Citation: WEI Yu-liang, GUI Ke-ting, LIU Xiang-xiang, LIANG Hui, GU Shao-chen, REN Dong-dong. Performance of Mn-Ce co-doped siderite catalysts in the selective catalytic reduction of NO_x by NH₃[J]. Journal of Fuel Chemistry and Technology, ;2019, 47(12): 1495-1503. shu

Performance of Mn-Ce co-doped siderite catalysts in the selective catalytic reduction of NO_x by NH₃

Key Laboratory of Energy Thermal Conversion and Control of Ministry of Education, School of Energy and Environment, Southeast University, Nanjing 210096, China

Corresponding author: GUI Ke-ting, ktgui@seu.edu.cn
Received Date: 3 September 2019
Revised Date: 12 November 2019

Fund Project: the National Natural Science Foundation of China 51276039Environmental Protection Research Project of Jiangsu Province 2015008The project was supported by the National Natural Science Foundation of China (51276039) and Environmental Protection Research Project of Jiangsu Province (2015008)

Figures(10)

Siderite, rich in the transition elements, is an idea material to prepare the catalysts for the selective catalytic reduction (SCR) of NO_x by NH₃. In this work, siderite was doped with Mn and Ce and the performance of Mn-Ce co-doped siderite catalysts in the removal of NO_x (de-NO_x) by SCR with NH₃ was then investigated. The results illustrate that FeCO₃ as the main component of siderite can be converted into Fe₂O₃ by calcination at 450℃. The doping of siderite with Mn and Ce can enhance the surface area and acidity of siderite and reduce the thermal stability of ammonium sulfate formed on the catalyst surface. As a result, the Mn-Ce co-doped siderite catalysts exhibit high efficiency in the de-NO_x by SCR and high resistance against sulfur. Over the 3%Mn1%Ce-siderite catalyst, high NO_x conversion (>90%) is achieved in the temperature window of 180-300℃; moreover, the NO_x conversion remains above 75% even after introducing SO₂ for 7.5 h.
- Mn-Ce co-doping,
- siderite,
- selective catalytic reduction,
- de-NO_x,
- sulfur resistance
1. [1]
  BUSCA G, LIETTI L, RAMIS G, BERTI F. Chemical and mechanistic aspects of the selective catalytic reduction of NO_x by ammonia over oxide catalysts: A review[J]. Appl Catal B: Environ, 1998,18(1/2):1-36.
2. [2]
  FORZATTI P. Environmental catalysis for stationary applications[J]. Catal Today, 2000,62(1):51-65.
3. [3]
  YANG S, WANG C, LI J, YAN N, MA L, CHANG H. Low temperature selective catalytic reduction of NO with NH₃ over Mn-Fe spinel: performance, mechanism and kinetic study[J]. Appl Catal B: Environ, 2011,110:71-80. doi: 10.1016/j.apcatb.2011.08.027
4. [4]
  LIU F, HE H, ZHANG C, SHAN W, SHI X. Mechanism of the selective catalytic reduction of NO_x with NH₃ over environmental-friendly iron titanate catalyst[J]. Catal Today, 2010,175(1):18-25.
5. [5]
  LIU C, YANG S, MA L, PENG Y, HAMIDREZA A, CHANG H, LI J. Comparison on the performance of α-Fe₂O₃ and γ-Fe₂O₃ for selective catalytic reduction of nitrogen oxides with ammonia[J]. Catal Lett, 2013,143(7):697-704. doi: 10.1007/s10562-013-1017-3
6. [6]
  XIE J, FANG D, HE F, CHEN J, FU Z, CHEN X. Performance and mechanism about MnO_x species included in MnO_x/TiO₂ catalysts for SCR at low temperature[J]. Catal Commun, 2012,28:77-81. doi: 10.1016/j.catcom.2012.08.022
7. [7]
  JIANG B Q, LIU Y, WU Z B. Low-temperature selective catalytic reduction of NO on MnO_x/TiO₂ prepared by different methods[J]. J Hazard Mater, 2009,162(2/3):1249-1254.
8. [8]
