Spectral Property and Thermal Quenching Behavior of Tb<sup>3+</sup>-Doped YAG: Ce Phosphor

Citation: GUO Wang, SHI Hong-Ling, HUANG Ji-Quan, DENG Zhong-Hua, YUAN Xuan-Yi, CAO Yong-Ge. Spectral Property and Thermal Quenching Behavior of Tb³⁺-Doped YAG: Ce Phosphor[J]. Chinese Journal of Structural Chemistry, 2016, 35(2): 326-334. doi: 10.14102/j.cnki.0254-5861.2011-0871 shu

Spectral Property and Thermal Quenching Behavior of Tb³⁺-Doped YAG: Ce Phosphor

1.
a Beijing Key Laboratory of Opto-electronic Functional Materials & Micro-nano Devices, Renmin University of China, Beijing 100872, China;
2.
b Key Lab of Optoelectronic Materials Chemistry and Physics, Fujian Institute of Research on the Structure of Matter, Chinese Academy of Sciences, Fuzhou 350002, China
基金项目:
This work was supported by the National Natural Science Foundation of China (51272282, 51302311) (51272282, 51302311)

Technology (Z13111000280000) (Z13111000280000)

the Education Commission of Beijing (2011010329) (2011010329)

摘要: A series of YAG:Ce, Tb phosphors were synthesized by vacuum sintering method. Moreover, their spectral properties, thermal quenching behaviors and color rendering properties were investigated systematically. The photoluminescence emission spectra of YAG:Ce, Tb show a great red shift compared with that of YAG:Ce. Direct energy transfer from Tb³⁺ to Ce³⁺ ions is verified based on the analysis of different photoluminescence spectra. The quenching temperature for Tb³⁺-doped YAG:Ce phosphors is about 490 K. The thermal activation energy is estimated to be 0.18 and 0.291 eV for Tb³⁺-doped YAG:Ce and YAG:Ce phosphors, respectively. The smaller activation energy for Tb³⁺-doped YAG:Ce means a more rapid nonradiative transition from 5d to 4f state, thus resulting in the lower quenching temperature. In addition, white LEDs with improved color rendering properties are achieved by using modified YAG:Ce, Tb phosphors.

关键词:

English

Spectral Property and Thermal Quenching Behavior of Tb³⁺-Doped YAG: Ce Phosphor

1.
a Beijing Key Laboratory of Opto-electronic Functional Materials & Micro-nano Devices, Renmin University of China, Beijing 100872, China;
2.
b Key Lab of Optoelectronic Materials Chemistry and Physics, Fujian Institute of Research on the Structure of Matter, Chinese Academy of Sciences, Fuzhou 350002, China
Received Date: 29 June 2015
Fund Project:

Abstract: A series of YAG:Ce, Tb phosphors were synthesized by vacuum sintering method. Moreover, their spectral properties, thermal quenching behaviors and color rendering properties were investigated systematically. The photoluminescence emission spectra of YAG:Ce, Tb show a great red shift compared with that of YAG:Ce. Direct energy transfer from Tb³⁺ to Ce³⁺ ions is verified based on the analysis of different photoluminescence spectra. The quenching temperature for Tb³⁺-doped YAG:Ce phosphors is about 490 K. The thermal activation energy is estimated to be 0.18 and 0.291 eV for Tb³⁺-doped YAG:Ce and YAG:Ce phosphors, respectively. The smaller activation energy for Tb³⁺-doped YAG:Ce means a more rapid nonradiative transition from 5d to 4f state, thus resulting in the lower quenching temperature. In addition, white LEDs with improved color rendering properties are achieved by using modified YAG:Ce, Tb phosphors.

Key words:

