Citation: Deng Qing-Zhou, Chen De-Min, Yang Ke, Chen Lian, Li Bin-Hui, Zheng Sui-Sheng, Liu Shi, Tong Min, Li Yi-Yi. Modification of a Rapidly Solidifide AB2 Type Hydrogen Storage Alloy by Ball-milling[J]. Acta Physico-Chimica Sinica, 1999, 15(05): 420-425. doi: 10.3866/PKU.WHXB19990507
一种快速凝固AB2型储氢合金的球磨改性
通过熔纺（melt-spinning）法制备了Zr0.9Ti0.1（Ni0.57V0.1Mn0.28C0.05）2.1合金，并与Co3Mo混合球磨以改善其动力学性能. 结果发现，经过球磨，储氢合金与作为催化剂的Co3Mo接触更加紧密，电化学容量和活化性能得到明显改善交流. 阻抗测试表明，球磨大大改善了合金的表面活性．但长时间的球磨可使合金进一步非晶化，导致容量及活性的下降．实验结果还表明，将快速凝固合金与具有电催化作用的Co3Mo球磨得到的电极材料，其活性要高于合金与只作为导体的铜粉进行球磨或在无添加剂条件下进行球磨得到的电极材料．
English
Modification of a Rapidly Solidifide AB2 Type Hydrogen Storage Alloy by Ball-milling
Zr0. 9Ti0. 1 (Ni0.57V0.1Mn0. 28Co0. 05 )2.1 alloy was prepared by melt-spinning and ball-milled with Co3Mo additive to improve its kinetic characteristics. It was shown that after 2 h milling the alloy exhibited a much improved activation performance as well as electrochemical capacity. Electrochemical impedance experiments also showed that ball-milling of the alloy with Co3Mo could improve the surface activity to a great extent. This can be attributed to the catalytic effect of Co3Mo, which had a much closer contact with the alloy powder after ball-milling, on hydrogen oxidation. However, long time milling could decrease the capacity gradually due to the further amorphization of the alloy. The experimental results also showed that the alloy ball-milled with electrochemically catalytic material such as Co3Mo exhibited a better activity than those milled without any additives or with a metal powder such as Cu acting only as a conductor.
扫一扫看文章
计量
- PDF下载量: 2618
- 文章访问数: 3345
- HTML全文浏览量: 18
下载: