Citation: Hu Ji-Ming, Meng Hui-Min, Zhang Jian-Qing, Cao Chu-Nan. Aging Performances of Ti Based IrO₂＋Ta₂O₅ Anodes in Sulfuric Acid During Electrolysis[J]. Acta Physico-Chimica Sinica, ;2002, 18(01): 14-20. doi: 10.3866/PKU.WHXB20020104 shu

Aging Performances of Ti Based IrO₂＋Ta₂O₅ Anodes in Sulfuric Acid During Electrolysis

1.
Department of Chemistry,Zhejiang University,Hangzhou　310027;Corrosion and Protection Center,University of Science and Technology Beijing,Beijing 100083;State Key Laboratory For Corrosion and Protection,Institute of Metal Research,Chinese Academy of Sciences,Shenyang　110016

Received Date: 29 June 2001
Available Online: 15 January 2002

Physicochemical and electrochemical performances of long service life Ti/70％IrO230％Ta2O5 (mole fraction) anodes prepared at 450 ℃ have been investigated over the whole electrolysis time in H2SO4 solution .The results showed that the whole electrolysis process of this anode could be divided into three stages consisting of ‘active',‘stable' and ‘deactive' ones.In the first two stages,the dissolution of coated oxides was dominated (with preferential loss of IrO2 component).It was found that,in these two stages,the preferential orientations of (110) and (101) planes in IrO2 rutile decreased with the electrolysis time,and that of (002) plane increased,while the preferential orientations remained to be stabilized in the ‘deactive' region.This indicated that the loss mechanism of the catalyst coatings was changed.Electrochemical impedance spectroscopy (EIS) measurements showed a slight increase in oxygen evolution reaction resistance of the oxide catalysts while a sharp rise in totally physical impedance of the whole anode in the ‘deactive' region.Xray diffraction analysis (XRD) showed that the intensity of TiO2 rutile reflections increased with the electrolysis time,with a sharp increasing in ‘deactive' region.According to the experimental results the degradation mechanism for long service life Ti based coating anodes has been proposed.
- Degradation mechanism;Titanium anodes;IrO₂;Ta₂O₅
1. [1]
  Xiaoning TANG , Shu XIA , Jie LEI , Xingfu YANG , Qiuyang LUO , Junnan LIU , An XUE . Fluorine-doped MnO₂ with oxygen vacancy for stabilizing Zn-ion batteries. Chinese Journal of Inorganic Chemistry, 2024, 40(9): 1671-1678. doi: 10.11862/CJIC.20240149
2. [2]
  Qiang Zhang , Yuanbiao Huang , Rong Cao . Imidazolium-Based Materials for CO₂ Electroreduction. Acta Physico-Chimica Sinica, 2024, 40(4): 2306040-0. doi: 10.3866/PKU.WHXB202306040
3. [3]
  Yanhui Guo , Li Wei , Zhonglin Wen , Chaorong Qi , Huanfeng Jiang . Recent Progress on Conversion of Carbon Dioxide into Carbamates. Acta Physico-Chimica Sinica, 2024, 40(4): 2307004-0. doi: 10.3866/PKU.WHXB202307004
4. [4]
  Zhiquan Zhang , Baker Rhimi , Zheyang Liu , Min Zhou , Guowei Deng , Wei Wei , Liang Mao , Huaming Li , Zhifeng Jiang . Insights into the Development of Copper-Based Photocatalysts for CO₂ Conversion. Acta Physico-Chimica Sinica, 2024, 40(12): 2406029-0. doi: 10.3866/PKU.WHXB202406029
5. [5]
  Hailang JIA , Pengcheng JI , Hongcheng LI . Preparation and performance of nickel doped ruthenium dioxide electrocatalyst for oxygen evolution. Chinese Journal of Inorganic Chemistry, 2025, 41(8): 1632-1640. doi: 10.11862/CJIC.20240398
6. [6]
  Caixia Lin , Zhaojiang Shi , Yi Yu , Jianfeng Yan , Keyin Ye , Yaofeng Yuan . Ideological and Political Design for the Electrochemical Synthesis of Benzoxathiazine Dioxide Experiment. University Chemistry, 2024, 39(2): 61-66. doi: 10.3866/PKU.DXHX202309005
7. [7]
  Bing WEI , Jianfan ZHANG , Zhe CHEN . Research progress in fine tuning of bimetallic nanocatalysts for electrocatalytic carbon dioxide reduction. Chinese Journal of Inorganic Chemistry, 2025, 41(3): 425-439. doi: 10.11862/CJIC.20240201
8. [8]
