MOF-Conductive Polymer Composite Film as Electrocatalyst for Oxygen Reduction in Acidic Media

Rui-Xue ZHUGE Peng-Chao SHI Teng ZHANG

Citation:  Rui-Xue ZHUGE, Peng-Chao SHI, Teng ZHANG. MOF-Conductive Polymer Composite Film as Electrocatalyst for Oxygen Reduction in Acidic Media[J]. Chinese Journal of Structural Chemistry, 2022, 41(3): 2203062-2203069. doi: 10.14102/j.cnki.0254-5861.2011-3350 shu

MOF-Conductive Polymer Composite Film as Electrocatalyst for Oxygen Reduction in Acidic Media

English

  • Metal-organic frameworks (MOFs) are a class of 3D porous materials composed of metal ions or clusters and organic linkers[1-7]. Owing to their high surface areas, tunable pore sizes and capability for functionalization, MOFs have found potential applications on gas adsorption[8, 9], separation[10-12], chemical sensing[13, 14], catalysis[15-18], drug delivery[19-22] and many other fields[23, 24] in the past 20 years. Recently, electrochemical applications of MOFs have been also intensively explored[25-32]. MOFs constructed from redox-active metal nodes or redox-active linkers or decorated with redox-active functional groups have been reported as electrocatalysts for oxygen reduction, oxygen evolution or organic electrochemical transformations[33-36]. However, one major drawback of MOFs in electrochemical applications is the insulating nature of most MOF materials, which hinders electron transfer between MOF particles and electrodes[37-42]. Three strategies have been proposed to improve the conductivity of MOFs and MOF-based materials: (i) developing conductive MOFs[37]; (ii) converting MOFs to MOF-derived carbon materials at high temperature[43]; (iii) constructing composite materials with MOFs and conductive matrix such as carbon[44-48], metal nanoparticles[41, 49] or conductive polymers[50-53]. Among these strategies, fabrication of MOF-conductive polymer composites is of particular interest as it allows conductivity improvement as well as the retention of porous MOF structures and well-defined electroactive sites in MOF pores/channels. Moreover, the interaction between MOF particles and conductive polymer matrix can be readily tuned by introducing pendant groups on polymer backbones and MOF particle surfaces, and thus enhanced electron transfer efficiencies can be expected. Although there have been several reports on electrochemical applications of MOF-conductive polymer composites, not much efforts have been put on making such a composite film or membrane device. Such MOF-based, porous and conductive films/membranes will potentially be applied as gas-diffusive or selective electrodes. As most MOFs are ready for inner-surface functionalization, it will open up possibilities for highly selective electrochemical sensing or electrocatalysis.

    In this work, we report the fabrication and oxygen reduction reaction (ORR) catalytic activity of PCN-222(Fe)/PEDOT: PSS (PEDOT = poly(3, 4-ethylenedioxythiophene), PSS = polystyrenesulfonate) film. PCN-222(Fe) is built from redox-active Fe-porphyrin-derived linkers and reported to be active for electrochemical sensing applications[50]. The selfdoping PEDOT: PSS matrix can exhibit conductivity up to 3000 S×cm-1 upon acid treatment[54, 55], which facilitates electron transfer between the electrodes and MOF particles. As a result, the MOF-conductive polymer composite film device showed enhanced electrocatalytic activities compared with the bare PCN-222(Fe) particles.

    PEDOT: PSS (Clevios PH 1000, 1.3 wt.% in water) solution was purchased from H. C. Starck. Nafion® (5 wt.% in lower aliphatic alcohols and water) solution was purchased from Sigma-Aldrich. All other reagents were used as received from multiple suppliers (Adamas, Sinopharm, Strem, etc.) without further purification.

    PCN-222(Fe) nanoparticles were synthesized via a solvothermal method with modified literature procedure[56, 57]. In a typical procedure, 20 mg (0.86 mmol) of ZrCl4 was dissolved in 4 mL DMF in a 20 mL Pyrex vial, to which a mixture of 100 μL H2O, 20 mg FeTCPPCl and 240 μL (4.2 mmol) acetic acid was added. The resulting solution was then put in a preheated oven at 120 ℃ for 15 min. After the reaction mixture was cooled to room temperature, PCN-222(Fe) nanoparticles were separated by centrifugation and subsequently washed with fresh DMF and acetone for several times. The obtained solid was then heated in a DMF/8M HCl mixture at 120 ℃ for 12 hours to completely remove the unreacted ligands and zirconium species, followed by guest exchange with acetone and vacuum-drying to give activated PCN-222(Fe).

