Citation: GENG Tong-Mou. Synthesis and Thermoreversible Swelling Behavior of Hydrophobically Modified Intelligent Hydrogels P(NIPA-co-DiAB)[J]. Chinese Journal of Applied Chemistry, ;2010, 27(6): 637-641. doi: 10.3724/SP.J.1095.2010.90504 shu

Synthesis and Thermoreversible Swelling Behavior of Hydrophobically Modified Intelligent Hydrogels P(NIPA-co-DiAB)

GENG Tong-Mou

School of Chemistry and Chemical Engineering, Anqing Teachers College, Anqing 246011

Received Date: 20 July 2009
Revised Date: 16 November 2009

Temperature-sensitive hydrogels P(NIPA-co-DiAB) with aromatic group as hydrophobe was were prepared by free radical micellar crosslinking copolymerization with N-isopropyl acrylamide(NIPA) and N,N-dially benzylamine(DiAB) as comonomers,N,N-methylene-bis-acrylamide(BIS) as crosslinker,sodium dodecyl sulfate(SDS) as surfactant and ammonium persulfate(APS)-tetramethylethylenediamine(TMEDA) as initiator system.The influence of DiAB content on the properties of the hydrogels was discussed.In the initial swelling stage,the swelling behavior of the four hydrogels changed from Fickian kinetics to non-Fickian with increasing of molar fraction x(DiAB) from 0 to 3%.While x(DiAB) values were 0,1%,2% and 3%,the equilibrium swelling ratio SR0 of P(NIPA-co-DiAB) hydrogels were 63.6,93.5,141.6 and 167.4 in distilled water;63.1,71.0,59.0 and 77.5 in a 0.01 mol/L SDS solution;37.6,42.2,44.1 and 60.0 in a 0.01mol/L CTAB solution;30.9,49.4,68.5 and 88.3 in a 0.01 mol/L Triton X-100 solution respectively.It was found that the SR0 values of P(NIPA-co-DiAB) hydrogels were greater than that of PNIPA,and the SR0 values of the four hydrogels in distilled water were greater than those in 0.01 mol/L aqueous surfactant solution.The volume phase transition temperature or lower critical swelling temperature(LCST) of PNIPA hydrogel was enhanced from 32.5℃ in distilled water to 35.4℃,45.6℃ or 80℃ in a 0.01 mol/L Triton X-100,CTAB or SDS solution,respectively.The LCST of P(NIPA-co-DiAB) hydrogels was increased from 32.0~32.5℃ in distilled water to 34.7~35.6℃,about 45.8~46.2℃ or 80℃ in a 0.01 mol/L Triton X-100,CTAB or SDS solution,respectively.It was shown that the LCST of P(NIPA-co-DiAB) hydrogels was increased by adding surfactant.The high volume transition temperature was essentially independent of hydrophobic comonomer DiAB content.
- N-isopropylacrylamide,
- N,N-dially benzylamine,
- hydrophobically modified polymers,
- intelligent hydrogel,
- surfactant
1. [1]
  Yukai Jiang , Yihan Wang , Yunkai Zhang , Yunping Wei , Ying Ma , Na Du . Characterization and Phase Diagram of Surfactant Lyotropic Liquid Crystal. University Chemistry, 2024, 39(4): 114-118. doi: 10.3866/PKU.DXHX202309033
2. [2]
  Yuena Yang , Xufang Hu , Yushan Liu , Yaya Kuang , Jian Ling , Qiue Cao , Chuanhua Zhou . The Realm of Smart Hydrogels. University Chemistry, 2024, 39(5): 172-183. doi: 10.3866/PKU.DXHX202310125
3. [3]
  Congying Lu , Fei Zhong , Zhenyu Yuan , Shuaibing Li , Jiayao Li , Jiewen Liu , Xianyang Hu , Liqun Sun , Rui Li , Meijuan Hu . Experimental Improvement of Surfactant Interface Chemistry: An Integrated Design for the Fusion of Experiment and Simulation. University Chemistry, 2024, 39(3): 283-293. doi: 10.3866/PKU.DXHX202308097
4. [4]
  Hongyun Liu , Jiarun Li , Xinyi Li , Zhe Liu , Jiaxuan Li , Cong Xiao . Course Ideological and Political Design of a Comprehensive Chemistry Experiment: Constructing a Visual Molecular Logic System Based on Intelligent Hydrogel Film Electrodes. University Chemistry, 2024, 39(2): 227-233. doi: 10.3866/PKU.DXHX202309070
5. [5]
  Yongmin Zhang , Shuang Guo , Mingyue Zhu , Menghui Liu , Sinong Li . Design and Improvement of Physicochemical Experiments Based on Problem-Oriented Learning: a Case Study of Liquid Surface Tension Measurement. University Chemistry, 2024, 39(2): 21-27. doi: 10.3866/PKU.DXHX202307026
6. [6]
  Caixia Lin , Ting Liu , Zhaojiang Shi , Hong Yan , Keyin Ye , Yaofeng Yuan . Innovative Experiment of Electrochemical Dearomative Spirocyclization of N-Acyl Sulfonamides. University Chemistry, 2025, 40(4): 359-366. doi: 10.12461/PKU.DXHX202406107
7. [7]
