Citation: LI Guo-Min, ZHU Bao-Shun, LIANG Li-Ping, TIAN Yu-Ming, LÜ Bao-Liang, WANG Lian-Cheng. Core-Shell Co₃Fe₇@C Composite as Efficient Microwave Absorbent[J]. Acta Physico-Chimica Sinica, ;2017, 33(8): 1715-1720. doi: 10.3866/PKU.WHXB201704174 shu

Core-Shell Co₃Fe₇@C Composite as Efficient Microwave Absorbent

1.
School of Materials Science and Engineering, Taiyuan University of Science and Technology, Taiyuan 030024, P. R. China;
2.
Key Laboratory of Carbon Materials, Institute of Coal Chemistry, Chinese Academy of Sciences, Taiyuan 030001, P. R. China

Received Date: 6 December 2016
Revised Date: 3 April 2017

Fund Project: The project was supported by the Doctoral Scientific Research Foundation of Taiyuan University of Science and Technology, China (20152030).

To reduce the density of the absorbent Co₃Fe₇, a core-shell Co₃Fe₇@C microwave absorbent was synthesized by preparing an iron/cobalt-containing carbon precursor followed by high-temperature carbonization. According to the X-ray diffraction (XRD) and transmission electron microscopy (TEM) results, Co₃Fe₇ particles were coated with graphitized carbon layers to form a core-shell structure. Furthermore, the Co₃Fe₇@C composite with a surface area and density of 358.5 m²·g^-1 and 2.25 g·cm^-3, respectively, exhibited excellent microwave absorbability. A minimum reflection loss (RL) of -43.5 dB and an effective bandwidth (RL below -10 dB) of 4.1 GHz were obtained at the coating thickness of 2 mm, which could be mainly attributed to the effective impedance match and multiple interfacial polarizations. Owing to the low density and remarkable microwave absorption, we believe that the Co₃Fe₇@C composite can be a promising candidate for use as a lightweight and efficient microwave absorbent.
- Core-shell structure,
- Composite,
- Lightweight,
- Microwave absorption
1. [1]
2. [2]
3. [3]
4. [4]
5. [5]
6. [6]
7. [7]
8. [8]
9. [9]
10. [10]
11. [11]
12. [12]
13. [13]
14. [14]
15. [15]
16. [16]
17. [17]
18. [18]
19. [19]
20. [20]
21. [21]
22. [22]
23. [23]
24. [24]
25. [25]
26. [26]
27. [27]
28. [28]
29. [29]
30. [30]
31. [31]
32. [32]
33. [33]
34. [34]
35. [35]
1. [1]
  Yanan Liu , Xiaogang Su , Di Lan , Jiangyong Liu , Weihai Ma , Yaqing Liu . Bimetallic MOF-derived CoZn-C/MWCNTs composite for lightweight and wideband microwave absorption. Acta Physico-Chimica Sinica, 2026, 42(6): 100276-0. doi: 10.1016/j.actphy.2026.100276
2. [2]
  Endong YANG , Haoze TIAN , Ke ZHANG , Yongbing LOU . Efficient oxygen evolution reaction of CuCo₂O₄/NiFe-layered bimetallic hydroxide core-shell nanoflower sphere arrays. Chinese Journal of Inorganic Chemistry, 2024, 40(5): 930-940. doi: 10.11862/CJIC.20230369
3. [3]
  Shihao Tan , Caiyun Cui , Shuwei Ma , Liangsen Zhu , Xianguo Liu . Introducing nanocrystalline/amorphous heterostructures on laminated FeSiBCr to synchronously enhance absorption, expand absorption bandwidth and reduce matching thickness. Acta Physico-Chimica Sinica, 2026, 42(7): 100283-. doi: 10.1016/j.actphy.2026.100283
4. [4]
  Chen Pu , Daijie Deng , Henan Li , Li Xu . Fe_0.64Ni_0.36@Fe₃NiN Core-Shell Nanostructure Encapsulated in N-Doped Carbon Nanotubes for Rechargeable Zinc-Air Batteries with Ultralong Cycle Stability. Acta Physico-Chimica Sinica, 2024, 40(2): 2304021-0. doi: 10.3866/PKU.WHXB202304021
5. [5]
  Bo Liang , Yuyijian Zhao , Siyu Wang , Shihan Huang , Fangke Zhou , Chuankun Zhang , Yue Wang , Xiaoming Guo . Synergistic molecular assembly and impedance matching in polyimide-derived porous carbon nanosheets for advanced microwave absorption. Acta Physico-Chimica Sinica, 2026, 42(6): 100285-0. doi: 10.1016/j.actphy.2026.100285
6. [6]
  Xiangyu CAO , Jiaying ZHANG , Yun FENG , Linkun SHEN , Xiuling ZHANG , Juanzhi YAN . Synthesis and electrochemical properties of bimetallic-doped porous carbon cathode material. Chinese Journal of Inorganic Chemistry, 2025, 41(3): 509-520. doi: 10.11862/CJIC.20240270
7. [7]
  Longfei MA , Fang SI , Congjie PAN , Xinhua WANG . Synthesis and crystal structure of extended tetrathiafulvalene derivatives and cupric bromide charge transfer complexes. Chinese Journal of Inorganic Chemistry, 2026, 42(6): 1229-1236. doi: 10.11862/CJIC.20250355
