Citation:
Sher Bahadar Khan, Kalsoom Akhtar, Jongchul Seo, Haksoo Han, Malik Abdul Rub. EFFECT OF NANO-FILLER DISPERSION ON THE THERMAL, MECHANICAL AND WATER SORPTION PROPERTIES OF GREEN ENVIRONMENTAL POLYMER[J]. Chinese Journal of Polymer Science,
2012, 30(5): 735-743.
doi:
10.1007/s10118-012-1168-5
EFFECT OF NANO-FILLER DISPERSION ON THE THERMAL, MECHANICAL AND WATER SORPTION PROPERTIES OF GREEN ENVIRONMENTAL POLYMER
English
EFFECT OF NANO-FILLER DISPERSION ON THE THERMAL, MECHANICAL AND WATER SORPTION PROPERTIES OF GREEN ENVIRONMENTAL POLYMER
Abstract:
Partially exfoliated nanocomposite (2) has been synthesized by intercalation of poly(propylene carbonate) (PPC) into commercial clay, Cloisite 20B (PPC/C-20B). Nanocomposite 2 was characterized phiso-chemically and exhibited high thermal, mechanical and anti-water sorption properties as compared to PPC and intercalated nanocomposite (1) of PPC/C-20B having same amount of clay. TGA results revealed that the thermal decomposition temperature (Td, 50%) of 2 increased significantly, being 40 K and 17 K higher than that of pure PPC and 1, respectively, while DSC measurements indicated that the nano-filler dispersion of 2 increased the glass transition temperature from 21℃ to 31℃. Accordingly, 2 showed high elastic modulus, hardness and anti-water absorption capacity. These thermal, mechanical and anti-water absorption improvements are of great importance for the application of PPC as packaging and biomaterials.
-
Key words:
- Poly(propylene carbonate)
-
-
-
[1]
-
[1]
-