Citation: Yuan You-Zhu, Zhang Yu, Chen Zhong, Zhang Hong-Bin, Cai Qi-Rui. Structure and Hydroformylation Performance of Supported Aqueous-phase Rh Catalyst[J]. Acta Physico-Chimica Sinica, ;1998, 14(11): 1013-1019. doi: 10.3866/PKU.WHXB19981110 shu

Structure and Hydroformylation Performance of Supported Aqueous-phase Rh Catalyst

1.
Department of Chemistry,Institute of Physical Chemistry,State Key Laboratory for Physical Chemistry of Solid Surface,Xiamen University,Xiamen 361005

Received Date: 9 February 1998
Available Online: 15 November 1998

The catalytic activity of hydroformylation of 1-hexene over SiO2-supported TPPTSRh(acac)(CO)2 (SAPC) was found to be evidently promoted when a proper amount of water-vapor was introduced into the reactant. Characterization results by using MAS NMR 31p spectra revealed that there were three types of phosphine species in the as-prepared SAPC: uncoordinated ligand TPPTS (over 70 mol%), surface complex {Rh(CO)(TPPTS)2} (chemical shift at δ=32.4, about 15 mol%), and unknown (about 10 mol%). By pre-treatment at 373 K for 2 under dry-snygas or at 333 K for 2 h under wet-syngas, the amount of phosphine species of the surface complex{Rh(CO)(TPPTS)2} was slightly increased to 20-30mol%, accompanying a few changes in ratios of the other phsophine species. When the SAPC was pre-treated at 373 K for 2 h under wet-syngas, however, the phosphine species at chemical shift of 32.4 was increased by over 40 mol% due to the in-situ formation of the surface complex {Rh(CO)(TPPTS)2}. It was found that the peak at δ=32.4 was also a principal one in the MAS NMR 31P spectra of the working SAPC, which demonstrated that the surface complex of {Rh(CO)(TPPTS)2 } would be a catalytic active species for olefin hydroformyaltion. After hydroformylation for 43 h, the deactivation of the catalyst occurred, corresponding to the observations of a broadness in peak ascribed to the surface complex of {An(CO)(TPPTS)z} in the MAS NMR 31P spectra, indicating that there existed de-coordination of the surface complex and oxidation of the ligand TPPTS during the reaction. The results suggest that a proper amount of water-vapor was able to accelerate the formation of active Rh-complex on the catalyst surface and thus increase the catalytic activity, whereas, it could be inevitably to cause the de-coordination of the surface complex and the oxidation of phosphine ligand under the reaction condition, hence leading to the deactivation of the catalyst.
- Hydroformylation,
- Supported aqueous-phase catalyst,
- MAS NMR31P spectroscopy,
- 1-hexene
1. [1]
  Jingzhao Cheng , Shiyu Gao , Bei Cheng , Kai Yang , Wang Wang , Shaowen Cao . 4-氨基-1H-咪唑-5-甲腈修饰供体-受体型氮化碳光催化剂的构建及其高效光催化产氢研究. Acta Physico-Chimica Sinica, 2024, 40(11): 2406026-. doi: 10.3866/PKU.WHXB202406026
2. [2]
  Bing LIU , Huang ZHANG , Hongliang HAN , Changwen HU , Yinglei ZHANG . Visible light degradation of methylene blue from water by triangle Au@TiO₂ mesoporous catalyst. Chinese Journal of Inorganic Chemistry, 2024, 40(5): 941-952. doi: 10.11862/CJIC.20230398
3. [3]
  Asif Hassan Raza , Shumail Farhan , Zhixian Yu , Yan Wu . 用于高效制氢的双S型ZnS/ZnO/CdS异质结构光催化剂. Acta Physico-Chimica Sinica, 2024, 40(11): 2406020-. doi: 10.3866/PKU.WHXB202406020
4. [4]
  Xi YANG , Chunxiang CHANG , Yingpeng XIE , Yang LI , Yuhui CHEN , Borao WANG , Ludong YI , Zhonghao HAN . Co-catalyst Ni₃N supported Al-doped SrTiO₃: Synthesis and application to hydrogen evolution from photocatalytic water splitting. Chinese Journal of Inorganic Chemistry, 2025, 41(3): 440-452. doi: 10.11862/CJIC.20240371
5. [5]
  Xuejie Wang , Guoqing Cui , Congkai Wang , Yang Yang , Guiyuan Jiang , Chunming Xu . 碳基催化剂催化有机液体氢载体脱氢研究进展. Acta Physico-Chimica Sinica, 2025, 41(5): 100044-. doi: 10.1016/j.actphy.2024.100044
6. [6]
  Juan WANG , Zhongqiu WANG , Qin SHANG , Guohong WANG , Jinmao LI . NiS and Pt as dual co-catalysts for the enhanced photocatalytic H₂ production activity of BaTiO₃ nanofibers. Chinese Journal of Inorganic Chemistry, 2024, 40(9): 1719-1730. doi: 10.11862/CJIC.20240102
7. [7]