1. [1]
  (1) Blasse, G.; Grabmaier, B. C. Luminescent Materials. Springer, Berlin 1994.(1) Blasse, G.; Grabmaier, B. C. Luminescent Materials. Springer, Berlin 1994.
2. [2]
  (2) Gan, L.; Mao, Z. Y.; Xu, F. F.; Zhu, Y. C.; Liu, X. J. Molten salt synthesis of YAG:Ce³⁺ phosphors from oxide raw materials. Ceram. Int. 2014, 40, 5067-5071.(2) Gan, L.; Mao, Z. Y.; Xu, F. F.; Zhu, Y. C.; Liu, X. J. Molten salt synthesis of YAG:Ce³⁺ phosphors from oxide raw materials. Ceram. Int. 2014, 40, 5067-5071.
3. [3]
  (3) Nakamua, S.; Fasol, G. The blue Laser Diode. Springer, Berlin 1996.(3) Nakamua, S.; Fasol, G. The blue Laser Diode. Springer, Berlin 1996.
4. [4]
  (4) Schubert, E. F.; Kim, J. K. Solid-state light sources getting smart. Science 2005, 308, 1274-1278.(4) Schubert, E. F.; Kim, J. K. Solid-state light sources getting smart. Science 2005, 308, 1274-1278.
5. [5]
  (5) You, F. T.; Bos, A. J. J.; Shi, Q. F.; Huang, S. H.; Dorenbos, P. Phys. Rev. B. Thermoluminescence investigation of donor (Ce³⁺, Pr³⁺, Tb³⁺) acceptor (Eu³⁺, Yb³⁺) pairs in Y₃Al₅O₁₂. 2012, 85, 115101-1-6.(5) You, F. T.; Bos, A. J. J.; Shi, Q. F.; Huang, S. H.; Dorenbos, P. Phys. Rev. B. Thermoluminescence investigation of donor (Ce³⁺, Pr³⁺, Tb³⁺) acceptor (Eu³⁺, Yb³⁺) pairs in Y₃Al₅O₁₂. 2012, 85, 115101-1-6.
6. [6]
  (6) Pan, Y. X.; Wu, M. M.; Su, Q. Tailored photoluminescence of YAG:Ce phosphor through various methods. J. Phys. Chem. Solids 2004, 65, 845-850.(6) Pan, Y. X.; Wu, M. M.; Su, Q. Tailored photoluminescence of YAG:Ce phosphor through various methods. J. Phys. Chem. Solids 2004, 65, 845-850.
7. [7]
  (7) Jang, H. S.; Im, W. B.; Lee, D. C.; Jeon, D. Y.; Kim, S. S. Enhancement of red spectral emission intensity of Y₃Al₅O₁₂:Ce³⁺ phosphor via Pr co-doping and Tb substitution for the application to white LEDs. J. Lumin. 2007, 126, 371-377.(7) Jang, H. S.; Im, W. B.; Lee, D. C.; Jeon, D. Y.; Kim, S. S. Enhancement of red spectral emission intensity of Y₃Al₅O₁₂:Ce³⁺ phosphor via Pr co-doping and Tb substitution for the application to white LEDs. J. Lumin. 2007, 126, 371-377.
8. [8]
  (8) Mukherjee, S.; Sudarsan, V.; Vatsa, R. K.; Tyagi, A. K. Luminescence studies on lanthanide ions (Eu³⁺, Dy³⁺ and Tb³⁺) doped YAG:Ce nano-phosphors. J. Lumin. 2009, 129, 69-72.(8) Mukherjee, S.; Sudarsan, V.; Vatsa, R. K.; Tyagi, A. K. Luminescence studies on lanthanide ions (Eu³⁺, Dy³⁺ and Tb³⁺) doped YAG:Ce nano-phosphors. J. Lumin. 2009, 129, 69-72.
9. [9]
  (9) Jung, K. Y.; Lee, H. W. Enhanced luminescent properties of Y₃Al₅O₁₂:Tb³⁺,Ce³⁺ phosphor prepared by spray pyrolysis. J. Lumin. 2007, 126, 469-474.(9) Jung, K. Y.; Lee, H. W. Enhanced luminescent properties of Y₃Al₅O₁₂:Tb³⁺,Ce³⁺ phosphor prepared by spray pyrolysis. J. Lumin. 2007, 126, 469-474.
10. [10]
  (10) Blasse, G.; Bril, A. Investigation of some Ce³⁺-activated phosphors. J. Chem. Phys. 1967, 47, 5139-5145.(10) Blasse, G.; Bril, A. Investigation of some Ce³⁺-activated phosphors. J. Chem. Phys. 1967, 47, 5139-5145.
11. [11]
  (11) Jacobs, R. R.; Krupke, W. F.; Weber, M. J. Measurement of excited-state-absorption loss for Ce³⁺ in Y₃Al₅O₁₂and implications for tunable 5d → 4f rare-earth lasers. Appl. Phys. Lett. 1978, 33, 410-412.(11) Jacobs, R. R.; Krupke, W. F.; Weber, M. J. Measurement of excited-state-absorption loss for Ce³⁺ in Y₃Al₅O₁₂and implications for tunable 5d → 4f rare-earth lasers. Appl. Phys. Lett. 1978, 33, 410-412.
12. [12]
  (12) Rack, P. D.; Holloway, P. H. The structure, device physics, and material properties of thin film electroluminescent displays. Mater. Sci. Eng. R 1998, 171-219.(12) Rack, P. D.; Holloway, P. H. The structure, device physics, and material properties of thin film electroluminescent displays. Mater. Sci. Eng. R 1998, 171-219.