    In a typical procedure, 7 mg of PCN-222(Fe) nanoparticles and 40 μL Nafion® solution were added to 1 mL of PEDOT: PSS aqueous solution and sonicated for 1 h to prepare the PCN-222(Fe)/PEDOT: PSS ink (referred to as the "ink" below). 2.2 μL of the ink (7 mg⋅mL−1) was drop-cast onto a polished 3-mm glassy carbon electrode (S = 0.07 cm2), dried under ambient conditions and treated with 50% H2SO4 for 10 min. Subsequently, the electrode was washed with deionized water to remove excess H2SO4 and dried under room temperature. For RDE measurements, similar procedure was applied except that 7.4 μL of the ink was drop-cast onto the 5.6-mm glassy carbon disk electrode (S = 0.25 cm2).

    Cyclic voltammograms (CVs) were recorded on an electrochemical workstation (CHI1140C, CH Instrument). Aqueous solution of H2SO4 (0.5 M, pH = 0.52) was used as the electrolyte in all LSV and CV measurements. Standard threeelectrode setup was applied with a carbon rod counter electrode and a Ag/AgCl/KCl(sat.) reference electrode. Modified glass carbon electrodes (see above) were used as the working electrode. Rotating disk electrode (RDE) measurements were carried out on an electrode rotator (Pine Instrument). Linear sweep voltammograms (LSVs) of RDE measurements were recorded at different rotation rates with a potential scan rate of 10 mV⋅s−1.

    In RDE experiments, n was calculated by Levich equation:

    $ j_\text{L} = 0.20nF\text{C}_\text{O}(\text{D}_\text{O})^{2/3}ω^{1/2}\text{ν}^{-1/6} $

    Here, jL represents the limiting current density; n is the average electron transfer number in ORR; ω is the rotation rate in the unit of rpm; F is the Faraday constant (96485 C⋅mol-1); CO, DO and ν represent the concentration of O2 (1.1 × 10-6 mol⋅cm-3), the diffusion constant of O2 (1.9 × 10-5 cm2⋅s-1) and the kinematics viscosity of the solution (0.01 cm2⋅s−1), respectively.

    Control potential electrolysis was performed in 0.5 M H2SO4 (aq) using a PCN-222(Fe)/PEDOT: PSS film-coated glassy carbon working electrode. Catholyte and anolyte (25 mL each) regions were separated by a Nafion 117 film. After one-hour electrolysis at –0.25 V vs. RHE, 1.0 mL of catholyte was mixed with excess Ce(IV) solution (2.0 mL, 140 μM), while the concentration of residue Ce(IV) was determined by UV-vis spectrometry at 320 nm.

    The amount of hydrogen peroxide produced in electrolysis was calculated according to the consumption of cerium sulfate:

    $ 2\text{Ce}^{4+} + \text{H}_{2}\text{O}_{2} = 2\text{Ce}^{3+} + 2\text{H}^{+} + \text{O}_{2} $

    The formation of pure PCN-222(Fe) phase was confirmed by powder X-ray diffraction (PXRD) patterns (Fig. 1a). Scan electron microscopic (SEM) images (Fig. 2a) showed that the obtained nanoparticles are in rugby shape with an average diameter of 174 nm and length of 348 nm. Inclusion of PCN-222(Fe) particles in the composite film was confirmed by multiple characterization. Inductively coupled plasma optical emission spectroscopic (ICP-OES) analysis (Table S1) gave a Fe content of 1.4% and a Zr content of 6.54% for PCN-222(Fe)/PEDOT: PSS film. Assuming all Fe and Zr elements in the composite film come from PCN-222(Fe), it is calculated that PCN-222(Fe) particles weigh 44 wt.% of the composite film, consistent with the calculation based on material feed (36~43 wt.%). While PEDOT: PSS-only film showed no significant XRD signal, the PCN-222(Fe)/PEDOT: PSS film exhibits characteristic XRD peaks for PCN-222(Fe), showing that the MOF nanoparticles are successfully included in the film and stable under acidic conditions (Fig. 1a). FT-IR spectrum of the composite film (Fig. 1b) displays characteristic 2927 and 999 cm−1 peaks for PCN-222(Fe), which corresponds to C–H and Fe–N stretching vibration, respectively[50, 58, 59]. The morphology of PCN-222(Fe)/PEDOT: PSS film was also explored by scanning electron microscopy (SEM). As shown in Fig. 2b, PCN-222(Fe) nanoparticles distribute evenly in the composite film. The particle distribution was also confirmed by EDS elemental mapping measurements (Fig. S2). Cross-section SEM images shows that the thickness of PCN-222(Fe)/PEDOT: PSS film is approximately 3.5 μm (Fig. 2d), slightly thicker than pure PEDOT: PSS film, which is about 2 μm (Fig. 2c).

    Figure 1

    Figure 1.  (a) XRD patterns of simulated PCN-222(Fe), as-prepared PCN-222(Fe), PEDOT: PSS film and PCN-222(Fe)/PEDOT: PSS film.