  Qingqing SHEN , Xiangbowen DU , Kaicheng QIAN , Zhikang JIN , Zheng FANG , Tong WEI , Renhong LI . Self-supporting Cu/α-FeOOH/foam nickel composite catalyst for efficient hydrogen production by coupling methanol oxidation and water electrolysis. Chinese Journal of Inorganic Chemistry, 2024, 40(10): 1953-1964. doi: 10.11862/CJIC.20240028
8. [8]
  Shuang Yang , Qun Wang , Caiqin Miao , Ziqi Geng , Xinran Li , Yang Li , Xiaohong Wu . Ideological and Political Education Design for Research-Oriented Experimental Course of Highly Efficient Hydrogen Production from Water Electrolysis in Aerospace Perspective. University Chemistry, 2024, 39(11): 269-277. doi: 10.12461/PKU.DXHX202403044
9. [9]
  Xue Liu , Lipeng Wang , Luling Li , Kai Wang , Wenju Liu , Biao Hu , Daofan Cao , Fenghao Jiang , Junguo Li , Ke Liu . Cu基和Pt基甲醇水蒸气重整制氢催化剂研究进展. Acta Physico-Chimica Sinica, 2025, 41(5): 100049-. doi: 10.1016/j.actphy.2025.100049
10. [10]
  Zhuoming Liang , Ming Chen , Zhiwen Zheng , Kai Chen . Multidimensional Studies on Ketone-Enol Tautomerism of 1,3-Diketones By ¹H NMR. University Chemistry, 2024, 39(7): 361-367. doi: 10.3866/PKU.DXHX202311029
11. [11]
  Zhanggui DUAN , Yi PEI , Shanshan ZHENG , Zhaoyang WANG , Yongguang WANG , Junjie WANG , Yang HU , Chunxin LÜ , Wei ZHONG . Preparation of UiO-66-NH₂ supported copper catalyst and its catalytic activity on alcohol oxidation. Chinese Journal of Inorganic Chemistry, 2024, 40(3): 496-506. doi: 10.11862/CJIC.20230317
12. [12]
  Qiangqiang SUN , Pengcheng ZHAO , Ruoyu WU , Baoyue CAO . Multistage microporous bifunctional catalyst constructed by P-doped nickel-based sulfide ultra-thin nanosheets for energy-efficient hydrogen production from water electrolysis. Chinese Journal of Inorganic Chemistry, 2024, 40(6): 1151-1161. doi: 10.11862/CJIC.20230454
13. [13]
  Juntao Yan , Liang Wei . 2D S-Scheme Heterojunction Photocatalyst. Acta Physico-Chimica Sinica, 2024, 40(10): 2312024-. doi: 10.3866/PKU.WHXB202312024
14. [14]
  Yue Zhao , Yanfei Li , Tao Xiong . Copper Hydride-Catalyzed Nucleophilic Additions of Unsaturated Hydrocarbons to Aldehydes and Ketones. University Chemistry, 2024, 39(4): 280-285. doi: 10.3866/PKU.DXHX202309001
15. [15]
  Zelong LIANG , Shijia QIN , Pengfei GUO , Hang XU , Bin ZHAO . Synthesis and electrocatalytic CO₂ reduction performance of metal-organic framework catalysts loaded with silver particles. Chinese Journal of Inorganic Chemistry, 2025, 41(1): 165-173. doi: 10.11862/CJIC.20240409
16. [16]
  Yuchen Zhou , Huanmin Liu , Hongxing Li , Xinyu Song , Yonghua Tang , Peng Zhou . Designing thermodynamically stable noble metal single-atom photocatalysts for highly efficient non-oxidative conversion of ethanol into high-purity hydrogen and value-added acetaldehyde. Acta Physico-Chimica Sinica, 2025, 41(6): 100067-. doi: 10.1016/j.actphy.2025.100067
17. [17]
  Yu Wang , Haiyang Shi , Zihan Chen , Feng Chen , Ping Wang , Xuefei Wang . Hollow AgPt@Pt core-shell cocatalyst with electron-rich Pt^δ^- shell for boosting selectivity of photocatalytic H₂O₂ production for faceted BiVO₄. Acta Physico-Chimica Sinica, 2025, 41(7): 100081-. doi: 10.1016/j.actphy.2025.100081
18. [18]
  Hailang JIA , Hongcheng LI , Pengcheng JI , Yang TENG , Mingyun GUAN . Preparation and performance of N-doped carbon nanotubes composite Co₃O₄ as oxygen reduction reaction electrocatalysts. Chinese Journal of Inorganic Chemistry, 2024, 40(4): 693-700. doi: 10.11862/CJIC.20230402
19. [19]
  Fangxuan Liu , Ziyan Liu , Guowei Zhou , Tingting Gao , Wenyu Liu , Bin Sun . Hollow structured photocatalysts. Acta Physico-Chimica Sinica, 2025, 41(7): 100071-. doi: 10.1016/j.actphy.2025.100071
20. [20]
  Yi YANG , Shuang WANG , Wendan WANG , Limiao CHEN . Photocatalytic CO₂ reduction performance of Z-scheme Ag-Cu₂O/BiVO₄ photocatalyst. Chinese Journal of Inorganic Chemistry, 2024, 40(5): 895-906. doi: 10.11862/CJIC.20230434

Get Citation

PDF

XML

Metrics

PDF Downloads(2167)
Abstract views(3448)
HTML views(14)

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

Address：Zhongguancun North First Street 2,100190 Beijing, PR China Tel: +86-010-82449177-888

DownLoad: Full-Size Img PowerPoint

Return