  ELLMERS I, VELEZ R P, BENTRUP U, BRUCKNER A, GUNERT W. Oxidation and selective reduction of NO over Fe-ZSM-5-How related are these reactions?[J]. J Catal, 2014,311:199-211. doi: 10.1016/j.jcat.2013.11.024
9. [9]
  YAO G H, GUI K T, WANG F. Low-temperature De-NO_x by selective catalytic reduction based on iron-based catalysts[J]. Chem Eng Technol, 2010,33(7):1093-1098. doi: 10.1002/ceat.201000015
10. [10]
  WU Z, JIANG B, LIU Y, ZHAO W, GUAN B. Experimental study on a low-temperature SCR catalyst based on MnO_x/TiO₂ prepared by so-gel method[J]. J Hazard Mater, 2007,145(3):488-494. doi: 10.1016/j.jhazmat.2006.11.045
11. [11]
  JIA B, GUO J, LUO H, SHU S, FANG N, LI J. Study of NO removal and resistance to SO₂ and H₂O of MnO_x/TiO₂, MnO_x/ZrO₂ and MnO_x/ZrO₂-TiO₂[J]. Appl Catal A: Gen, 2018,553:82-90. doi: 10.1016/j.apcata.2017.12.016
12. [12]
  GUO R, LI M, SUN P, PAN W, LIU S, LIU J, SUN X, LIU S. Mechanistic investigation of the promotion effect of Bi modification on the NH₃-SCR performance of Ce/TiO₂ catalyst[J]. J Phys Chem C, 2017,121(49):27535-27545. doi: 10.1021/acs.jpcc.7b10342
13. [13]
  XU L, LI X S, CROCKER M, ZHANG Z S, ZHU A M, SHI C. A study of the mechanism of low-temperature SCR of NO with NH₃ on MnO_x/CeO₂[J]. J Mol Catal A: Chem, 2013,378:82-90. doi: 10.1016/j.molcata.2013.05.021
14. [14]
  ZHAO W, TANG Y, WAN Y, LI L, YAO S, LI X, GU J, LI Y, SHI J. Promotion effects of SiO₂ or/and Al₂O₃ doped CeO₂/TiO₂ catalysts for selective catalytic reduction of NO by NH₃[J]. J Hazard Mater, 2014,278:350-359. doi: 10.1016/j.jhazmat.2014.05.071
15. [15]
  DU X, WANG X, CHEN Y, GAO X, ZHANG L. Supported mental sulfates on Ce-TiO_x as catalysts for NH₃-SCR of NO: High resistances to SO₂ and potassium[J]. J Ind Eng Chem, 2016,36:271-278. doi: 10.1016/j.jiec.2016.02.013
16. [16]
  YE D, REN X, QU R, LIU S, ZHENG C, GAO X. Designing SO₂-resistant cerium-based catalyst by modifying with Fe₂O₃ for the selective catalytic reduction of NO with NH₃[J]. J Mol Catal, 2019,462:10-18. doi: 10.1016/j.mcat.2018.10.007
17. [17]
  JIN R, LIU Y, WANG Y, CEN W, WU Z, WANG H, WENG X. The role of cerium in the improved SO₂ tolerance for NO reduction with NH₃ over Mn-Ce/TiO₂ catalyst at low temperature[J]. Appl Catal B: Environ, 2014,148/149:582-588. doi: 10.1016/j.apcatb.2013.09.016
18. [18]
  HUANG L, LI X, HUA J. Effect of Sn doping on denitrification and sulfur resistance performance of Ce-Mn/AC catalyst[J]. Adv Eng Sci, 2019,51(5):185-191.
19. [19]
  ZHAO S, LIU L, WANG J, XIONG H. Effect of Fe, Ce and Cu on low temperature denitrification and sulphur resistance of Mn/AC catalysts[J]. Appl Chem Ind, 2019,48(9):2107-2112.
20. [20]
  WU Y, LIANG H, ZHAO C, CHEN X, CHEN C, DAI C, TANG J. Effect of support on low temperature denitrification performance of Mn-Ce catalysts[J]. Pet Process Petrochem, 2019,50(40):44-48.
21. [21]
  ZHANG L, LI L, CAO Y, YAO X, GE C, GAO F, DENG Y, TANG C, DONG L. Getting insight into the influence of SO₂ on TiO₂/CeO₂ for the selective catalytic reduction of NO by NH₃[J]. Appl Catal B: Environ, 2015,165:589-598. doi: 10.1016/j.apcatb.2014.10.029
22. [22]
  JIN R, YUE L, WU Z, WANG H, GU T. Low-temperature selective catalytic reduction of NO with NH₃ over Mn-Ce oxides supported on TiO₂ and Al₂O₃: A comparative study[J]. Chemosphere, 2010,78(9):1160-1166. doi: 10.1016/j.chemosphere.2009.11.049
23. [23]
  XU W, HE H, YU Y. Deactivation of a Ce/TiO₂ catalyst by SO₂ in the selective catalytic reduction of NO by NH₃[J]. J Phys Chem C, 2009,113(11):4426-4432. doi: 10.1021/jp8088148
24. [24]