    Figure 2

    Figure 2.  (a, b) SEM images of (a) PCN-222(Fe) and (b) PCN-222(Fe)/PEDOT: PSS film. Inset: distribution of particle size. (c, d) Cross-section SEM images of (c) PEDOT: PSS film and (d) PCN-222/PEDOT: PSS film

    The electrochemical performance of PCN-222(Fe)/PEDOT: PSS film was investigated in nitrogen or oxygen saturated 0.5 M H2SO4 with a three-electrode system. Under nitrogen atmosphere, PEDOT: PSS film showed a broad reduction signal down to –0.142 V vs. reversible hydrogen electrode (RHE) and the corresponding oxidation at –0.122 V vs. RHE, which are attributed to the reduction and oxidation of PEDOT backbones (Fig. 3a). PCN-222(Fe)/PEDOT: PSS film showed a reduction peak at 0.078 V vs. RHE, which corresponds to Fe(III)TCPP/Fe(II)TCPP reduction[60-62] (Fig. 3a). In anodic scan, the oxidation peak appears at 0.048 V vs. RHE due to the coexistence of Fe(II)TCPP/Fe(III)TCPP and PEDOT backbone oxidation processes. Both reduction and oxidation peaks on PCN-222(Fe)/PEDOT: PSS film showed linear dependence with CV scan rates (Figs. 3d and S3), consistent with the presence of surface-bounded electroactive Fe-porphyrin species. When PCN-222(Fe) nanoparticles were deposited directly on glassy carbon electrode without making the composite film, no obvious oxidation or reduction peaks were observed (Fig. 3a). In oxygen-saturated 0.5 M H2SO4 electrolyte (Fig. 3b), the oxygen reduction peak on PCN-222(Fe)/PEDOT: PSS film electrode appears at 0.156 V vs. RHE with a peak current density of 2.18 mA·cm−2. The ORR peak currents showed typical diffusive behavior with linear dependence with the square root of CV scan rates (Fig. 3f), showing that the final electroactive species is dissolved oxygen. In this case, the FeIII/II reduction peak cannot be clearly differentiated due to the rapid reaction between the generated Fe(II)TCPP and O2[60]. A well-defined adsorptive Fe(II)TCPP-Fe(III)TCPP oxidation peak is found at 0.083 V vs. RHE(Fig. 3b) during anodic scans, indicating good reversibility of the FeIII/II reduction process. Remarkably, oxygen reduction on PCN-222(Fe)/PEDOT: PSS film takes place at more positive potential and exhibits a higher peak current density than those of PCN-222(Fe) nanoparticles (0.043 V vs. RHE; 0.64 mA·cm−2). These results clearly indicate that the ORR performance of PCN-222(Fe) is significantly improved through inclusion in conductive PEDOT: PSS matrix. Such enhanced electrochemical performance of MOF-conductive polymer composite can be attributed to better electron transfer rate between the MOF nanoparticles and electrode through conductive polymer matrix.

    Figure 3

    Figure 3.  (a, b) Cyclic voltammograms (CVs) of PCN-222(Fe), PEDOT: PSS film and PCN-222(Fe)/PEDOT: PSS film in (a) N2 or (b) O2-saturated 0.5 M H2SO4 electrolyte at a scan rate of 100 mV·s−1. (c, e) The CVs of the PCN-222(Fe)/PEDOT: PSS film in (c) N2 or (e) O2-saturated 0.5 M H2SO4 electrolyte at different scan rates (10~200 mV·s−1). (d) The plot of reduction peak current density (jp) vs. scan rate (v) in N2-saturated 0.5 M H2SO4 electrolyte. (f) The plot of reduction peak current density (jp) vs. the square root of scan rate (v 1/2) in O2-saturated 0.5 M H2SO4 electrolyte

    The ORR performance and mechanism of PCN-222(Fe)/PEDOT: PSS film were further studied by rotating disk electrode (RDE) techniques. PCN-222(Fe)/PEDOT: PSS film exhibits an oxygen reduction half-wave potential of 0.28 V vs. RHE, more positive than PCN-222(Fe) or PEDOT: PSS only film (Fig. 4a). The composite film also shows a higher ORR limiting current of 2.5 mA⋅cm-2 than the two components separately. Therefore, the composite film has better ORR activity than either PEDOT: PSS only film or PCN-222(Fe) nanoparticles, showing that the synergistic effect between the two components does enhance its performance. While the rotation rates increase from 400 to 1600 rpm, the ORR limiting current densities of PCN-222(Fe)/PEDOT: PSS film increase gradually from 1.39 to 2.45 mA·cm-2 (Fig. 4b). Fitting the Levich plot (jL vs. ω1/2) from 400 to 1600 rpm gave an n value between 1.9~2.0 at the potential range from –0.07 to –0.27 V vs. RHE (Fig. 4c). These results indicates that 2-electron (O2 to H2O2) reduction process dominates on the PCN-222(Fe)/PEDOT: PSS film electrode.

