Citation: Hong-wei WANG, Jun-xia WU, Xiao-yan WANG, Hong WANG, Jin-rong LIU. Formation of perovskite-type LaNiO₃ on La-Ni/Al₂O₃-ZrO₂ catalysts and their performance for CO methanation[J]. Journal of Fuel Chemistry and Technology, ;2021, 49(2): 186-197. doi: 10.1016/S1872-5813(21)60012-9 shu

Formation of perovskite-type LaNiO₃ on La-Ni/Al₂O₃-ZrO₂ catalysts and their performance for CO methanation

1.
College of Chemical Engineering, Inner Mongolia University of Technology, Hohhot 010051, China

Author Bio: 王宏伟，男，出生于1990年08月，在读博士，主要从事CO/CO₂甲烷化催化剂的相关研究工作
Corresponding author: Hong WANG, hongwang396@imut.edu.cn
Received Date: 24 September 2020
Revised Date: 9 November 2020

Figures(13)

The carbon deposition and sintering of Ni-based catalysts, used in CO methanation, are the main problems to be solved. In this paper, supported LaNiO₃/Al₂O₃-ZrO₂ catalyst was prepared by neutralization hydrolysis-citric acid complexation method. The effects of La-Ni loading and calcination temperature of support on the structure and catalytic activity of the catalyst were investigated. The structural evolution of catalyst precursor before and after reduction was studied via XRD, H₂-TPR, BET, XPS, TEM and other characterization methods. The results showed that the catalyst supported by homogeneous Al-Zr solid solution was beneficial to form the active component with LaNiO₃ structure, and the Ni⁰ derived from LaNiO₃ was the key factor for keeping the activity at high temperature. The La-Ni loading affected the formation of LaNiO₃ and the reduction state of Ni. Among the catalysts studied, 30% of the La-Ni loading was more favorable for the formation of perovskite LaNiO₃. The Ni⁰ and La₂O₃ reduced from LaNiO₃ were highly dispersed on the surface of the support, and the Ni⁰ nanoparticles were anchored by the support and La₂O₃, which inhibited the migration and aggregation of Ni⁰ particles at high temperature and thus led to high thermal stability.
- CO methanation,
- aluminum zirconium composite oxide,
- perovskite,
- nickel,
- lanthanum oxide
1. [1]
  LIU Q, SUN J, FENG Q. A La-promoted Ni/MgAl₂O₄ catalyst with superior methanation performance for the production of synthetic natural gas[J]. Catal Today,2020,339:127−134. doi: 10.1016/j.cattod.2019.07.034
2. [2]
  RONSCH S, SCHNEIDER J, MATTHISCHKE S. Review on methanation - From fundamentals to current projects[J]. Fuel,2016,166:276−296. doi: 10.1016/j.fuel.2015.10.111
3. [3]
  HAN Y, QUAN Y, HAO P. Highly anti-sintering and anti-coking ordered mesoporous silica carbide supported nickel catalyst for high temperature CO methanation[J]. Fuel,2019,257:116006.
4. [4]
  KAMATA H, TIAN Z Q, IZUMI Y. Dispersed and high loading Ni catalyst stabilized in porous SiO₂ matrix for substituted natural gas production[J]. Catal Today,2018,299:193−200. doi: 10.1016/j.cattod.2017.03.003
5. [5]
  ZHANG A H, ZHU J, DUAN W H. CO methanation on Ni(111) and modified Ni₃Al(111) surfaces: A first-principle study[J]. Surf Sci,2007,601(2):475−478. doi: 10.1016/j.susc.2006.10.009
6. [6]
