A 1D coordination polymer (CP), (TBA) [Bi(bp4do)Br₄] (1), was synthesized by the assembly of 4, 4' - bipyridine -N, N'-dioxide (bp4do) and Bi³⁺ (TBA⁺=tetrabutylammonium). 1 exhibits a red luminescence with a quantum yield of up to 69%. A solid-state thin-film sensor (1/PVP) with extremely high luminescence stability was prepared by combining 1 with polyvinyl pyrrolidone (PVP). 1/PVP has a wide - range sensing capability for 11 NH₃/amine vapors with rapid response. During the sensing process, its luminescence color changed from red to blue, which was easy for naked -eye observation. The sensing mechanism is NH₃/amine-induced collapse of the framework of 1. Furthermore, 1/PVP has been successfully applied to monitoring food freshness such as meat/aquatic products.

以二甲基亚砜(DMSO)为溶剂，通过溶剂热挥发法合成了硫酸锌开放骨架[Zn(SO₄)(DMSO)] (1)基质。再将2，6-萘二酸(P)低剂量掺杂到基质1中，制备了一种同时具有荧光和室温磷光(RTP)性质的复合物P@1。P@1具有肉眼可见的绿色RTP，持续时间约为2 s。P@1对Pb²⁺表现出选择性磷光增强响应，检测限为2.52 μmol·L^-1。其检测机制主要是Pb—O配位作用诱导体系磷光增强。有趣的是，P@1可作为双通道探针通过荧光猝灭快速检测Fe³⁺，检测限为0.038 μmol·L^-1。其识别机制可能归因于P@1与Fe³⁺之间的竞争性能量吸收。

高导热石墨烯膜是近年来备受关注的高功率电子器件用散热材料。导热系数作为一项评价其基础性能的重要参数，实现其精确测量对于理解材料基础物性、优化制备工艺以及实际工程应用都具有重要意义。然而，现有的商业化导热测试设备，囿于测试原理、样品尺寸等因素，难以同时实现高效、准确、可靠的测量。开发操作简便、测试快捷、精度优异、可跨尺度的测量方案仍是一个重要挑战。本文提出基于稳态电热法的石墨烯膜导热系数的精确可靠测量方法，结合实验测试与仿真模拟，基于原理分析、测试优化、数据处理等三个方面，显著提升导热测量的精度与效率。测量结果的准确性受到热损校正、样品尺寸、系统设计以及数据处理等四方面因素影响。实验结果表明，热辐射和热对流引起的热损失会影响样品的温度分布和测量结果，可通过控制样品尺寸和温升来控制。对实验数据进行筛选和预处理也可以有效提高测量精度。通过实验与仿真结合，我们提出了可行的操作指南与标准化的测试方案。通过优化，该方法测量误差低于3.0%，不确定性降至0.5%，响应时间达毫秒级。本工作为准确评估材料导热性能提供有益指导，也为导热材料的热管理工程应用提供技术支撑。