAN . Preparation and photocatalytic performance of CeO₂-reduced graphene oxide by thermal decomposition. Chinese Journal of Inorganic Chemistry, 2024, 40(9): 1708-1718. doi: 10.11862/CJIC.20240067
14. [14]
  Zijian Jiang , Yuang Liu , Yijian Zong , Yong Fan , Wanchun Zhu , Yupeng Guo . Preparation of Nano Zinc Oxide by Microemulsion Method and Study on Its Photocatalytic Activity. University Chemistry, 2024, 39(5): 266-273. doi: 10.3866/PKU.DXHX202311101
15. [15]
  Zhiwen HU , Ping LI , Yulong YANG , Weixia DONG , Qifu BAO . Morphology effects on the piezocatalytic performance of BaTiO₃. Chinese Journal of Inorganic Chemistry, 2025, 41(2): 339-348. doi: 10.11862/CJIC.20240172
16. [16]
  Wen YANG , Didi WANG , Ziyi HUANG , Yaping ZHOU , Yanyan FENG . La promoted hydrotalcite derived Ni-based catalysts: In situ preparation and CO₂ methanation performance. Chinese Journal of Inorganic Chemistry, 2024, 40(3): 561-570. doi: 10.11862/CJIC.20230276
17. [17]
  Siyu HOU , Weiyao LI , Jiadong LIU , Fei WANG , Wensi LIU , Jing YANG , Ying ZHANG . Preparation and catalytic performance of magnetic nano iron oxide by oxidation co-precipitation method. Chinese Journal of Inorganic Chemistry, 2024, 40(8): 1577-1582. doi: 10.11862/CJIC.20230469
18. [18]
  Haiyuan Wang , Yiming Tang , Haoran Guo , Guohui Chen , Yajing Sun , Chao Zhao , Zhen Zhang . Comprehensive Chemistry Experimental Teaching Design Based on the Integration of Science and Education: Preparation and Catalytic Properties of Silver Nanomaterials. University Chemistry, 2024, 39(10): 219-228. doi: 10.12461/PKU.DXHX202404067
19. [19]
  Xin Han , Zhihao Cheng , Jinfeng Zhang , Jie Liu , Cheng Zhong , Wenbin Hu . Design of Amorphous High-Entropy FeCoCrMnBS (Oxy) Hydroxides for Boosting Oxygen Evolution Reaction. Acta Physico-Chimica Sinica, 2025, 41(4): 100033-. doi: 10.3866/PKU.WHXB202404023
20. [20]
  Xinzhe HUANG , Lihui XU , Yue YANG , Liming WANG , Zhangyong LIU , Zhongjian WANG . Preparation and visible light responsive photocatalytic properties of BiSbO₄/BiOBr. Chinese Journal of Inorganic Chemistry, 2025, 41(2): 284-292. doi: 10.11862/CJIC.20240212

Get Citation

PDF

XML

Metrics

PDF Downloads(2139)
Abstract views(3506)
HTML views(56)

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

Address：Zhongguancun North First Street 2,100190 Beijing, PR China Tel: +86-010-82449177-888

DownLoad: Full-Size Img PowerPoint

Return