Citation: ZHAO Xiu-Hua, JIANG Xiao-Yuan, CHEN Hong-Hua, ZHENG Xiao-Ming. Preparation and Characterization of CuO/Ce_0.5Ti_0.5O₂ and Its Catalytic Activity for NO+CO Reaction[J]. Acta Physico-Chimica Sinica, ;2008, 24(06): 1023-1029. doi: 10.3866/PKU.WHXB20080619 shu

Preparation and Characterization of CuO/Ce_0.5Ti_0.5O₂ and Its Catalytic Activity for NO+CO Reaction

1.
Institute of Catalysis, Department of Chemistry, College of Science, Zhejiang University, Hangzhou 310028, P. R. China

Received Date: 27 November 2007
Available Online: 25 April 2008

Using Ce0.5Ti0.5O2 as carrier, CuO/Ce0.5Ti0.5O2 catalysts with different CuO loadings were prepared by the impregnation method. The catalytic activities of the catalysts for NO+CO reaction were examined with a micro-reactor gas chromatography reaction system and the catalysts were characterized by of TPR, XRD, and Raman spectroscopy. It was found that the activity of CuO/Ce0.5Ti0.5O2 for NO+CO reaction was depended on CuO loading, and became maximal when CuO loading was 22% and the calcined temperature was 500 ℃. However, after calcination at 700 ℃ 14%CuO/Ce0.5Ti0.5O2 had the highest activity, possibly due to the formation of CeTi2O6-mixed oxide. The TPR analysis showed that CuO/Ce0.5Ti0.5O2 had four TPRreduction peaks (α, β, γ, and δ peaks). The α and β peaks were the reduction of highly dispersed CuO species; the γpeak was due to the isolated bulk CuO interacted intensively with Ce0.5Ti0.5O2; and the δ peak was due to the bulk CuO on the surface of CuO/Ce0.5Ti0.5O2. As shown by XRD, CuO/Ce0.5Ti0.5O2 calcined at 700 ℃ had new oxide CeTi2O6, and the diffraction peaks of CeTi2O6 became obvious as the calcined temperature increased, indicating that high temperature enhanced solid reaction of Ce and Ti, and formation of CeTi2O6. The Raman results indicated that after calcination Ce0.5Ti0.5O2 was no longer a simple combination of TiO2 and CeO2, but had formed new crystal structure.
- CuO/Ce0.5Ti0.5O2; NO+CO reaction; CeTi2O6; Raman spectroscopy
1. [1]
  Tianlong Zhang , Rongling Zhang , Hongsheng Tang , Yan Li , Hua Li . Online Monitoring and Mechanistic Analysis of 3,5-diamino-1,2,4-triazole (DAT) Synthesis via Raman Spectroscopy: A Recommendation for a Comprehensive Instrumental Analysis Experiment. University Chemistry, 2024, 39(6): 303-311. doi: 10.3866/PKU.DXHX202312006
2. [2]
  Hengyi ZHU , Liyun JU , Haoyue ZHANG , Jiaxin DU , Yutong XIE , Li SONG , Yachao JIN , Mingdao ZHANG . Efficient regeneration of waste LiNi_0.5Co_0.2Mn_0.3O₂ cathode toward high-performance Li-ion battery. Chinese Journal of Inorganic Chemistry, 2025, 41(4): 625-638. doi: 10.11862/CJIC.20240358
3. [3]