    Figure 4

    Figure 4.  (a) RDE linear sweep voltammograms (LSVs) of PCN-222(Fe)/PEDOT: PSS film, PEDOT: PSS film, PCN-222(Fe) and Pt/C in O2-saturated 0.5 M H2SO4 electrolyte at a rotation rate of 1600 rpm. (b) RDE LSVs of PCN-222(Fe)/PEDOT: PSS film in O2-saturated 0.5 M H2SO4 electrolyte at various rotation rates. (c) Levich plots (jL vs. ω1/2) of PCN-222(Fe)/PEDOT: PSS film. (d) It curves of PCN-222(Fe)/PEDOT: PSS at −0.25 V vs RHE

    Rotating ring-disk electrode (RRDE) studies were further utilized to examine the amount of H2O2 produced during ORR processes. Surprisingly, RRDE measurements gave an apparent electron transfer number (n) between 3.7~3.8 and H2O2 yield of 8.6% at the potential range below 0.14V vs. RHE (Fig. S6). This result is inconsistent with the above RDE results, which suggests a two-electron process that dominates the ORR process on PCN-222(Fe)/PEDOT: PSS film electrode. Therefore, we next quantified the production of H2O2 by Ce(IV) spectrometric titration. Electrolysis at –0.25 V vs. RHE gave a current density of about 0.5 mA⋅cm-2 (Fig. 4d). After one-hour electrolysis, the catholyte was collected and analyzed by UV-vis spectrum. The production rate and Faraday efficiency of hydrogen peroxide production are calculated to be 57.4 mmol⋅g-1⋅h-1 and 76%, respectively. The UV-vis quantification results correspond to an n value of 2.5, slightly higher than that from Levich plot but inconsistent with RRDE. We thus conclude that RRDE is not an accurate technique for hydrogen peroxide detection in our system, probably because hydrogen peroxide can be trapped in the MOF pores and fails to diffuse rapidly into the electrolyte. In this scenario, the apparent ring collection efficiency is lower, and hydrogen peroxide cannot be detected quantitatively by the ring electrode. This H2O2 trapping effect also accounts for the lower H2O2 production efficiency as detected in UV-vis experiment than in Levich plot. In a word, it can be concluded that PCN-222(Fe)/PEDOT: PSS film is a two-electron ORR catalyst in acidic media. The absence of a strong interaction between MOF and PEDOT matrix may limit the rate of electron transfer and the reduction of H2O2. Introduction of pendant carboxylic groups on polymer backbones could possibily enhance the interaction of polymer and MOF particles, and thus improve the performance of composite material.

    In this study, we constructed a MOF-conductive polymer composite film by combining PCN-222(Fe) particles and conductive PEDOT: PSS polymer. The conductive PEDOT: PSS matrix is expected to facilitate electron transfer between electrode and PCN-222(Fe) particles and lead to better electrocatalytic performance. As a proof-of-concept study, we tested the ORR activity of the composite film, which showed enhanced performance compared with PCN-222(Fe) particles or PEDOT: PSS only film. This study thus provides an example how conductive polymer matrix can improve the electrochemical performance of intrinsically non-conductive MOFs. We believe that the fabrication of MOF-conductive polymer composite materials will open up the possibilities for MOFs in multiple electrochemical applications such as electrocatalysis, energy storage and electrochemical sensing.


    The authors thank Ms. Ya-Qi Cui, Dr. Chu-Xin Wu and Prof. Lun-Hui Guan for the help on RDE measurements
    1. [1]

      Furukawa, H.; Cordova, K. E.; O'Keeffe, M.; Yaghi, O. M. The chemistry and applications of metal-organic frameworks. Science 2013, 341, 1230444−12. doi: 10.1126/science.1230444

    2. [2]

      Wang, Z.; Cohen, S. M. Postsynthetic modification of metal-organic frameworks. Chem. Soc. Rev. 2009, 38, 1315−1329. doi: 10.1039/b802258p

    3. [3]

      Kreno, L. E.; Leong, K.; Farha, O. K.; Allendorf, M.; Hupp, J. T. Metal-organic framework materials as chemical sensors. Chem. Rev. 2012, 112, 1105−1125. doi: 10.1021/cr200324t

    4. [4]

      Stock, N.; Biswas, S. Synthesis of metal-organic frameworks (MOFs): routes to various MOF topologies, morphologies, and composites. Chem. Rev. 2012, 112, 933−969. doi: 10.1021/cr200304e

    5. [5]

      Jiao, L.; Wang, Y.; Jiang, H. L.; Qiang, X. Metal-organic frameworks as platforms for catalytic applications. Adv. Mater. 2018, 30, 1703663−23. doi: 10.1002/adma.201703663

    6. [6]

      Yuan, S.; Feng, L.; Wang, K.; Pang, J.; Bosch, M.; Lollar, C.; Sun, Y.; Qin, J.; Yang, X.; Zhang, P. Stable metal-organic frameworks: design, synthesis, and applications. Adv. Mater. 2018, 30, 1704303−35. doi: 10.1002/adma.201704303