  Bao Jia , Yunzhe Ke , Shiyue Sun , Dongxue Yu , Ying Liu , Shuaishuai Ding . Innovative Experimental Teaching for the Preparation and Modification of Conductive Organic Polymer Thin Films in Undergraduate Courses. University Chemistry, 2024, 39(10): 271-282. doi: 10.12461/PKU.DXHX202404121
8. [8]
  Xiaofeng Xia , Jielian Zhu . Innovative Comprehensive Experimental Design: Synthesis of 6-Fluoro-N-benzoyl Tetrahydroquinoline. University Chemistry, 2024, 39(10): 344-352. doi: 10.12461/PKU.DXHX202405063
9. [9]
  Xi YANG , Chunxiang CHANG , Yingpeng XIE , Yang LI , Yuhui CHEN , Borao WANG , Ludong YI , Zhonghao HAN . Co-catalyst Ni₃N supported Al-doped SrTiO₃: Synthesis and application to hydrogen evolution from photocatalytic water splitting. Chinese Journal of Inorganic Chemistry, 2025, 41(3): 440-452. doi: 10.11862/CJIC.20240371
10. [10]
  Lirui Shen , Kun Liu , Ying Yang , Dongwan Li , Wengui Chang . Synthesis and Application of Decanedioic Acid-N-Hydroxysuccinimide Ester: Exploration of Teaching Reform in Comprehensive Applied Chemistry Experiment. University Chemistry, 2024, 39(8): 212-220. doi: 10.3866/PKU.DXHX202312035
11. [11]
  Junjun Huang , Ran Chen , Yajian Huang , Hang Zhang , Anran Zheng , Qing Xiao , Dan Wu , Ruxia Duan , Zhi Zhou , Fei He , Wei Yi . Discovery of an enantiopure N-[2-hydroxy-3-phenyl piperazine propyl]-aromatic carboxamide derivative as highly selective α_1D/1A-adrenoceptor antagonist and homology modelling. Chinese Chemical Letters, 2024, 35(11): 109594-. doi: 10.1016/j.cclet.2024.109594
12. [12]
  Yanglin Jiang , Mingqing Chen , Min Liang , Yige Yao , Yan Zhang , Peng Wang , Jianping Zhang . Experimental and Theoretical Investigations of Solvent Polarity Effect on ESIPT Mechanism in 4′-N,N-diethylamino-3-hydroxybenzoflavone. Acta Physico-Chimica Sinica, 2025, 41(2): 100012-. doi: 10.3866/PKU.WHXB202309027
13. [13]
  Xuejiao Wang , Suiying Dong , Kezhen Qi , Vadim Popkov , Xianglin Xiang . Photocatalytic CO₂ Reduction by Modified g-C₃N₄. Acta Physico-Chimica Sinica, 2024, 40(12): 2408005-. doi: 10.3866/PKU.WHXB202408005
14. [14]
  Zhongxin YU , Wei SONG , Yang LIU , Yuxue DING , Fanhao MENG , Shuju WANG , Lixin YOU . Fluorescence sensing on chlortetracycline of a Zn-coordination polymer based on mixed ligands. Chinese Journal of Inorganic Chemistry, 2024, 40(12): 2415-2421. doi: 10.11862/CJIC.20240304
15. [15]
  Xiao SANG , Qi LIU , Jianping LANG . Synthesis, structure, and fluorescence properties of Zn(Ⅱ) coordination polymers containing tetra-alkenylpyridine ligands. Chinese Journal of Inorganic Chemistry, 2024, 40(11): 2124-2132. doi: 10.11862/CJIC.20240158
16. [16]
  Xuefei Leng , Yanshai Wang , Hai Wang , Shengyang Tao . The In-Depth integration of “Industry-University-Research” in the Exploration and Practice of “Comprehensive Training in Polymer Engineering”. University Chemistry, 2025, 40(4): 66-71. doi: 10.12461/PKU.DXHX202405105
17. [17]
  Ruiying WANG , Hui WANG , Fenglan CHAI , Zhinan ZUO , Benlai WU . Three-dimensional homochiral Eu(Ⅲ) coordination polymer and its amino acid configuration recognition. Chinese Journal of Inorganic Chemistry, 2025, 41(5): 877-884. doi: 10.11862/CJIC.20250052
18. [18]
  Xiyuan Su , Zhenlin Hu , Ye Fan , Xianyuan Liu , Xianyong Lu . Change as You Want: Multi-Responsive Superhydrophobic Intelligent Actuation Material. University Chemistry, 2024, 39(5): 228-237. doi: 10.3866/PKU.DXHX202311059
19. [19]
  Tengjiao Wang , Tian Cheng , Rongjun Liu , Zeyi Wang , Yuxuan Qiao , An Wang , Peng Li . Conductive Hydrogel-based Flexible Electronic System: Innovative Experimental Design in Flexible Electronics. University Chemistry, 2024, 39(4): 286-295. doi: 10.3866/PKU.DXHX202309094
20. [20]
  Qiang Zhou , Pingping Zhu , Wei Shao , Wanqun Hu , Xuan Lei , Haiyang Yang . Innovative Experimental Teaching Design for 3D Printing High-Strength Hydrogel Experiments. University Chemistry, 2024, 39(6): 264-270. doi: 10.3866/PKU.DXHX202310064

Get Citation

PDF

XML

Metrics

PDF Downloads(3)
Abstract views(604)
HTML views(77)

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

Address：Zhongguancun North First Street 2,100190 Beijing, PR China Tel: +86-010-82449177-888

DownLoad: Full-Size Img PowerPoint

Return