Citation: ZHOU Qi, LI Zhi-Yang, ZHENG Bin. Preparation and Electrochemical Performance of Nanoporous Bimetallic Oxide NiCo₂O₄[J]. Chinese Journal of Inorganic Chemistry, ;2018, 34(6): 1103-1109. doi: 10.11862/CJIC.2018.146 shu

Preparation and Electrochemical Performance of Nanoporous Bimetallic Oxide NiCo₂O₄

State Key Laboratory of Advanced Processing and Recycling of Nonferrous Metals, Lanzhou University of Technology, Lanzhou 730050, China

Corresponding author: ZHOU Qi, zhouxq301@sina.com
Received Date: 21 January 2018
Revised Date: 26 March 2018

Figures(7)

Nanoporous Ni and Ni-Co alloys were prepared by a method of rapid quenching and de-alloying, and the samples were corroded and annealed to synthesize the nanoporous NiO and NiCo₂O₄ material respectively. The composition, morphology and microstructure of NiO and NiCo₂O₄ were analyzed by XRD, SEM, TEM and N₂ adsorption-desorption. The electrochemical performance was investigated by cyclic voltammetry and galvanostatic charge-discharge. The results show that the porous NiO has a uniform "mud crack" structure. The specific capacitance of nanoporous NiO is 375 F·g^-1 at current density of 1 A·g^-1 and its retention ratio remains at 67.5% when the current density increases to 20 A·g^-1. After galvanostatic charge-discharge 1 000 cycles at 4 A·g^-1, the retention ratio of specific capacitance is 81.7%. The porous NiCo₂O₄ has a lamellar structure. The specific capacitance of nanoporous NiCo₂O₄ is 674 F·g^-1 at current density of 1 A·g^-1 and its retention ratio remains at 72.0% when the current density increases to 20 A·g^-1. After galvanostatic charge-discharge 1 000 cycles at 4 A·g^-1, the retention ratio of specific capacitance is 92.9%. NiCo₂O₄ shows superior supercapacitive performance because of the mechanical stability of the bicontinuous nanoporous structure.
- rapid quenching,
- de-alloying,
- metallic oxide,
- electrochemical performance
1. [1]
  Viswanathan B. An Introduction to Energy Sources. Madras: National Center for Catalysis Research Department of Chem-istry Indian Institute of Technology, 2006: 289
2. [2]
  Burke A. J. Power Sources, 2000, 91(1):37-50 doi: 10.1016/S0378-7753(00)00485-7
3. [3]
  Long J W, Swider K E, Merzbacher C I, et al. Langmuir, 1999, 15(3):780-785 doi: 10.1021/la980785a
4. [4]
  Nam K W, Kim K B. J. Electrochem. Soc., 2002, 149(3):A346-A354 doi: 10.1149/1.1449951
5. [5]
  Zhao D D, Xu M W, Zhou W J, et al. Electrochim. Acta, 2008, 53(6):2699-2705 doi: 10.1016/j.electacta.2007.07.053
6. [6]
  Hu C C, Cheng C Y. Electrochem. Solid-State Lett., 2002, 5(3):A43-A46 doi: 10.1149/1.1448184
7. [7]
  Fu H Y, Wang Z Y, Li Y H, et al. Mater. Res. Innovations, 2015, 19(4):S255-S259
8. [8]
  Lu X, Bischoff E, Spolenak R, et al. Scr. Mater., 2007, 56(7):557-560 doi: 10.1016/j.scriptamat.2006.12.022
9. [9]
  Snyder J, Asanithi P, Dalton A B, et al. Adv. Mater., 2008, 20(24):4883-4886 doi: 10.1002/adma.v20:24
10. [10]
  Dan Z, Qin F, Makino A, et al. J. Alloys Compd., 2014, 586(5):S134-S138
11. [11]
  Erlebacher J, Aziz M J, Karma A, et al. Nature, 2001, 410(22):450-453
12. [12]
  Ding Y, Kim Y J, Erlebacher J. Adv. Mater., 2004, 16(21):1897-1990 doi: 10.1002/(ISSN)1521-4095