  Jianan Hong , Chenyu Xu , Yan Liu , Changqi Li , Menglin Wang , Yanwei Zhang . Decoding the interfacial competition between hydrogen evolution and CO₂ reduction via edge-active-site modulation in photothermal catalysis. Acta Physico-Chimica Sinica, 2025, 41(9): 100099-0. doi: 10.1016/j.actphy.2025.100099
9. [9]
  Bizhu Shao , Huijun Dong , Yunnan Gong , Jianhua Mei , Fengshi Cai , Jinbiao Liu , Dichang Zhong , Tongbu Lu . Metal-Organic Framework-Derived Nickel Nanoparticles for Efficient CO₂ Electroreduction in Wide Potential Windows. Acta Physico-Chimica Sinica, 2024, 40(4): 2305026-0. doi: 10.3866/PKU.WHXB202305026
10. [10]
  Yan Kong , Wei Wei , Lekai Xu , Chen Chen . Electrochemical Synthesis of Organonitrogen Compounds from N-integrated CO₂ Reduction Reaction. Acta Physico-Chimica Sinica, 2024, 40(8): 2307049-0. doi: 10.3866/PKU.WHXB202307049
11. [11]
  Xiaofei Liu , He Wang , Li Tao , Weimin Ren , Xiaobing Lu , Wenzhen Zhang . Electrocarboxylation of Benzylic Phosphates and Phosphinates with Carbon Dioxide. Acta Physico-Chimica Sinica, 2024, 40(9): 2307008-0. doi: 10.3866/PKU.WHXB202307008
12. [12]
  Jie ZHAO , Huili ZHANG , Xiaoqing LU , Zhaojie WANG . Theoretical calculations of CO₂ capture and separation by functional groups modified 2D covalent organic framework. Chinese Journal of Inorganic Chemistry, 2025, 41(2): 275-283. doi: 10.11862/CJIC.20240213
13. [13]
  Wei HE , Jing XI , Tianpei HE , Na CHEN , Quan YUAN . Application of solar-driven inorganic semiconductor-microbe hybrids in carbon dioxide fixation and biomanufacturing. Chinese Journal of Inorganic Chemistry, 2025, 41(1): 35-44. doi: 10.11862/CJIC.20240364
14. [14]
  Hui-Ying Chen , Hao-Lin Zhu , Pei-Qin Liao , Xiao-Ming Chen . Integration of Ru(Ⅱ)-Bipyridyl and Zinc(Ⅱ)-Porphyrin Moieties in a Metal-Organic Framework for Efficient Overall CO₂ Photoreduction. Acta Physico-Chimica Sinica, 2024, 40(4): 2306046-0. doi: 10.3866/PKU.WHXB202306046
15. [15]
  Jiaxin Su , Jiaqi Zhang , Shuming Chai , Yankun Wang , Sibo Wang , Yuanxing Fang . Optimizing Poly(heptazine imide) Photoanodes Using Binary Molten Salt Synthesis for Water Oxidation Reaction. Acta Physico-Chimica Sinica, 2024, 40(12): 2408012-0. doi: 10.3866/PKU.WHXB202408012
16. [16]
  Chi Zhang , Yi Xu , Xiaopeng Guo , Zian Jie , Ling Li . 五彩斑斓的秘密——物质显色机理. University Chemistry, 2025, 40(6): 266-275. doi: 10.12461/PKU.DXHX202407061
17. [17]
  Mingxuan Qi , Lanyu Jin , Honghe Yao , Zipeng Xu , Teng Cheng , Qi Chen , Cheng Zhu , Yang Bai . Recent progress on electrical failure and stability of perovskite solar cells under reverse bias. Acta Physico-Chimica Sinica, 2025, 41(8): 100088-0. doi: 10.1016/j.actphy.2025.100088
18. [18]
  Jichao XU , Ming HU , Xichang CHEN , Chunhui WANG , Leichen WANG , Lingyi ZHOU , Xing HE , Xiamin CHENG , Su JING . Construction and hydrogen peroxide-activated chemodynamic activity of ferrocene?benzoselenadiazole conjugate. Chinese Journal of Inorganic Chemistry, 2025, 41(8): 1495-1504. doi: 10.11862/CJIC.20250144
19. [19]
  Zhaoyu Wen , Na Han , Yanguang Li . Recent Progress towards the Production of H₂O₂ by Electrochemical Two-Electron Oxygen Reduction Reaction. Acta Physico-Chimica Sinica, 2024, 40(2): 2304001-0. doi: 10.3866/PKU.WHXB202304001
20. [20]
  Fan JIA , Wenbao XU , Fangbin LIU , Haihua ZHANG , Hongbing FU . Synthesis and electroluminescence properties of Mn²⁺ doped quasi-two-dimensional perovskites (PEA)₂Pb_yMn_1-yBr₄. Chinese Journal of Inorganic Chemistry, 2024, 40(6): 1114-1122. doi: 10.11862/CJIC.20230473

Get Citation

PDF

XML

Metrics

PDF Downloads(2536)
Abstract views(3154)
HTML views(36)

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

Address：Zhongguancun North First Street 2,100190 Beijing, PR China Tel: +86-010-82449177-888

DownLoad: Full-Size Img PowerPoint

Return

Aging Performances of Ti Based IrO2＋Ta2O5 Anodes in Sulfuric Acid During Electrolysis

Metrics

通讯作者: 陈斌, bchen63@163.com

Aging Performances of Ti Based IrO₂＋Ta₂O₅ Anodes in Sulfuric Acid During Electrolysis