8. [8]
  Renwei Feng , Congmin Fan , Di Lan , Lanxiang Liu , Qinchuan He , Yiqun Wang . Anchoring strategy-induced conductive loss in Ni-MOF@expanded graphite composites to achieve broadband microwave absorption. Acta Physico-Chimica Sinica, 2026, 42(8): 100301-0. doi: 10.1016/j.actphy.2026.100301
9. [9]
  Min LI , Xianfeng MENG . Preparation and microwave absorption properties of ZIF-67 derived Co@C/MoS₂ nanocomposites. Chinese Journal of Inorganic Chemistry, 2024, 40(10): 1932-1942. doi: 10.11862/CJIC.20240065
10. [10]
  Shuai Zhang , Haifeng Li , Shijie Zhang , Shun Wang , Suxuan Du , Zhiwei Zhao , Xiaomiao Zhao , Xiaowei Liang . Microwave assisted construction of Ta₂CT_x MXene/CuInS₂ heterostructures toward enhanced dielectric loss and broadband electromagnetic wave absorption. Acta Physico-Chimica Sinica, 2026, 42(8): 100305-0. doi: 10.1016/j.actphy.2026.100305
11. [11]
  Junjie Zhang , Yue Wang , Qiuhan Wu , Ruquan Shen , Han Liu , Xinhua Duan . Preparation and Selective Separation of Lightweight Magnetic Molecularly Imprinted Polymers for Trace Tetracycline Detection in Milk. University Chemistry, 2024, 39(5): 251-257. doi: 10.3866/PKU.DXHX202311084
12. [12]
  Ruolin CHENG , Yue WANG , Xiyao NIU , Huagen LIANG , Ling LIU , Shijian LU . Efficient photothermal catalytic CO₂ cycloaddition over W₁₈O₄₉/rGO composites. Chinese Journal of Inorganic Chemistry, 2025, 41(7): 1276-1284. doi: 10.11862/CJIC.20240424
13. [13]
  Changqing MIAO , Fengjiao CHEN , Wenyu LI , Shujie WEI , Yuqing YAO , Keyi WANG , Ni WANG , Xiaoyan XIN , Ming FANG . Crystal structures, DNA action, and antibacterial activities of three tetranuclear lanthanide-based complexes. Chinese Journal of Inorganic Chemistry, 2024, 40(12): 2455-2465. doi: 10.11862/CJIC.20240192
14. [14]
  Huafeng SHI . Construction of MnCoNi layered double hydroxide@Co-Ni-S amorphous hollow polyhedron composite with excellent electrocatalytic oxygen evolution performance. Chinese Journal of Inorganic Chemistry, 2025, 41(7): 1380-1386. doi: 10.11862/CJIC.20240378
15. [15]
  Siming Bian , Sijie Luo , Junjie Ou . Application of van Deemter Equation in Instrumental Analysis Teaching: A New Type of Core-Shell Stationary Phase. University Chemistry, 2025, 40(3): 381-386. doi: 10.12461/PKU.DXHX202406087
16. [16]
  Zhiyang Li , Hui Deng , Xinqi Cai , Zhuo Chen . Magnetic Core/Shell-Capsules Locally Neutralize Gastric Acid for Efficient Delivery of Active Probiotics. Acta Physico-Chimica Sinica, 2024, 40(7): 2306051-0. doi: 10.3866/PKU.WHXB202306051
17. [17]
  Qiang Wang , Jifan Yang , Xiaolei Su , Yi Liu . La₂O₃ decorated Ti₃C₂T_x MXene: temperature regulation and frequency selective surface synergy for enhanced X-Band microwave absorption. Acta Physico-Chimica Sinica, 2026, 42(8): 100308-0. doi: 10.1016/j.actphy.2026.100308
18. [18]
  Yu Wang , Haiyang Shi , Zihan Chen , Feng Chen , Ping Wang , Xuefei Wang . 具有富电子Pt^δ−壳层的空心AgPt@Pt核壳催化剂：提升光催化H₂O₂生成选择性与活性. Acta Physico-Chimica Sinica, 2025, 41(7): 100081-0. doi: 10.1016/j.actphy.2025.100081
19. [19]
  Fan Wu , Wenchang Tian , Jin Liu , Qiuting Zhang , YanHui Zhong , Zian Lin . Core-Shell Structured Covalent Organic Framework-Coated Silica Microspheres as Mixed-Mode Stationary Phase for High Performance Liquid Chromatography. University Chemistry, 2024, 39(11): 319-326. doi: 10.12461/PKU.DXHX202403031
20. [20]
  Zhongning Tian , Jinyuan Liu , Meng Zhang , Qianqian Jia , Mingbo Liu , Zhenjiang Li , Ting Wang , Wenjie Zhao , Dongwei Ma , Xueli Qi . Constructing selenium-vacancy-rich SiC@CoSe_2−x nanocomposites to boost dipole and interfacial polarization for electromagnetic wave absorption. Acta Physico-Chimica Sinica, 2026, 42(8): 100323-0. doi: 10.1016/j.actphy.2026.100323

Get Citation

PDF

XML

Metrics

PDF Downloads(4)
Abstract views(1243)
HTML views(174)

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

Core-Shell Co3Fe7@C Composite as Efficient Microwave Absorbent

Metrics

通讯作者: 陈斌, bchen63@163.com

Core-Shell Co₃Fe₇@C Composite as Efficient Microwave Absorbent