  CASTILLO J, ARTEAGA-PÉREZ L E, KARELOVIC A. The consequences of surface heterogeneity of cobalt nanoparticles on the kinetics of CO methanation[J]. Catal Sci Technol,2019,9(22):6415−6427. doi: 10.1039/C9CY01753D
7. [7]
  CHEN S, ABDEL-MAGEED A M, GAUCKLER C. Selective CO methanation on isostructural Ru nanocatalysts: The role of support effects[J]. J Catal,2019,373:103−115. doi: 10.1016/j.jcat.2019.03.015
8. [8]
  ABDEL-MAGEED A M, WIDMANN D, OLESEN S E. Selective CO methanation on highly active Ru/TiO₂ catalysts: Identifying the physical origin of the observed activation/deactivation and loss in selectivity[J]. ACS Catal,2018,8(6):5399−5414. doi: 10.1021/acscatal.8b00384
9. [9]
  FAJÍN J L C, GOMES J R B, D. S. CORDEIRO M N. Mechanistic study of carbon monoxide methanation over pure and rhodium- or ruthenium-doped nickel catalysts[J]. J Phys Chem C,2015,119(29):16537−16551. doi: 10.1021/acs.jpcc.5b01837
10. [10]
  JENEWEIN B, FUCHS M, HAYEK K. The CO methanation on Rh/CeO₂ and CeO₂/Rh model catalysts: A comparative study[J]. Surf Sci. 2003, 532−535: 364-369.
11. [11]
  HU X, YAN W, DING W. Bifunctional palladium composite membrane for hydrogen separation and catalytic CO methanation[J]. Chin J Catal,2013,34(9):1720−1729. doi: 10.1016/S1872-2067(12)60636-6
12. [12]
  LI S, GONG D, TANG H. Preparation of bimetallic Ni@Ru nanoparticles supported on SiO₂ and their catalytic performance for CO methanation[J]. Chem Eng J,2018,334:2167−2178. doi: 10.1016/j.cej.2017.11.124
13. [13]
  ZHAO B, YAO Y, SHI H. Preparation of Ni/SiO₂ catalyst via novel plasma-induced micro-combustion method[J]. Catal Today,2019,337:28−36. doi: 10.1016/j.cattod.2019.04.068
14. [14]
  ROMBI E, CUTRUFELLO M G, ATZORI L. CO methanation on Ni-Ce mixed oxides prepared by hard template method[J]. Appl Catal A:Gen,2016,515:144−153. doi: 10.1016/j.apcata.2016.02.002
15. [15]
  ZHAI Y, XIONG J, LI C. Influence of preparation method on performance of a metal supported perovskite catalyst for combustion of methane[J]. J Rare Earths,2010,28(1):54−58. doi: 10.1016/S1002-0721(09)60050-8
16. [16]
  GONG D, LI S, GUO S. Lanthanum and cerium co-modified Ni/SiO₂ catalyst for CO methanation from syngas[J]. Appl Surf Sci,2018,434:351−364. doi: 10.1016/j.apsusc.2017.10.179
17. [17]
  HWANG S, HONG U G, LEE J. Methanation of carbon dioxide over mesoporous nickel-M-alumina (M = Fe, Zr, Ni, Y, and Mg) xerogel catalysts: Effect of second metal[J]. Catal Lett,2012,142(7):860−868. doi: 10.1007/s10562-012-0842-0
18. [18]
  JIANG P, ZHAO J, HAN Y. Highly active and dispersed Ni/Al₂O₃ catalysts for CO methanation prepared by the cation-anion double-hydrolysis method: Effects of Zr, Fe, and Ce promoters[J]. Ind Eng Chem Res,2019,58(27):11728−11738. doi: 10.1021/acs.iecr.9b00002
19. [19]
  LI Z, ZHAO T, ZHANG L. Promotion effect of additive Fe on Al₂O₃ supported Ni catalyst for CO₂ methanation[J]. Appl Organomet Chem,2018,32(5).
20. [20]
  PHUNG T K, PHAM T L M, NGUYEN A-N T. Effect of supports and promoters on the performance of Ni-based catalysts in ethanol steam reforming[J]. Chem Eng Technol,2020,43(4):672−688.
21. [21]