    7. [7]

      Wu, Z.; Guo, S.; Kong, L. H. Doping [Ru(bpy)3]2+ into metal-organic framework to facilitate the separation and reuse of noble-metal photosensitizer during CO2 photoreduction. Chin. J. Catal. 2021, 42, 1790−1797. doi: 10.1016/S1872-2067(21)63820-2

    8. [8]

      Li, J. R.; Kuppler, R. J.; Zhou, H. C. Selective gas adsorption and separation in metal-organic frameworks. Chem. Soc. Rev. 2009, 38, 1477−1504. doi: 10.1039/b802426j

    9. [9]

      Woellner, M.; Hausdorf, S.; Klein, N.; Mueller, P.; Martin, W. S.; Kaskel, S. Adsorption and detection of hazardous trace gases by metal-organic frameworks. Adv. Mater. 2018, 30, 1704679. doi: 10.1002/adma.201704679

    10. [10]

      Lin, R. B.; Xiang, S. C.; Zhou, W.; Chen, B. Microporous metal-organic framework materials for gas separation. Chem. 2020, 6, 337−363. doi: 10.1016/j.chempr.2019.10.012

    11. [11]

      Shah, M.; McCarthy, M. C.; Sachdeva, S.; Lee, A. K.; Jeong, H. K. Current status of metal-organic framework membranes for gas separations: promises and challenges. Ind. Eng. Chem. Res. 2012, 51, 2179−2199. doi: 10.1021/ie202038m

    12. [12]

      Kang, Z. X.; Fan, L. L.; Sun, D. F. Recent advances and challenges of metal-organic framework membranes for gas separation. J. Mater. Chem. A 2017, 5, 10073−10091. doi: 10.1039/C7TA01142C

    13. [13]

      Hu, Z.; Deibert, B. J.; Li, J. Luminescent metal-organic frameworks for chemical sensing and explosive detection. Chem. Soc. Rev. 2014, 43, 5815−5840. doi: 10.1039/C4CS00010B

    14. [14]

      Yao, M. S.; Li, W. H.; Xu, G. Metal-organic frameworks and their derivatives for electrically-transduced gas sensors. Coord. Chem. Rev. 2021, 426, 213479−34. doi: 10.1016/j.ccr.2020.213479

    15. [15]

      Chen, L.; Xu, Q. Metal-organic framework composites for catalysis. Matter 2019, 1, 57−89. doi: 10.1016/j.matt.2019.05.018

    16. [16]

      Bavykina, A.; Kolobov, N.; Khan, I. S.; Bau, J. A.; Gascon, J. Metal-organic frameworks in heterogeneous catalysis: recent progress, new trends, and future perspectives. Chem. Rev. 2020, 120, 8468−8535. doi: 10.1021/acs.chemrev.9b00685

    17. [17]

      Huang, Y. B.; Liang, J.; Wang, X. S.; Cao, R. Multifunctional metal-organic framework catalysts: synergistic catalysis and tandem reactions. Chem. Soc. Rev. 2017, 46, 126−157. doi: 10.1039/C6CS00250A

    18. [18]

      Zhuo, T. C.; Song, Y.; Zhuang, G. L.; Chang, L. P.; Zhang, Z. M. H-bond-mediated selectivity control of formate versus CO during CO2 photoreduction with two cooperative Cu/X sites. J. Am. Chem. Soc. 2021, 143, 6114−6122. doi: 10.1021/jacs.0c13048

    19. [19]

      Wang, L.; Zheng, M.; Xie, Z. Nanoscale metal-organic frameworks for drug delivery: a conventional platform with new promise. J. Mater. Chem. B 2018, 6, 707−717. doi: 10.1039/C7TB02970E

    20. [20]

      Wang, Y.; Yan, J.; Wen, N. Metal-organic frameworks for stimuli-responsive drug delivery. Biomaterials 2020, 230, 119619−26. doi: 10.1016/j.biomaterials.2019.119619

    21. [21]

      Della Rocca, J.; Liu, D.; Lin, W. Nanoscale metal-organic frameworks for biomedical imaging and drug delivery. Acc. Chem. Res. 2011, 44, 957−968. doi: 10.1021/ar200028a

    22. [22]

      He, C.; Liu, D.; Lin, W. Nanomedicine applications of hybrid nanomaterials built from metal-ligand coordination bonds: nanoscale metal-organic frameworks and nanoscale coordination polymers. Chem. Rev. 2015, 115, 11079−11108. doi: 10.1021/acs.chemrev.5b00125

    23. [23]

      Yoon, M.; Suh, K.; Natarajan, S. Proton conduction in metal-organic frameworks and related modularly built porous solids. Angew. Chem. Int. Ed. 2013, 52, 2688−2700. doi: 10.1002/anie.201206410

    24. [24]

