Citation: Wen-Jun LI, Cheng-Hao FANG, Peng LÜ, Ke-Han YU, Zhong-Yue WANG, Wei WEI. Hydrothermal Synthesis and Electrochemical Properties of Na₃V₂(PO₄)₂O₂F Cathode for Sodium-Ion Batteries[J]. Chinese Journal of Inorganic Chemistry, ;2021, 37(7): 1204-1210. doi: 10.11862/CJIC.2021.141 shu

Hydrothermal Synthesis and Electrochemical Properties of Na₃V₂(PO₄)₂O₂F Cathode for Sodium-Ion Batteries

College of Electronic and Optical Engineering & College of Microelectronics, Nanjing University of Posts and Telecommunications, Nanjing 210023, China

Corresponding author: Zhong-Yue WANG, zywang@njupt.edu.cn Wei WEI, weiwei@njupt.edu.cn
Received Date: 22 January 2021
Revised Date: 23 April 2021

Figures(6)

Na₃V₂(PO₄)₂O₂F (NVPOF) sodium ion battery cathode materials were prepared by hydrothermal method, and the morphology, structure and electrochemical properties were investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM) and galvanostatic charge/discharge (GCD). The results showed that as-prepared pure phase NVPOF had regular tetraprisms morphology, which was 1~3 μm in length, 300 nm~1 μm in width, and the ratio of length to width was 2~3. NVPOF showed two pairs of stable charging and discharging platforms, the discharge specific capacities of NVPOF were 124.2 and 70.5 mAh·g^-1 at 0.2C and 2C at room temperature, and decreased to 105.8 and 59.6 mAh·g^-1 after 100 cycles, the capacity retention rate were about 85.2% and 84.5% while the Coulombic efficiency was more than 97%. In addition, NVPOF also had good electrochemical performance at low temperature (0 ℃). By coating reduced graphene oxide (rGO) to increase the electrical conductivity, NVPOF@rGO presented high specific discharge capacities of 124.4 and 88.4 mAh·g^-1 at 0.2C and 2C at room temperature. The specific capacity was still 78.7 mAh·g^-1 after 200 cycles at 2C, and the capacity retention rate was as high as 89% while the Coulomb efficiency was always about 99%, showing excellent rate and cycling performance.
- Na₃V₂(PO₄)₂O₂F,
- hydrothermal method,
- sodium ion battery,
- cycle performance
1. [1]
  Mukai K, Inoue T, Kato Y, Shirai S. ACS Omega, 2017, 2: 864-872 doi: 10.1021/acsomega.6b00551
2. [2]
  Sharma M, Murugavel S, Kaghazchi P. J. Power Sources, 2020, 469: 228348 doi: 10.1016/j.jpowsour.2020.228348
3. [3]
  Sevinc S, Tekin B, Ata A, Morcrette M, Perrot H, Sel O, Demir-Cakan R. J. Power Sources, 2019, 412: 55-62 doi: 10.1016/j.jpowsour.2018.11.035
4. [4]
  Zhang W, Liu Y T, Chen C J, Li Z, Huang Y H, Hu X L. Small, 2015, 11: 3822-3829 doi: 10.1002/smll.201500783
5. [5]
  Jiang Y, Yang Z Z, Li W H, Zeng L C, Pan F S, Wang M, Wei X, Hu G T, Gu L, Yu Y. Adv. Energy Mater. , 2015, 5: 1402104 doi: 10.1002/aenm.201402104
6. [6]
  Qi Y, Mu L, Zhao J, Hu Y S, Liu H, Dai S. Angew. Chem. Int. Ed. , 2015, 54: 9911-9916 doi: 10.1002/anie.201503188
7. [7]
  Bianchini M, Xiao P, Wang Y, Ceder G. Adv. Energy Mater. , 2017, 7: 1700514 doi: 10.1002/aenm.201700514
8. [8]
  Guo J Z, Wang P F, Wu X L, Zhang X H, Yan Q Y, Chen H, Zhang J P, Guo Y G. Adv. Mater. , 2017, 29: 1701968 doi: 10.1002/adma.201701968
9. [9]
  Song H Y, Eom K S. Adv. Funct. Mater. , 2020, 30: 2003086 doi: 10.1002/adfm.202003086
10. [10]
  Huang H, Yin S C, Nazar L F. Electrochem. Solid-State Lett. , 2001, 4: A170-A172 doi: 10.1149/1.1396695
11. [11]
  Yin Y M, Xiong F Y, Pei C Y, Xu Y N, An Q Y, Tan S S, Zhuang Z C, Sheng J Z, Li Q D, Mai L Q. Nano Energy, 2017, 41: 452-459 doi: 10.1016/j.nanoen.2017.09.056
12. [12]