  ZHANG M, YU F, LI J. High CO methanation performance of two-dimensional Ni/MgAl layered double oxide with enhanced oxygen vacancies via flash nanoprecipitation[J]. Catalysts,2018,8(9).
22. [22]
  DING C, GAO X, HAN Y. Effects of surface states over core-shell Ni@SiO₂ catalysts on catalytic partial oxidation of methane to synthesis gas[J]. J Energy Chem,2015,24(1):45−53. doi: 10.1016/S2095-4956(15)60283-2
23. [23]
  SI J, LIU G, LIU J. Ni nanoparticles highly dispersed on ZrO₂ and modified with La₂O₃ for CO methanation[J]. RSC Adv,2016,6(15):12699−12707. doi: 10.1039/C5RA26888E
24. [24]
  HAN Y, WEN B, ZHU M. Lanthanum incorporated in MCM-41 and its application as a support for a stable Ni-based methanation catalyst[J]. J Rare Earths,2018,36(4):367−373. doi: 10.1016/j.jre.2017.07.016
25. [25]
  RABELO-NETO R C, SALES H B E, INOCÊNCIO C V M. CO₂ reforming of methane over supported LaNiO₃ perovskite-type oxides[J]. Appl Catal B: Environ,2018,221:349−361. doi: 10.1016/j.apcatb.2017.09.022
26. [26]
  ZHAO L, HAN T, WANG H. Ni-Co alloy catalyst from LaNi_1−xCo_xO₃ perovskite supported on zirconia for steam reforming of ethanol[J]. Appl Catal B: Environ,2016,187:19−29. doi: 10.1016/j.apcatb.2016.01.007
27. [27]
  WANG X, ZHU L, ZHUO Y. Enhancement of CO₂ methanation over La-Modified Ni/SBA-15 catalysts prepared by different doping methods[J]. ACS Sustainable Chem Eng,2019,7(17):14647−14660. doi: 10.1021/acssuschemeng.9b02563
28. [28]
  LIU Q, GU F, GAO J. Coking-resistant Ni-ZrO₂/Al₂O₃ catalyst for CO methanation[J]. J Energy Chem,2014,23(6):761−770. doi: 10.1016/S2095-4956(14)60210-2
29. [29]
  ZHANG X, RUI N, JIA X. Effect of decomposition of catalyst precursor on Ni/CeO₂ activity for CO methanation[J]. Chin J Catal,2019,40(4):495−503. doi: 10.1016/S1872-2067(19)63289-4
30. [30]
  NGUYEN T T M, WISSING L, SKJØTH-RASMUSSEN M S. High temperature methanation: Catalyst considerations[J]. Catal Today,2013,215:233−238. doi: 10.1016/j.cattod.2013.03.035
31. [31]
  GUO C, WU Y, QIN H. CO methanation over ZrO₂/Al₂O₃ supported Ni catalysts: A comprehensive study[J]. Fuel Process Technol,2014,124:61−69. doi: 10.1016/j.fuproc.2014.02.017
32. [32]
  LIN J, MA C, WANG Q. Enhanced low-temperature performance of CO₂ methanation over mesoporous Ni/Al₂O₃-ZrO₂ catalysts[J]. Appl Catal B: Environ,2019,243:262−272. doi: 10.1016/j.apcatb.2018.10.059
33. [33]
  LI L, HUO M, ZHANG Y. Synthesis of nickel catalysts supported on Zr-doped ordered mesoporous Al₂O₃ and their catalytic performance for low-temperature CO₂ reforming of CH₄[J]. J Porous Mater,2017,24(6):1613−1625. doi: 10.1007/s10934-017-0401-6
34. [34]
  SOUZA M M V M, ARANDA D A G, SCHMAL M. Reforming of methane with carbon dioxide over Pt/ZrO₂/Al₂O₃ catalysts[J]. J Catal,2001,204(2):498−511. doi: 10.1006/jcat.2001.3398
35. [35]
  SONG J H, HAN S J, SONG I K. Hydrogen production by steam reforming of ethanol over mesoporous Ni-Al₂O₃-ZrO₂ catalysts[J]. Catal Surv Asia,2017,21(3):114−129. doi: 10.1007/s10563-017-9230-5
36. [36]
  MORADI G R, RAHMANZADEH M, KHOSRAVIAN F. The effects of partial substitution of Ni by Zn in LaNiO₃ perovskite catalyst for methane dry reforming[J]. J CO₂ Util,2014,6:7−11. doi: 10.1016/j.jcou.2014.02.001