      Li, A. L.; Gao, Q.; Xu, J. Proton-conductive metal-organic frameworks: recent advances and perspectives. Coord. Chem. Rev. 2017, 344, 54−82. doi: 10.1016/j.ccr.2017.03.027

    25. [25]

      Li, J. H.; Wang, Y. S.; Chen, Y. C.; Kun, C. W. Metal-organic frameworks toward electrocatalytic applications. Appl. Sci. 2019, 9, 2427−19. doi: 10.3390/app9122427

    26. [26]

      Lu, X. F.; Xia, B. Y.; Zang, S. Q. Metal-organic frameworks based electrocatalysts for the oxygen reduction reaction. Angew. Chem. Int. Ed. 2020, 59, 4634−4650. doi: 10.1002/anie.201910309

    27. [27]

      Liao, P. Q.; Shen, J. Q.; Zhang, J. P. Metal-organic frameworks for electrocatalysis. Coord. Chem. Rev. 2018, 373, 22−48. doi: 10.1016/j.ccr.2017.09.001

    28. [28]

      Ko, M.; Mendecki, L.; Eagleton, A. M.; Durbin, C. G.; Mirica, K. A. Employing conductive metal-organic frameworks for voltammetric detection of neurochemicals. J. Am. Chem. Soc. 2020, 142, 11717−11733. doi: 10.1021/jacs.9b13402

    29. [29]

      Liu, L. T.; Zhou, Y. L.; Liu, S.; Mao, T. The applications of metal organic frameworks in electrochemical sensors. ChemElectroChem. 2018, 5, 6−19. doi: 10.1002/celc.201700931

    30. [30]

      Morozan, A.; Jaouen, F. Metal organic frameworks for electrochemical applications. Energy Environ. Sci. 2012, 5, 9269−9290. doi: 10.1039/c2ee22989g

    31. [31]

      Wang, H. F.; Chen, L.; Pang, H.; Kaskel, S.; Xu, Q. MOF-derived electrocatalysts for oxygen reduction, oxygen evolution and hydrogen evolution reactions. Chem. Soc. Rev. 2020, 49, 1414−1448. doi: 10.1039/C9CS00906J

    32. [32]

      Xia, W.; Mahmood, A.; Zou, R. Q. Metal-organic frameworks and their derived nanostructures for electrochemical energy storage and conversion. Energy Environ. Sci. 2015, 8, 1837−1866. doi: 10.1039/C5EE00762C

    33. [33]

      Zhao, S.; Wang, Y.; Dong, J.; He, C. T.; Tang, Z. Y. Ultrathin metal-organic framework nanosheets for electrocatalytic oxygen evolution. Nat. Energy 2016, 1, 1−10.

    34. [34]

      Jia, G.; Gao, Y. F.; Zhang, W.; Cao, Z.; Li, C.; Liu, J. Metal-organic frameworks as heterogeneous catalysts for electrocatalytic oxidative carbonylation of methanol to dimethyl carbonate. Electrochem. Commun. 2013, 34, 211−214. doi: 10.1016/j.elecom.2013.06.013

    35. [35]

      Lions, M.; Tommasino, J. B.; Chattot, R.; Abeykoon, B.; Fateeva, A. Insights into the mechanism of electrocatalysis of the oxygen reduction reaction by a porphyrinic metal organic framework. Chem. Commun. 2017, 53, 6496−6499. doi: 10.1039/C7CC02113E

    36. [36]

      Zhang, C. Y.; Wang, M. Y.; Liu, L.; Xu, X. Electrochemical investigation of a new Cu-MOF and its electrocatalytic activity towards H2O2 oxidation in alkaline solution. Electrochem. Commun. 2013, 33, 131−134. doi: 10.1016/j.elecom.2013.04.026

    37. [37]

      Sun, L.; Campbell, M. G.; Dinca, M. Electrically conductive porous metal-organic frameworks. Angew. Chem. Int. Ed. Engl. 2016, 55, 3566−3579. doi: 10.1002/anie.201506219

    38. [38]

      Wang, T. C.; Hod, I.; Audu, C. O.; Vermeulen, N. A.; Nguyen, S. T.; Farha, O. K.; Hupp, J. T. Rendering high surface area, mesoporous metal-organic frameworks electronically conductive. ACS Appl. Mater. Interfaces 2017, 9, 12584−12591. doi: 10.1021/acsami.6b16834

    39. [39]

      Huang, T. Y.; Kung, C. W.; Liao, Y. T.; Wu, K. C. Enhanced charge collection in MOF-525-PEDOT nanotube composites enable highly sensitive biosensing. Adv. Sci. 2017, 4, 1700261−8. doi: 10.1002/advs.201700261

    40. [40]

      Kung, C. W.; Li, Y. S.; Lee, M. H.; Wang, S. Y.; Chang, W. H. In situ growth of porphyrinic metal-organic framework nanocrystals on graphene nanoribbons for the electrocatalytic oxidation of nitrite. J. Mater. Chem. A 2016, 4, 10673−10682. doi: 10.1039/C6TA02563C