  WU Z, JIN R, LIU Y, WANG H. Ceria modified MnO_x/TiO₂ as a superior catalyst for NO reduction with NH₃ at low-temperature[J]. Catal Commun, 2008,9(13):2217-2220. doi: 10.1016/j.catcom.2008.05.001
25. [25]
  KIJLSTRA W S, BIERVLIET M, POELS E K, BLIEK A. Deactivation by SO₂ of MnO_x/Al₂O₃ catalysts used for the selective catalytic reduction of NO with NH₃ at low temperatures[J]. Appl Catal B: Environ, 1998,16(4):327-337. doi: 10.1016/S0926-3373(97)00089-1
26. [26]
  ZHU Z, NIU H, LIU Z, LIU S. Decomposition and reactivity of NH₄HSO₄ on V₂O₅/AC catalysts used for NO reduction with ammonia[J]. J Catal, 2000,195(2):268-278. doi: 10.1006/jcat.2000.2961
1. [1]
  Xiaoqiang Wang , Fangyuan Zhou , Yue Liu , Zhongbiao Wu . CePO₄ supported Cr catalyst with superior sulfur tolerance for selective catalytic oxidation of ammonia. Chinese Chemical Letters, 2025, 36(7): 110420-. doi: 10.1016/j.cclet.2024.110420
2. [2]
  Chen Lian , Si-Han Zhao , Hai-Lou Li , Xinhua Cao . A giant Ce-containing poly(tungstobismuthate): Synthesis, structure and catalytic performance for the decontamination of a sulfur mustard simulant. Chinese Chemical Letters, 2024, 35(10): 109343-. doi: 10.1016/j.cclet.2023.109343
3. [3]
  Shuangxi Li , Huijun Yu , Tianwei Lan , Liyi Shi , Danhong Cheng , Lupeng Han , Dengsong Zhang . NO_x reduction against alkali poisoning over Ce(SO₄)₂-V₂O₅/TiO₂ catalysts by constructing the Ce⁴⁺–SO₄²⁻ pair sites. Chinese Chemical Letters, 2024, 35(5): 108240-. doi: 10.1016/j.cclet.2023.108240
4. [4]
  Tianbo Jia , Lili Wang , Zhouhao Zhu , Baikang Zhu , Yingtang Zhou , Guoxing Zhu , Mingshan Zhu , Hengcong Tao . Modulating the degree of O vacancy defects to achieve selective control of electrochemical CO₂ reduction products. Chinese Chemical Letters, 2024, 35(5): 108692-. doi: 10.1016/j.cclet.2023.108692
5. [5]
  Shuqi Yu , Yu Yang , Keisuke Kuroda , Jian Pu , Rui Guo , Li-An Hou . Selective removal of Cr(Ⅵ) using polyvinylpyrrolidone and polyacrylamide co-modified MoS₂ composites by adsorption combined with reduction. Chinese Chemical Letters, 2024, 35(6): 109130-. doi: 10.1016/j.cclet.2023.109130
6. [6]
  Jingtai Bi , Yupeng Cheng , Mengmeng Sun , Xiaofu Guo , Shizhao Wang , Yingying Zhao . Efficient and selective photocatalytic nitrite reduction to N₂ through CO₂ anion radical by eco-friendly tartaric acid activation. Chinese Chemical Letters, 2024, 35(11): 109639-. doi: 10.1016/j.cclet.2024.109639
7. [7]
  Mingzhu Jiang , Panqing Wang , Qiheng Chen , Yue Zhang , Qi Wu , Lei Tan , Tianxiang Ning , Lingjun Li , Kangyu Zou . Enabling the Nb/Ti co-doping strategy for improving structure stability and rate capability of Ni-rich cathode. Chinese Chemical Letters, 2025, 36(6): 110040-. doi: 10.1016/j.cclet.2024.110040
8. [8]
  Jiawei Ge , Hao Wan , Feng Gao , Heyuan Tian , Jiangying Qu , Xian Wang , Junjie Ge . B and Sr co-doping suppressed Pt oxidative passivation enables fast water oxidation in PEMWE. Chinese Chemical Letters, 2026, 37(10): 111657-. doi: 10.1016/j.cclet.2025.111657
9. [9]
  Zaisheng Jin , Fuli Wang , Yongjie Shen , Xiaonan Hu , Yanqi Chen , Jin Zhang , Ming Xie , Penglu Wang , Dengsong Zhang . Iron-based catalysts for NO_x reduction: Reaction mechanism and anti-poisoning strategies. Chinese Chemical Letters, 2026, 37(4): 111733-. doi: 10.1016/j.cclet.2025.111733
10. [10]
  Haixia Wu , Kailu Guo . Sulfur reduction reaction mechanism elucidated with in situ Raman spectroscopy. Chinese Chemical Letters, 2025, 36(6): 110654-. doi: 10.1016/j.cclet.2024.110654