13. [13]
14. [14]
  Erlebacher J, Sieradzki K. Scr. Mater., 2003, 49(10):991-996 doi: 10.1016/S1359-6462(03)00471-8
15. [15]
  ZHOU Qi, ZHENG Bin, LI Zhi-Yang, et al. Chinese J. Inorg Chem., 2017, 33(8):1416-1422 doi: 10.11862/CJIC.2017.145
16. [16]
  Wu Z B, Pu X L, Zhu Y R, et al. J. Alloys Compd., 2015, 632:208-217 doi: 10.1016/j.jallcom.2015.01.147
17. [17]
  Kuang M, Zhang W, Guo X L, et al. Ceram. Int., 2014, 40(7):10005-10011 doi: 10.1016/j.ceramint.2014.02.099
18. [18]
  Hosogai S, Tsutsumi H. J. Power Sources, 2009, 194(2):1213-1217 doi: 10.1016/j.jpowsour.2009.06.044
19. [19]
  Toupin M, Brousse T, Bélanger D. Chem. Mater., 2004, 16(16):3184-3190 doi: 10.1021/cm049649j
1. [1]
  Ping ZHANG , Chenchen ZHAO , Xiaoyun CUI , Bing XIE , Yihan LIU , Haiyu LIN , Jiale ZHANG , Yu'nan CHEN . Preparation and adsorption-photocatalytic performance of ZnAl@layered double oxides. Chinese Journal of Inorganic Chemistry, 2024, 40(10): 1965-1974. doi: 10.11862/CJIC.20240014
2. [2]
  Chuanming GUO , Kaiyang ZHANG , Yun WU , Rui YAO , Qiang ZHAO , Jinping LI , Guang LIU . Performance of MnO₂-0.39IrO_x composite oxides for water oxidation reaction in acidic media. Chinese Journal of Inorganic Chemistry, 2024, 40(6): 1135-1142. doi: 10.11862/CJIC.20230459
3. [3]
  Kun Xu , Xinxin Song , Zhilei Yin , Jian Yang , Qisheng Song . Comprehensive Experimental Design of Preferential Orientation of Zinc Metal by Heat Treatment for Enhanced Electrochemical Performance. University Chemistry, 2024, 39(4): 192-197. doi: 10.3866/PKU.DXHX202309050
4. [4]
  Xinpeng LIU , Liuyang ZHAO , Hongyi LI , Yatu CHEN , Aimin WU , Aikui LI , Hao HUANG . Ga₂O₃ coated modification and electrochemical performance of Li_1.2Mn_0.54Ni_0.13Co_0.13O₂ cathode material. Chinese Journal of Inorganic Chemistry, 2024, 40(6): 1105-1113. doi: 10.11862/CJIC.20230488
5. [5]
  Yuting ZHANG , Zunyi LIU , Ning LI , Dongqiang ZHANG , Shiling ZHAO , Yu ZHAO . Nickel vanadate anode material with high specific surface area through improved co-precipitation method: Preparation and electrochemical properties. Chinese Journal of Inorganic Chemistry, 2024, 40(11): 2163-2174. doi: 10.11862/CJIC.20240204
6. [6]
  Jiahong ZHENG , Jiajun SHEN , Xin BAI . Preparation and electrochemical properties of nickel foam loaded NiMoO₄/NiMoS₄ composites. Chinese Journal of Inorganic Chemistry, 2024, 40(3): 581-590. doi: 10.11862/CJIC.20230253
7. [7]
  Zhuo Wang , Xue Bai , Kexin Zhang , Hongzhi Wang , Jiabao Dong , Yuan Gao , Bin Zhao . MOF模板法合成氮掺杂碳材料用于增强电化学钠离子储存和去除. Acta Physico-Chimica Sinica, 2025, 41(3): 2405002-. doi: 10.3866/PKU.WHXB202405002
8. [8]
  Qi Li , Pingan Li , Zetong Liu , Jiahui Zhang , Hao Zhang , Weilai Yu , Xianluo Hu . Fabricating Micro/Nanostructured Separators and Electrode Materials by Coaxial Electrospinning for Lithium-Ion Batteries: From Fundamentals to Applications. Acta Physico-Chimica Sinica, 2024, 40(10): 2311030-. doi: 10.3866/PKU.WHXB202311030
9. [9]
  Yuyao Wang , Zhitao Cao , Zeyu Du , Xinxin Cao , Shuquan Liang . Research Progress of Iron-based Polyanionic Cathode Materials for Sodium-Ion Batteries. Acta Physico-Chimica Sinica, 2025, 41(4): 100035-. doi: 10.3866/PKU.WHXB202406014
10. [10]