37. [37]
  WANG S, ZHANG L, ZHANG W Y. Selective conversion of CO₂ into propene and butene[J]. Chem,2020,6:1−20. doi: 10.1016/j.chempr.2019.12.023
1. [1]
  Dong-Ling Kuang , Song Chen , Shaoru Chen , Yong-Jie Liao , Ning Li , Lai-Hon Chung , Jun He . 2D Zirconium-based metal-organic framework/bismuth(III) oxide nanorods composite for electrocatalytic CO2-to-formate reduction. Chinese Journal of Structural Chemistry, 2024, 43(7): 100301-100301. doi: 10.1016/j.cjsc.2024.100301
2. [2]
  Qiang Wu , Baofeng Wang . Exploring synthetic strategy for stabilizing nickel-rich layered oxide cathodes through structural design. Chinese Chemical Letters, 2024, 35(12): 110089-. doi: 10.1016/j.cclet.2024.110089
3. [3]
  Cheng PENG , Jianwei WEI , Yating CHEN , Nan HU , Hui ZENG . First principles investigation about interference effects of electronic and optical properties of inorganic and lead-free perovskite Cs₃Bi₂X₉ (X=Cl, Br, I). Chinese Journal of Inorganic Chemistry, 2024, 40(3): 555-560. doi: 10.11862/CJIC.20230282
4. [4]
  Jiayu Bai , Songjie Hu , Lirong Feng , Xinhui Jin , Dong Wang , Kai Zhang , Xiaohui Guo . Manganese vanadium oxide composite as a cathode for high-performance aqueous zinc-ion batteries. Chinese Chemical Letters, 2024, 35(9): 109326-. doi: 10.1016/j.cclet.2023.109326
5. [5]
  Xinyi Hu , Riguang Zhang , Zhao Jiang . Depositing the PtNi nanoparticles on niobium oxide to enhance the activity and CO-tolerance for alkaline methanol electrooxidation. Chinese Journal of Structural Chemistry, 2023, 42(11): 100157-100157. doi: 10.1016/j.cjsc.2023.100157
6. [6]
  Tian TIAN , Meng ZHOU , Jiale WEI , Yize LIU , Yifan MO , Yuhan YE , Wenzhi JIA , Bin HE . Ru-doped Co₃O₄/reduced graphene oxide: Preparation and electrocatalytic oxygen evolution property. Chinese Journal of Inorganic Chemistry, 2025, 41(2): 385-394. doi: 10.11862/CJIC.20240298
7. [7]
  Jun Luo , Yanya Liu , Jianghuaxiong Zhu , Chengxiong Wang , Yunkun Zhao , Dong Yan , Jian Li , Lichao Jia . A proton-conducting solid oxide fuel cell for co-production of ethylene and power via ethane conversion. Chinese Chemical Letters, 2025, 36(7): 110171-. doi: 10.1016/j.cclet.2024.110171
8. [8]
  Jumei Zhang , Ziheng Zhang , Gang Li , Hongjin Qiao , Hua Xie , Ling Jiang . Ligand-mediated reactivity in CO oxidation of yttrium-nickel monoxide carbonyl complexes. Chinese Chemical Letters, 2025, 36(2): 110278-. doi: 10.1016/j.cclet.2024.110278
9. [9]
  Xiuxiu Jia , Tao Yin , Nianpeng Li , Hua Zhang , Anxian Shi , Abdukader Abdukayum , Sanshuang Gao , Guangzhi Hu . Reticulated lanthanum (La) carbonate-carbon composite for efficient phosphorus removal from eutrophic wastewater. Chinese Chemical Letters, 2025, 36(6): 110398-. doi: 10.1016/j.cclet.2024.110398
10. [10]
  Lijun Yan , Shiqi Chen , Penglu Wang , Xiangyu Liu , Lupeng Han , Tingting Yan , Yuejin Li , Dengsong Zhang . Hydrothermally stable metal oxide-zeolite composite catalysts for low-temperature NO_x reduction with improved N₂ selectivity. Chinese Chemical Letters, 2024, 35(6): 109132-. doi: 10.1016/j.cclet.2023.109132
