纳米复合固体超强酸S2O82-/CoFe2O4催化合成癸二酸二乙酯

引用本文: 金华峰, 李宝璋. 纳米复合固体超强酸S₂O₈^2-/CoFe₂O₄催化合成癸二酸二乙酯[J]. 应用化学, 2003, 20(1): 10-14. shu

Citation: JIN Hua-Feng, LI Bao-Zhang. Preparation of Nanosized Solid Superacid S₂O₈^2-/CoFe₂O₄ and Catalytic Synthesis of Diethyl Sebacate[J]. Chinese Journal of Applied Chemistry, 2003, 20(1): 10-14. shu

纳米复合固体超强酸S₂O₈^2-/CoFe₂O₄催化合成癸二酸二乙酯

金华峰 ^{a,
,} ,
李宝璋 ^b,

1.
a 安康师范专科学校化学系安康 725000;
2.
b 西北大学化工系西安

通讯作者: 金华峰,男,1966年生,副教授;E-mail:hfjin5155@hotmail.com;研究方向:纳米材料制备及多相催化

基金项目:
陕西省教育厅自然科学专项应用基础研究项目(01JK203) (01JK203)

中国石油天然气集团公司科学研究与开发项目(99081603) (99081603)

安康师专科研基金项目(2002AZXZR003) (2002AZXZR003)

摘要: 将硫酸钴、硫酸亚铁在NaOH溶液中与NaHCO₃反应制得碱式碳酸盐前驱体,后者用(NH₄)₂S₂O₈浸渍、干燥,再经500℃焙烧得到固体超强酸催化剂S₂O₈^2-/CoFe₂O₄。产物经XRD、TEM、BET、TG-DTA及化学法等检测,含硫量4.52%,粒径为42 nm,比表面积为146 m²/g,粒度均匀。催化剂的酸强度处于-16.02和-14.52之间。以该固体酸为催化剂,由癸二酸和无水乙醇合成了癸二酸二乙酯。最佳反应条件为:n(醇):n(酸)=4.0:1.0,癸二酸0.1 mol,催化剂1.0 g,反应时间25h。在此反应条件下,酯化率可达93.6%。

关键词:

English

Preparation of Nanosized Solid Superacid S₂O₈^2-/CoFe₂O₄ and Catalytic Synthesis of Diethyl Sebacate

JIN Hua-Feng ^{a,
,} ,
LI Bao-Zhang ^b,

1.
a Department of Chemistry, Ankang Teacher's College, Ankang 725000;
2.
b Department of Chemical Engineering, Northwest University, Xi'an

Corresponding author: 金华峰,男,1966年生,副教授;E-mail:hfjin5155@hotmail.com;研究方向:纳米材料制备及多相催化

Received Date: 12 August 2002
Fund Project:
陕西省教育厅自然科学专项应用基础研究项目(01JK203)

中国石油天然气集团公司科学研究与开发项目(99081603)

安康师专科研基金项目(2002AZXZR003)

Abstract: Reacting the mixture of fine cobalt sulfate and ferrous sulfate with PEG-600 in NaOH solution(at pH=9.0) gave a precusor, CoFeO(OH)₂O, which after immersion in (NH₄O)₂S₂O₈ solution, reacting, drying and calcinating at 500℃ afforded the title solid superacid S₂O₈^2-/CoFe₂O₄. The compound was characterized by XRD, TEM, BET, TG-DTA techniques and chemical analysis. The results show that S₂O₈^2-/CoFe₂O₄ was sized in 42 nm with specific surface area of 146 m²/g. The solid superacid S₂O₈^2-/CoFe₂O₄ was used as catalyst in synthesis of diethyl sebacate from absolute ethanol and sebacic acid. At the conditions of 1.0 g catalyst with the acid strength of -16.02< H₀< -14.52, 0.1 mol sebacic acid, molar ratio of absolute ehtanol to sebacic acid 4.0:1.0, and reaction time of 2.5 h, diethyl sebacate in yield of 93.6% was obtained.

Key words:

扫一扫看文章

计量

PDF下载量: 0
文章访问数: 0
HTML全文浏览量: 0

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

纳米复合固体超强酸S₂O₈^2-/CoFe₂O₄催化合成癸二酸二乙酯

通讯作者: 金华峰,男,1966年生,副教授;E-mail:hfjin5155@hotmail.com;研究方向:纳米材料制备及多相催化

English

Preparation of Nanosized Solid Superacid S₂O₈^2-/CoFe₂O₄ and Catalytic Synthesis of Diethyl Sebacate

Corresponding author: 金华峰,男,1966年生,副教授;E-mail:hfjin5155@hotmail.com;研究方向:纳米材料制备及多相催化

CCS Chemistry：嵌段共聚物自组装成 “三明治”二维有机材料，实现纳米级压力传感功能

CCS Chemistry：颜徐州、鲍哲南：你的皮肤可能是一片SPMs

CCS Chemistry：工作高效不疲劳，只须让催化剂动起来

CCS Chemistry：静电组装导向聚合- 聚电解质纳米凝胶量化制备新策略

CCS Chemistry：金黄色葡萄球菌醛基脱氢酶是如何识别特异性底物的？

计量

通讯作者: 陈斌, bchen63@163.com

中国化学会秘书处