  Jingzhuo Tian , Chaohong Guan , Haobin Hu , Enzhou Liu , Dongyuan Yang . Waste plastics promoted photocatalytic H₂ evolution over S-scheme NiCr₂O₄/twinned-Cd_0.5Zn_0.5S homo-heterojunction. Acta Physico-Chimica Sinica, 2025, 41(6): 100068-. doi: 10.1016/j.actphy.2025.100068
4. [4]
  Shiyi WANG , Chaolong CHEN , Xiangjian KONG , Lansun ZHENG , Lasheng LONG . Polynuclear lanthanide compound [Ce₄^ⅢCe₆^Ⅳ(μ₃-O)₄(μ₄-O)₄(acac)₁₄(CH₃O)₆]·2CH₃OH for the hydroboration of amides to amine. Chinese Journal of Inorganic Chemistry, 2025, 41(1): 88-96. doi: 10.11862/CJIC.20240342
5. [5]
  Qin Li , Huihui Zhang , Huajun Gu , Yuanyuan Cui , Ruihua Gao , Wei-Lin Dai . In situ Growth of Cd_0.5Zn_0.5S Nanorods on Ti₃C₂ MXene Nanosheet for Efficient Visible-Light-Driven Photocatalytic Hydrogen Evolution. Acta Physico-Chimica Sinica, 2025, 41(4): 100031-. doi: 10.3866/PKU.WHXB202402016
6. [6]
  Lina Guo , Ruizhe Li , Chuang Sun , Xiaoli Luo , Yiqiu Shi , Hong Yuan , Shuxin Ouyang , Tierui Zhang . 层状双金属氢氧化物的层间阴离子对衍生的Ni-Al₂O₃催化剂光热催化CO₂甲烷化反应的影响. Acta Physico-Chimica Sinica, 2025, 41(1): 2309002-. doi: 10.3866/PKU.WHXB202309002
7. [7]
  Ru SONG , Biao WANG , Chunling LU , Bingbing NIU , Dongchao QIU . Electrochemical properties of stable and highly active PrBa_0.5Sr_0.5Fe_1.6Ni_0.4O_5+δ cathode material. Chinese Journal of Inorganic Chemistry, 2025, 41(4): 639-649. doi: 10.11862/CJIC.20240397
8. [8]
  Dong-Xue Jiao , Hui-Li Zhang , Chao He , Si-Yu Chen , Ke Wang , Xiao-Han Zhang , Li Wei , Qi Wei . Layered (C5H6ON)2[Sb2O(C2O4)3] with a large birefringence derived from the uniform arrangement of π-conjugated units. Chinese Journal of Structural Chemistry, 2024, 43(6): 100304-100304. doi: 10.1016/j.cjsc.2024.100304
9. [9]
  Qiang ZHAO , Zhinan GUO , Shuying LI , Junli WANG , Zuopeng LI , Zhifang JIA , Kewei WANG , Yong GUO . Cu₂O/Bi₂MoO₆ Z-type heterojunction: Construction and photocatalytic degradation properties. Chinese Journal of Inorganic Chemistry, 2024, 40(5): 885-894. doi: 10.11862/CJIC.20230435
10. [10]
  Zhinan GUO , Junli WANG , Qiang ZHAO , Zhifang JIA , Zuopeng LI , Kewei WANG , Yong GUO . Cu₂O/Bi₂CrO₆ Z-scheme heterojunction: Construction and photocatalytic degradation properties for tetracycline. Chinese Journal of Inorganic Chemistry, 2025, 41(4): 741-752. doi: 10.11862/CJIC.20240403
11. [11]
  Wenlong LI , Xinyu JIA , Jie LING , Mengdan MA , Anning ZHOU . Photothermal catalytic CO₂ hydrogenation over a Mg-doped In₂O_3-x catalyst. Chinese Journal of Inorganic Chemistry, 2024, 40(5): 919-929. doi: 10.11862/CJIC.20230421
12. [12]
  Yi Yang , Xin Zhou , Miaoli Gu , Bei Cheng , Zhen Wu , Jianjun Zhang . Femtosecond transient absorption spectroscopy investigation on ultrafast electron transfer in S-scheme ZnO/CdIn₂S₄ photocatalyst for H₂O₂ production and benzylamine oxidation. Acta Physico-Chimica Sinica, 2025, 41(6): 100064-. doi: 10.1016/j.actphy.2025.100064
13. [13]