  Jin H Y, Dong J, Uchaker E, Zhang Q F, Zhou X Z, Hou S E, Li J Y, Cao G Z. J. Mater. Chem. A, 2015, 3: 17563-17568 doi: 10.1039/C5TA03164H
13. [13]
  Wang Y Y, Hou B H, Guo J Z, Ning Q L, Pang W L, Wang J W, Lü C L, Wu X L. Adv. Energy Mater. , 2018, 8: 1703252 doi: 10.1002/aenm.201703252
14. [14]
  Gu Z Y, Guo J Z, Yang Y, Yu H Y, Xi X T, Zhao X X, Guan H Y, He X Y, Wu X L. Inorg. Chem. Front. , 2019, 6: 988-995 doi: 10.1039/C8QI01374H
15. [15]
  Sun H B, Guo J Z, Zhang Y, Wei T, Zhou Y X, Zhang L L, Wu X L, Huang Y, Luo W. ACS Appl. Mater. Interfaces, 2019, 11: 24192-24197 doi: 10.1021/acsami.9b07647
16. [16]
  Zhao X X, Gu Z Y, Li W H, Yang X, Guo J Z, Wu X L. Chem. Eur. J. , 2020, 26: 7823-7830 doi: 10.1002/chem.202000943
17. [17]
  Chen H, Mi H W, Sun L N, Zhang P X, Li Y L. ChemElectroChem, 2018, 5: 2593-2599 doi: 10.1002/celc.201800740
18. [18]
  Zhang L L, Liu J, Wei C, Sun P P, Gao L, Ding X K, Liang G, Yang X L, Huang Y H. ACS Appl. Mater. Interfaces, 2019, 12: 3670-3680
19. [19]
  Sauvage F, Quarez E, Tarascon J M, Baudrin E. Solid State Sci. , 2006, 8: 1215-1221 doi: 10.1016/j.solidstatesciences.2006.05.009
20. [20]
  GU Z Y, GUO J Z, YANG Y, LÜ H Y, ZHAO X X, XI X T, HE X Y, WU X L. Chinese J. Inorg. Chem. , 2018, 34: 1641-1648 doi: 10.11862/CJIC.2018.204
1. [1]
  Jianbao Mei , Bei Li , Shu Zhang , Dongdong Xiao , Pu Hu , Geng Zhang . Enhanced Performance of Ternary NASICON-Type Na_3.5-xMn_0.5V_1.5-xZr_x(PO₄)₃/C Cathodes for Sodium-Ion Batteries. Acta Physico-Chimica Sinica, 2024, 40(12): 2407023-. doi: 10.3866/PKU.WHXB202407023
2. [2]
  Yuyao Wang , Zhitao Cao , Zeyu Du , Xinxin Cao , Shuquan Liang . Research Progress of Iron-based Polyanionic Cathode Materials for Sodium-Ion Batteries. Acta Physico-Chimica Sinica, 2025, 41(4): 100035-. doi: 10.3866/PKU.WHXB202406014
3. [3]
  Yu Guo , Zhiwei Huang , Yuqing Hu , Junzhe Li , Jie Xu . 钠离子电池中铁基异质结构负极材料的最新研究进展. Acta Physico-Chimica Sinica, 2025, 41(3): 2311015-. doi: 10.3866/PKU.WHXB202311015
4. [4]
  Zhicheng JU , Wenxuan FU , Baoyan WANG , Ao LUO , Jiangmin JIANG , Yueli SHI , Yongli CUI . MOF-derived nickel-cobalt bimetallic sulfide microspheres coated by carbon: Preparation and long cycling performance for sodium storage. Chinese Journal of Inorganic Chemistry, 2025, 41(4): 661-674. doi: 10.11862/CJIC.20240363
5. [5]
  Zhuo WANG , Xiaotong LI , Zhipeng HU , Junqiao PAN . Three-dimensional porous carbon decorated with nano bismuth particles: Preparation and sodium storage properties. Chinese Journal of Inorganic Chemistry, 2025, 41(2): 267-274. doi: 10.11862/CJIC.20240223
6. [6]
  Ruofan Yin , Zhaoxin Guo , Rui Liu , Xian-Sen Tao . Ultrafast synthesis of Na₃V₂(PO₄)₃ cathode for high performance sodium-ion batteries. Chinese Chemical Letters, 2025, 36(2): 109643-. doi: 10.1016/j.cclet.2024.109643
7. [7]
  Qinjin DAI , Shan FAN , Pengyang FAN , Xiaoying ZHENG , Wei DONG , Mengxue WANG , Yong ZHANG . Performance of oxygen vacancy-rich V-doped MnO₂ for high-performance aqueous zinc ion battery. Chinese Journal of Inorganic Chemistry, 2025, 41(3): 453-460. doi: 10.11862/CJIC.20240326
8. [8]
  Pengyang FAN , Shan FAN , Qinjin DAI , Xiaoying ZHENG , Wei DONG , Mengxue WANG , Xiaoxiao HUANG , Yong ZHANG . Preparation and performance of rich 1T-MoS₂ nanosheets for high-performance aqueous zinc ion battery cathode materials. Chinese Journal of Inorganic Chemistry, 2025, 41(4): 675-682. doi: 10.11862/CJIC.20240339
9. [9]