11. [11]
  Zhenjie Yang , Chenyang Hu , Xuan Pang , Xuesi Chen . Sequence design in terpolymerization of ε-caprolactone, CO₂ and cyclohexane oxide: Random ester-carbonate distributions lead to large-span tunability. Chinese Chemical Letters, 2024, 35(5): 109340-. doi: 10.1016/j.cclet.2023.109340
12. [12]
  Jinglin CHENG , Xiaoming GUO , Tao MENG , Xu HU , Liang LI , Yanzhe WANG , Wenzhu HUANG . NiAlNd catalysts for CO₂ methanation derived from the layered double hydroxide precursor. Chinese Journal of Inorganic Chemistry, 2024, 40(8): 1592-1602. doi: 10.11862/CJIC.20240152
13. [13]
  Wenjing Dai , Lan Luo , Zhen Yin . Interface reconstruction of hybrid oxide electrocatalysts for seawater oxidation. Chinese Journal of Structural Chemistry, 2025, 44(3): 100442-100442. doi: 10.1016/j.cjsc.2024.100442
14. [14]
  Hui Bian , Xinyi Yuan , Nan Zhang , Zhuo Xu , Juhong Lian , Ruibin Jiang , Junqing Yan , Deng Li , Shengzhong (Frank) Liu . Correlating vacancy-defect density with CO₂ activation for promoted CO₂ methanation over CsPbBr₃ photocatalyst. Chinese Chemical Letters, 2025, 36(7): 111034-. doi: 10.1016/j.cclet.2025.111034
15. [15]
  Zili Ma , Zeyu Li , Jun Lv . Shortening the formation time of oxide thin film photoelectrodes from hours to seconds. Chinese Journal of Structural Chemistry, 2025, 44(4): 100450-100450. doi: 10.1016/j.cjsc.2024.100450
16. [16]
  Chen-Xin Wang , Guang-Lei Li , Yu Hang , Dan-Feng Lu , Jian-Qi Ye , Hao Su , Bing Hou , Tao Suo , Dan Wen . Shock-resistant wearable pH sensor based on tungsten oxide aerogel. Chinese Chemical Letters, 2025, 36(7): 110502-. doi: 10.1016/j.cclet.2024.110502
17. [17]
  Zhenkang Ai , Hui Chen , Xuebin Liao . Nickel-catalyzed decarboxylative difluoromethylation and alkylation of alkenes. Chinese Chemical Letters, 2025, 36(3): 109954-. doi: 10.1016/j.cclet.2024.109954
18. [18]
  Zhijie Zhang , Xun Li , Huiling Tang , Junhao Wu , Chunxia Yao , Kui Li . Cs₂CuBr₄ perovskite quantum dots confined in mesoporous CuO framework as a p-n type S-scheme heterojunction for efficient CO₂ photoconversion. Chinese Chemical Letters, 2024, 35(11): 109700-. doi: 10.1016/j.cclet.2024.109700
19. [19]
  Xiao-Bo Liu , Ren-Ming Liu , Xiao-Di Bao , Hua-Jian Xu , Qi Zhang , Yu-Feng Liang . Nickel-catalyzed reductive formylation of aryl halides via formyl radical. Chinese Chemical Letters, 2024, 35(12): 109783-. doi: 10.1016/j.cclet.2024.109783
20. [20]
  Chaozheng He , Jia Wang , Ling Fu , Wei Wei . Nitric oxide assists nitrogen reduction reaction on 2D MBene: A theoretical study. Chinese Chemical Letters, 2024, 35(5): 109037-. doi: 10.1016/j.cclet.2023.109037

Get Citation

PDF

XML

Metrics

PDF Downloads(11)
Abstract views(2270)
HTML views(426)

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

Formation of perovskite-type LaNiO3 on La-Ni/Al2O3-ZrO2 catalysts and their performance for CO methanation

Metrics

通讯作者: 陈斌, bchen63@163.com

Formation of perovskite-type LaNiO₃ on La-Ni/Al₂O₃-ZrO₂ catalysts and their performance for CO methanation