APPLICATION OF WAXD AND SAXS TO STRUCTURAL ANALYSIS OF PA1010+BMI
摘要:
WAXD and SAXS for PA1010+BMI system have been measured.The results obtained with the help of Ruland and 1D EDCF,showed that Wc,x,the long period L and the thickness of the crystal lamellae do decreased with BMI content at PA10101+BMI system.Comparing both experimental and calculated density ρc values indicated that the values were of better conformity.Adding BMI into PA1010 caused an increase in distortion.The results from SAXS analysis have also led to the conclusion that a crystal-amorphous interphase could exist in lamellae of semicrystalline polymers and a three-phase model instead of traditional two-phase model should be used.
English
APPLICATION OF WAXD AND SAXS TO STRUCTURAL ANALYSIS OF PA1010+BMI
Abstract:
WAXD and SAXS for PA1010+BMI system have been measured.The results obtained with the help of Ruland and 1D EDCF,showed that Wc,x,the long period L and the thickness of the crystal lamellae do decreased with BMI content at PA10101+BMI system.Comparing both experimental and calculated density ρc values indicated that the values were of better conformity.Adding BMI into PA1010 caused an increase in distortion.The results from SAXS analysis have also led to the conclusion that a crystal-amorphous interphase could exist in lamellae of semicrystalline polymers and a three-phase model instead of traditional two-phase model should be used.