  Min WANG , Dehua XIN , Yaning SHI , Wenyao ZHU , Yuanqun ZHANG , Wei ZHANG . Construction and full-spectrum catalytic performance of multilevel Ag/Bi/nitrogen vacancy g-C₃N₄/Ti₃C₂T_x Schottky junction. Chinese Journal of Inorganic Chemistry, 2024, 40(6): 1123-1134. doi: 10.11862/CJIC.20230477
14. [14]
  Tianbo Jia , Lili Wang , Zhouhao Zhu , Baikang Zhu , Yingtang Zhou , Guoxing Zhu , Mingshan Zhu , Hengcong Tao . Modulating the degree of O vacancy defects to achieve selective control of electrochemical CO₂ reduction products. Chinese Chemical Letters, 2024, 35(5): 108692-. doi: 10.1016/j.cclet.2023.108692
15. [15]
  Fei ZHOU , Xiaolin JIA . Co₃O₄/TiO₂ composite photocatalyst: Preparation and synergistic degradation performance of toluene. Chinese Journal of Inorganic Chemistry, 2024, 40(11): 2232-2240. doi: 10.11862/CJIC.20240236
16. [16]
  Xinpeng LIU , Liuyang ZHAO , Hongyi LI , Yatu CHEN , Aimin WU , Aikui LI , Hao HUANG . Ga₂O₃ coated modification and electrochemical performance of Li_1.2Mn_0.54Ni_0.13Co_0.13O₂ cathode material. Chinese Journal of Inorganic Chemistry, 2024, 40(6): 1105-1113. doi: 10.11862/CJIC.20230488
17. [17]
  Xiuzheng Deng , Changhai Liu , Xiaotong Yan , Jingshan Fan , Qian Liang , Zhongyu Li . Carbon dots anchored NiAl-LDH@In₂O₃ hierarchical nanotubes for promoting selective CO₂ photoreduction into CH₄. Chinese Chemical Letters, 2024, 35(6): 108942-. doi: 10.1016/j.cclet.2023.108942
18. [18]
  Shuangxi Li , Huijun Yu , Tianwei Lan , Liyi Shi , Danhong Cheng , Lupeng Han , Dengsong Zhang . NO_x reduction against alkali poisoning over Ce(SO₄)₂-V₂O₅/TiO₂ catalysts by constructing the Ce⁴⁺–SO₄²⁻ pair sites. Chinese Chemical Letters, 2024, 35(5): 108240-. doi: 10.1016/j.cclet.2023.108240
19. [19]
  Peng YUE , Liyao SHI , Jinglei CUI , Huirong ZHANG , Yanxia GUO . Effects of Ce and Mn promoters on the selective oxidation of ammonia over V₂O₅/TiO₂ catalyst. Chinese Journal of Inorganic Chemistry, 2025, 41(2): 293-307. doi: 10.11862/CJIC.20240210
20. [20]
  Zhijie Zhang , Xun Li , Huiling Tang , Junhao Wu , Chunxia Yao , Kui Li . Cs₂CuBr₄ perovskite quantum dots confined in mesoporous CuO framework as a p-n type S-scheme heterojunction for efficient CO₂ photoconversion. Chinese Chemical Letters, 2024, 35(11): 109700-. doi: 10.1016/j.cclet.2024.109700

Get Citation

PDF

XML

Metrics

PDF Downloads(2042)
Abstract views(2909)
HTML views(22)

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

Address：Zhongguancun North First Street 2,100190 Beijing, PR China Tel: +86-010-82449177-888

DownLoad: Full-Size Img PowerPoint

Return

Preparation and Characterization of CuO/Ce0.5Ti0.5O2 and Its Catalytic Activity for NO+CO Reaction

Metrics

通讯作者: 陈斌, bchen63@163.com

Preparation and Characterization of CuO/Ce_0.5Ti_0.5O₂ and Its Catalytic Activity for NO+CO Reaction