    41. [41]

      Wang, Y.; Wang, L.; Chen, H.; Ma, S. Fabrication of highly sensitive and stable hydroxylamine electrochemical sensor based on gold nanoparticles and metal-metalloporphyrin framework modified electrode. ACS Appl. Mater. Interfaces 2016, 8, 18173−18181. doi: 10.1021/acsami.6b04819

    42. [42]

      Chen, J.; Xu, Q.; Shu, Y.; Hu, X. Y. Synthesis of a novel Au nanoparticles decorated Ni-MOF/Ni/NiO nanocomposite and electrocatalytic performance for the detection of glucose in human serum. Talanta 2018, 184, 136−142. doi: 10.1016/j.talanta.2018.02.057

    43. [43]

      Ma, S.; Goenaga, G. A.; Call, A. V.; Liu, D. J. Cobalt imidazolate framework as precursor for oxygen reduction reaction electrocatalysts. Chem. Eur. J. 2011, 17, 2063−2067. doi: 10.1002/chem.201003080

    44. [44]

      Jahan, M.; Bao, Q.; Loh, K. P. Electrocatalytically active graphene-porphyrin MOF composite for oxygen reduction reaction. J. Am. Chem. Soc. 2012, 134, 6707−6713. doi: 10.1021/ja211433h

    45. [45]

      Zhang, Y.; Bo, X.; Luhana, C.; Wang, H.; Li, M.; Guo, L. Facile synthesis of a Cu-based MOF confined in macroporous carbon hybrid material with enhanced electrocatalytic ability. Chem. Commun. 2013, 49, 6885−6887. doi: 10.1039/c3cc43292k

    46. [46]

      Hu, X. Y.; Wang, Y.; Ge, H.; Ye, G.; Chen, H. H. Carbon functionalized metal organic framework/nafion composites as novel electrode materials for ultrasensitive determination of dopamine. J. Mater. Chem. B 2015, 3, 3747−3753. doi: 10.1039/C4TB01869A

    47. [47]

      Xu, G. D.; Zuo, Y. X.; Huang, B. Metal-organic framework-74-Ni/carbon nanotube composite as sulfur host for high performance lithium-sulfur batteries. J. Electroanal. Chem. 2018, 830, 43−49.

    48. [48]

      Xiong, W.; Li, H.; You, H.; Cao, M. N.; Cao, R. Encapsulating metal organic framework into hollow mesoporous carbon sphere as efficient oxygen bifunctional electrocatalyst. Natl. Sci. Rev. 2020, 7, 609−619. doi: 10.1093/nsr/nwz166

    49. [49]

      Xu, Z.; Yang, L.; Xu, C. Pt@UiO-66 heterostructures for highly selective detection of hydrogen peroxide with an extended linear range. Anal. Chem. 2015, 87, 3438−3444. doi: 10.1021/ac5047278

    50. [50]

      Chen, Y.; Sun, X.; Biswas, S.; Xie, Y.; Wang, Y.; Hu, X. Integrating polythiophene derivates to PCN-222(Fe) for electrocatalytic sensing of L-dopa. Biosens. Bioelectron. 2019, 141, 111470−8. doi: 10.1016/j.bios.2019.111470

    51. [51]

      Wang, Y.; Wang, L.; Huang, W. A metal-organic framework and conducting polymer based electrochemical sensor for high performance cadmium ion detection. J. Mater. Chem. A 2017, 5, 8385−8393. doi: 10.1039/C7TA01066D

    52. [52]

      Liang, X. Q.; Zhang, F.; Feng, W.; Zou, X. Q.; Zhao, C. J.; Na, H.; Liu, C.; Sun, F. X.; Zhu, G. S. From metal-organic framework (MOF) to MOF-polymer composite membrane: enhancement of low-humidity proton conductivity. Chem. Sci. 2013, 4, 983−992. doi: 10.1039/C2SC21927A

    53. [53]

      Jiang, H.; Liu, X. C.; Wu, Y. Metal-organic frameworks for high charge-discharge rates in lithium-sulfur batteries. Angew. Chem. Int. Ed. 2018, 57, 3916−3921. doi: 10.1002/anie.201712872

    54. [54]

      Xia, Y.; Sun, K.; Ouyang, J. Solution-processed metallic conducting polymer films as transparent electrode of optoelectronic devices. Adv. Mater. 2012, 24, 2436−2440. doi: 10.1002/adma.201104795

    55. [55]

      Kim, N.; Kee, S.; Lee, S. H. Highly conductive PEDOT: PSS nanofibrils induced by solution-processed crystallization. Adv. Mater. 2014, 26, 2268−2272. doi: 10.1002/adma.201304611

    56. [56]