  Xueyu Lin , Ruiqi Wang , Wujie Dong , Fuqiang Huang . 高性能双金属氧化物负极的理性设计及储锂特性. Acta Physico-Chimica Sinica, 2025, 41(3): 2311005-. doi: 10.3866/PKU.WHXB202311005
11. [11]
  Xiangyu CAO , Jiaying ZHANG , Yun FENG , Linkun SHEN , Xiuling ZHANG , Juanzhi YAN . Synthesis and electrochemical properties of bimetallic-doped porous carbon cathode material. Chinese Journal of Inorganic Chemistry, 2025, 41(3): 509-520. doi: 10.11862/CJIC.20240270
12. [12]
  Zhihuan XU , Qing KANG , Yuzhen LONG , Qian YUAN , Cidong LIU , Xin LI , Genghuai TANG , Yuqing LIAO . Effect of graphene oxide concentration on the electrochemical properties of reduced graphene oxide/ZnS. Chinese Journal of Inorganic Chemistry, 2024, 40(7): 1329-1336. doi: 10.11862/CJIC.20230447
13. [13]
  Xiaofeng Zhu , Bingbing Xiao , Jiaxin Su , Shuai Wang , Qingran Zhang , Jun Wang . Transition Metal Oxides/Chalcogenides for Electrochemical Oxygen Reduction into Hydrogen Peroxides. Acta Physico-Chimica Sinica, 2024, 40(12): 2407005-. doi: 10.3866/PKU.WHXB202407005
14. [14]
  Zhongyan Cao , Youzhi Xu , Menghua Li , Xiao Xiao , Xianqiang Kong , Deyun Qian . Electrochemically Driven Denitrative Borylation and Fluorosulfonylation of Nitroarenes. University Chemistry, 2025, 40(4): 277-281. doi: 10.12461/PKU.DXHX202407017
15. [15]
  Lina Guo , Ruizhe Li , Chuang Sun , Xiaoli Luo , Yiqiu Shi , Hong Yuan , Shuxin Ouyang , Tierui Zhang . 层状双金属氢氧化物的层间阴离子对衍生的Ni-Al₂O₃催化剂光热催化CO₂甲烷化反应的影响. Acta Physico-Chimica Sinica, 2025, 41(1): 2309002-. doi: 10.3866/PKU.WHXB202309002
16. [16]
  Yaping ZHANG , Tongchen WU , Yun ZHENG , Bizhou LIN . Z-scheme heterojunction β-Bi₂O₃ pillared CoAl layered double hydroxide nanohybrid: Fabrication and photocatalytic degradation property. Chinese Journal of Inorganic Chemistry, 2025, 41(3): 531-539. doi: 10.11862/CJIC.20240256
17. [17]
  Qianwen Han , Tenglong Zhu , Qiuqiu Lü , Mahong Yu , Qin Zhong . 氢电极支撑可逆固体氧化物电池性能及电化学不对称性优化. Acta Physico-Chimica Sinica, 2025, 41(1): 2309037-. doi: 10.3866/PKU.WHXB202309037
18. [18]
  Tiantian MA , Sumei LI , Chengyu ZHANG , Lu XU , Yiyan BAI , Yunlong FU , Wenjuan JI , Haiying YANG . Methyl-functionalized Cd-based metal-organic framework for highly sensitive electrochemical sensing of dopamine. Chinese Journal of Inorganic Chemistry, 2024, 40(4): 725-735. doi: 10.11862/CJIC.20230351
19. [19]
  Caixia Lin , Zhaojiang Shi , Yi Yu , Jianfeng Yan , Keyin Ye , Yaofeng Yuan . Ideological and Political Design for the Electrochemical Synthesis of Benzoxathiazine Dioxide Experiment. University Chemistry, 2024, 39(2): 61-66. doi: 10.3866/PKU.DXHX202309005
20. [20]
  Endong YANG , Haoze TIAN , Ke ZHANG , Yongbing LOU . Efficient oxygen evolution reaction of CuCo₂O₄/NiFe-layered bimetallic hydroxide core-shell nanoflower sphere arrays. Chinese Journal of Inorganic Chemistry, 2024, 40(5): 930-940. doi: 10.11862/CJIC.20230369

Get Citation

PDF

XML

Metrics

PDF Downloads(9)
Abstract views(1179)
HTML views(386)

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

Preparation and Electrochemical Performance of Nanoporous Bimetallic Oxide NiCo2O4

Metrics

通讯作者: 陈斌, bchen63@163.com

Preparation and Electrochemical Performance of Nanoporous Bimetallic Oxide NiCo₂O₄