11. [11]
  Jingtao Bi , Yupeng Cheng , Mengmeng Sun , Xiaofu Guo , Shizhao Wang , Yingying Zhao . Corrigendum to “Efficient and selective photocatalytic nitrite reduction to N₂ through CO₂ anion radical by eco-friendly tartaric acid activation” [Chinese Chemical Letters 35 (2024) 109639]. Chinese Chemical Letters, 2025, 36(7): 110867-. doi: 10.1016/j.cclet.2025.110867
12. [12]
  Han Yan , Jingming Yao , Zhangran Ye , Qiaoquan Lin , Ziqi Zhang , Shulin Li , Dawei Song , Zhenyu Wang , Chuang Yu , Long Zhang . Al-F co-doping towards enhanced electrolyte-electrodes interface properties for halide and sulfide solid electrolytes. Chinese Chemical Letters, 2025, 36(1): 109568-. doi: 10.1016/j.cclet.2024.109568
13. [13]
  Wenya Li , Yuanqi Yang , Yuqing Yang , Min Liang , Huizi Li , Xi Ke , Liying Liu , Yan Sun , Chunsheng Li , Zhicong Shi , Su Ma . Insights into magnesium and titanium co-doping to stabilize the O3-type NaCrO₂ cathode material for sodium-ion batteries. Chinese Chemical Letters, 2025, 36(10): 110388-. doi: 10.1016/j.cclet.2024.110388
14. [14]
  Lijun Yan , Shiqi Chen , Penglu Wang , Xiangyu Liu , Lupeng Han , Tingting Yan , Yuejin Li , Dengsong Zhang . Hydrothermally stable metal oxide-zeolite composite catalysts for low-temperature NO_x reduction with improved N₂ selectivity. Chinese Chemical Letters, 2024, 35(6): 109132-. doi: 10.1016/j.cclet.2023.109132
15. [15]
  Shanyuan Bi , Jin Zhang , Dengchao Peng , Danhong Cheng , Jianping Zhang , Lupeng Han , Dengsong Zhang . Improved N₂ selectivity for low-temperature NO_x reduction over etched ZSM-5 supported MnCe oxide catalysts. Chinese Chemical Letters, 2025, 36(5): 110295-. doi: 10.1016/j.cclet.2024.110295
16. [16]
  Jianmei Han , Peng Wang , Hua Zhang , Ning Song , Xuguang An , Baojuan Xi , Shenglin Xiong . Performance optimization of chalcogenide catalytic materials in lithium-sulfur batteries: Structural and electronic engineering. Chinese Chemical Letters, 2024, 35(7): 109543-. doi: 10.1016/j.cclet.2024.109543
17. [17]
  Na Li , Wenxue Wang , Peng Wang , Zhanying Sun , Xinlong Tian , Xiaodong Shi . Dual-defect engineering of catalytic cathode materials for advanced lithium-sulfur batteries. Chinese Chemical Letters, 2025, 36(3): 110731-. doi: 10.1016/j.cclet.2024.110731
18. [18]
  Pu ZHANG , Youzhu YU , Yuhua GUO , Zhongyuan ZHOU . Synthesis and photocatalytic CO₂ reduction properties of heterometallic salicylate Mn/Ti clusters. Chinese Journal of Inorganic Chemistry, 2026, 42(8): 1723-1732. doi: 10.11862/CJIC.20260103
19. [19]
  Qian-Qian Tang , Li-Fang Feng , Zhi-Peng Li , Shi-Hao Wu , Long-Shuai Zhang , Qing Sun , Mei-Feng Wu , Jian-Ping Zou . Single-atom sites regulation by the second-shell doping for efficient electrochemical CO₂ reduction. Chinese Chemical Letters, 2024, 35(9): 109454-. doi: 10.1016/j.cclet.2023.109454
20. [20]
  Yuxiang Zhang , Jia Zhao , Sen Lin . Nitrogen doping retrofits the coordination environment of copper single-atom catalysts for deep CO2 reduction. Chinese Journal of Structural Chemistry, 2024, 43(11): 100415-100415. doi: 10.1016/j.cjsc.2024.100415

Get Citation

PDF

XML

Metrics

PDF Downloads(8)
Abstract views(1557)
HTML views(155)

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

Performance of Mn-Ce co-doped siderite catalysts in the selective catalytic reduction of NOx by NH3

Metrics

通讯作者: 陈斌, bchen63@163.com

Performance of Mn-Ce co-doped siderite catalysts in the selective catalytic reduction of NO_x by NH₃