      Feng, D. W.; Gu, Z. Y.; Li, J. R.; Jiang, H. L.; Wei, Z. W. Zirconium-metalloporphyrin PCN-222: mesoporous metal-organic frameworks with ultrahigh stability as biomimetic catalysts. Angew. Chem. Int. Ed. 2012, 51, 10307−10310. doi: 10.1002/anie.201204475

    57. [57]

      He, T.; Xu, X.; Ni, B.; Wang, H.; Yong, L.; Hu, W.; Xun, W. Fast and scalable synthesis of uniform zirconium-, hafnium-based metal-organic framework nanocrystals. Nanoscale 2017, 9, 19209−19215. doi: 10.1039/C7NR06274E

    58. [58]

      Sohrabi, S.; Dehghanpour, S.; Ghalkhani, M. Three-dimensional metal-organic framework graphene nanocomposite as a highly efficient and stable electrocatalyst for the oxygen reduction reaction in acidic media. ChemCatChem. 2016, 8, 2356−2366. doi: 10.1002/cctc.201600298

    59. [59]

      Shi, L.; Yang, L. Q.; Zhang, H. B.; Chang, K.; Zhao, G.; Kako, T.; Ye, J. Implantation of iron(III) in porphyrinic metal organic frameworks for highly improved photocatalytic performance. Appl. Catal. B 2018, 224, 60−68. doi: 10.1016/j.apcatb.2017.10.033

    60. [60]

      Usov, P. M.; Huffman, B.; Epley, C. C.; Matthew, C. Study of electrocatalytic properties of metal-organic framework PCN-223 for the oxygen reduction reaction. ACS Appl. Mater. Interfaces 2017, 9, 33539−33543. doi: 10.1021/acsami.7b01547

    61. [61]

      Kadish, K. M.; Morrison, M. M.; Constant, L. A.; Dickens, L.; Davis, D. G. A study of solvent and substituent effects on the redox potentials and electron-transfer rate constants of substituted iron meso-tetraphenylporphyrins. J. Am. Chem. Soc. 1976, 98, 8387−8390. doi: 10.1021/ja00442a013

    62. [62]

      Hod, I.; Sampson, M. D.; Deria, P. Fe-porphyrin-based metal-organic framework films as high-surface concentration, heterogeneous catalysts for electrochemical reduction of CO2. ACS Catal. 2015, 5, 6302−6309. doi: 10.1021/acscatal.5b01767

  • Figure 1  (a) XRD patterns of simulated PCN-222(Fe), as-prepared PCN-222(Fe), PEDOT: PSS film and PCN-222(Fe)/PEDOT: PSS film.

    Figure 2  (a, b) SEM images of (a) PCN-222(Fe) and (b) PCN-222(Fe)/PEDOT: PSS film. Inset: distribution of particle size. (c, d) Cross-section SEM images of (c) PEDOT: PSS film and (d) PCN-222/PEDOT: PSS film

    Figure 3  (a, b) Cyclic voltammograms (CVs) of PCN-222(Fe), PEDOT: PSS film and PCN-222(Fe)/PEDOT: PSS film in (a) N2 or (b) O2-saturated 0.5 M H2SO4 electrolyte at a scan rate of 100 mV·s−1. (c, e) The CVs of the PCN-222(Fe)/PEDOT: PSS film in (c) N2 or (e) O2-saturated 0.5 M H2SO4 electrolyte at different scan rates (10~200 mV·s−1). (d) The plot of reduction peak current density (jp) vs. scan rate (v) in N2-saturated 0.5 M H2SO4 electrolyte. (f) The plot of reduction peak current density (jp) vs. the square root of scan rate (v 1/2) in O2-saturated 0.5 M H2SO4 electrolyte

    Figure 4  (a) RDE linear sweep voltammograms (LSVs) of PCN-222(Fe)/PEDOT: PSS film, PEDOT: PSS film, PCN-222(Fe) and Pt/C in O2-saturated 0.5 M H2SO4 electrolyte at a rotation rate of 1600 rpm. (b) RDE LSVs of PCN-222(Fe)/PEDOT: PSS film in O2-saturated 0.5 M H2SO4 electrolyte at various rotation rates. (c) Levich plots (jL vs. ω1/2) of PCN-222(Fe)/PEDOT: PSS film. (d) It curves of PCN-222(Fe)/PEDOT: PSS at −0.25 V vs RHE

  • 加载中
计量
  • PDF下载量:  0
  • 文章访问数:  51
  • HTML全文浏览量:  7
文章相关
  • 发布日期:  2022-03-01
  • 收稿日期:  2021-09-01
  • 接受日期:  2021-11-18
通讯作者: 陈斌, bchen63@163.com
  • 1. 

    沈阳化工大学材料科学与工程学院 沈阳 110142

  1. 本站搜索
  2. 百度学术搜索
  3. 万方数据库搜索
  4. CNKI搜索

/

返回文章