  Zhuo Wang , Xue Bai , Kexin Zhang , Hongzhi Wang , Jiabao Dong , Yuan Gao , Bin Zhao . MOF模板法合成氮掺杂碳材料用于增强电化学钠离子储存和去除. Acta Physico-Chimica Sinica, 2025, 41(3): 2405002-. doi: 10.3866/PKU.WHXB202405002
10. [10]
  Liuyun Chen , Wenju Wang , Tairong Lu , Xuan Luo , Xinling Xie , Kelin Huang , Shanli Qin , Tongming Su , Zuzeng Qin , Hongbing Ji . 软模板法诱导Cu/Al₂O₃深孔道结构促进等离子催化CO₂加氢制二甲醚. Acta Physico-Chimica Sinica, 2025, 41(6): 100054-. doi: 10.1016/j.actphy.2025.100054
11. [11]
  Xiaotian ZHU , Fangding HUANG , Wenchang ZHU , Jianqing ZHAO . Layered oxide cathode for sodium-ion batteries: Surface and interface modification and suppressed gas generation effect. Chinese Journal of Inorganic Chemistry, 2025, 41(2): 254-266. doi: 10.11862/CJIC.20240260
12. [12]
  Zhuo WANG , Junshan ZHANG , Shaoyan YANG , Lingyan ZHOU , Yedi LI , Yuanpei LAN . Preparation and photocatalytic performance of CeO₂-reduced graphene oxide by thermal decomposition. Chinese Journal of Inorganic Chemistry, 2024, 40(9): 1708-1718. doi: 10.11862/CJIC.20240067
13. [13]
  Doudou Qin , Junyang Ding , Chu Liang , Qian Liu , Ligang Feng , Yang Luo , Guangzhi Hu , Jun Luo , Xijun Liu . Addressing Challenges and Enhancing Performance of Manganese-based Cathode Materials in Aqueous Zinc-Ion Batteries. Acta Physico-Chimica Sinica, 2024, 40(10): 2310034-. doi: 10.3866/PKU.WHXB202310034
14. [14]
  Qingtang ZHANG , Xiaoyu WU , Zheng WANG , Xiaomei WANG . Performance of nano Li₂FeSiO₄/C cathode material co-doped by potassium and chlorine ions. Chinese Journal of Inorganic Chemistry, 2024, 40(9): 1689-1696. doi: 10.11862/CJIC.20240115
15. [15]
  Han ZHANG , Jianfeng SUN , Jinsheng LIANG . Hydrothermal synthesis and luminescent properties of broadband near-infrared Na₃CrF₆ phosphor. Chinese Journal of Inorganic Chemistry, 2025, 41(2): 349-356. doi: 10.11862/CJIC.20240098
16. [16]
  Tong Su , Yue Wang , Qizhen Zhu , Mengyao Xu , Ning Qiao , Bin Xu . Multiple conductive network for KTi₂(PO₄)₃ anode based on MXene as a binder for high-performance potassium storage. Chinese Chemical Letters, 2024, 35(8): 109191-. doi: 10.1016/j.cclet.2023.109191
17. [17]
  Hongyi LI , Aimin WU , Liuyang ZHAO , Xinpeng LIU , Fengqin CHEN , Aikui LI , Hao HUANG . Effect of Y(PO₃)₃ double-coating modification on the electrochemical properties of Li[Ni_0.8Co_0.15Al_0.05]O₂. Chinese Journal of Inorganic Chemistry, 2024, 40(7): 1320-1328. doi: 10.11862/CJIC.20230480
18. [18]
  Gregorio F. Ortiz . Some facets of the Mg/Na₃VCr_0.5Fe_0.5(PO₄)₃ battery. Chinese Chemical Letters, 2024, 35(10): 109391-. doi: 10.1016/j.cclet.2023.109391
19. [19]
  Chuanming GUO , Kaiyang ZHANG , Yun WU , Rui YAO , Qiang ZHAO , Jinping LI , Guang LIU . Performance of MnO₂-0.39IrO_x composite oxides for water oxidation reaction in acidic media. Chinese Journal of Inorganic Chemistry, 2024, 40(6): 1135-1142. doi: 10.11862/CJIC.20230459
20. [20]
  Zeyuan WANG , Songzhi ZHENG , Hao LI , Jingbo WENG , Wei WANG , Yang WANG , Weihai SUN . Effect of I₂ interface modification engineering on the performance of all-inorganic CsPbBr₃ perovskite solar cells. Chinese Journal of Inorganic Chemistry, 2024, 40(7): 1290-1300. doi: 10.11862/CJIC.20240021

Get Citation

PDF

XML

Metrics

PDF Downloads(35)
Abstract views(1856)
HTML views(569)

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

Hydrothermal Synthesis and Electrochemical Properties of Na3V2(PO4)2O2F Cathode for Sodium-Ion Batteries

Metrics

通讯作者: 陈斌, bchen63@163.com

Hydrothermal Synthesis and Electrochemical Properties of Na₃V₂(PO₄)₂O₂F Cathode for Sodium-Ion Batteries