13. [13]
  (13) Rodręguez-Rojas, R. A.; De la Rosa Cruz, E.; Dıaz-Torres, L. A.; Salas, P.; Melendrez, R.; barboza-Flores, M.; Meneses Nava, M. A.; Barbosa-Garcıa, O. Preparation, photo- and thermo-luminescence characterization of Tb³⁺ and Ce³⁺doped nanocrystalline Y₃Al₅O₁₂ exposed to UV-irradiation. Opt. Mater. 2004, 25, 285-293.(13) Rodręguez-Rojas, R. A.; De la Rosa Cruz, E.; Dıaz-Torres, L. A.; Salas, P.; Melendrez, R.; barboza-Flores, M.; Meneses Nava, M. A.; Barbosa-Garcıa, O. Preparation, photo- and thermo-luminescence characterization of Tb³⁺ and Ce³⁺doped nanocrystalline Y₃Al₅O₁₂ exposed to UV-irradiation. Opt. Mater. 2004, 25, 285-293.
14. [14]
  (14) Zhou, Y. H.; Lin, J.; Yu, M.; Wang, S. B.; Zhang, H. J. Synthesis-dependent luminescence properties of Y₃Al₅O₁₂:Re³⁺ (Re = Ce, Sm, Tb) phosphors. Mater. Lett. 2002, 56, 628-636.(14) Zhou, Y. H.; Lin, J.; Yu, M.; Wang, S. B.; Zhang, H. J. Synthesis-dependent luminescence properties of Y₃Al₅O₁₂:Re³⁺ (Re = Ce, Sm, Tb) phosphors. Mater. Lett. 2002, 56, 628-636.
15. [15]
  (15) Lin, Y. S.; Liu, R. S.; Cheng, B. M. Investigation of the luminescent properties of Tb^{3 +}-substituted YAG:Ce, Gd phosphors general topics. J. Electrochem. Soc. 2005, 152, 41-45.(15) Lin, Y. S.; Liu, R. S.; Cheng, B. M. Investigation of the luminescent properties of Tb^{3 +}-substituted YAG:Ce, Gd phosphors general topics. J. Electrochem. Soc. 2005, 152, 41-45.
16. [16]
  (16) Yang, H. S.; Kim, Y. S. Energy transfer-based spectral properties of Tb-, Pr-, or Sm-codoped YAG:Ce nanocrystalline phosphors. J. Lumin. 2008, 128, 1570-1576.(16) Yang, H. S.; Kim, Y. S. Energy transfer-based spectral properties of Tb-, Pr-, or Sm-codoped YAG:Ce nanocrystalline phosphors. J. Lumin. 2008, 128, 1570-1576.
17. [17]
  (17) Shmulovich, J.; Berkstresser, G. W.; Brasen, D. Tb³⁺ → Ce³⁺ energy transfer in Tb³⁺:Ce³⁺:YAG single crystalsa. J. Chem. Phys. 1985, 82, 3078-3082.(17) Shmulovich, J.; Berkstresser, G. W.; Brasen, D. Tb³⁺ → Ce³⁺ energy transfer in Tb³⁺:Ce³⁺:YAG single crystalsa. J. Chem. Phys. 1985, 82, 3078-3082.
18. [18]
  (18) Liu, X. R.; Wang, X. J.; Wang, Z. K. Selectively excited emission and Tb³⁺→ Ce³⁺ energy transfer in yttrium aluminum garnet. Phys. Rev. B 1989, 39, 10633-10639.(18) Liu, X. R.; Wang, X. J.; Wang, Z. K. Selectively excited emission and Tb³⁺→ Ce³⁺ energy transfer in yttrium aluminum garnet. Phys. Rev. B 1989, 39, 10633-10639.
19. [19]
  (19) Wong, C. M.; Rotman, S. R.; Warde, C. Optical studies of cerium doped yttrium aluminum garnet single crystals. Appl. Phys. Lett. 1984, 44, 1038-1040.(19) Wong, C. M.; Rotman, S. R.; Warde, C. Optical studies of cerium doped yttrium aluminum garnet single crystals. Appl. Phys. Lett. 1984, 44, 1038-1040.
20. [20]
  (20) Kelledouk, F.; Belt, T.; van den. Blasse, G. On the luminescence of bismuth, cerium, and chromium and yttrium aluminium borate. J. Chem. Phys. 1982, 76, 1194-1201.(20) Kelledouk, F.; Belt, T.; van den. Blasse, G. On the luminescence of bismuth, cerium, and chromium and yttrium aluminium borate. J. Chem. Phys. 1982, 76, 1194-1201.
21. [21]
  (21) Jia, D.; Meltzer, R. S.; Yen, W. M.; Jia, W.; Wang, X. Green phosphorescence of CaAl₂O₄: Tb³⁺, Ce³⁺ through persistence energy transfer. Appl. Phys. Lett. 2002, 90, 1535-1537.(21) Jia, D.; Meltzer, R. S.; Yen, W. M.; Jia, W.; Wang, X. Green phosphorescence of CaAl₂O₄: Tb³⁺, Ce³⁺ through persistence energy transfer. Appl. Phys. Lett. 2002, 90, 1535-1537.
22. [22]
  (22) You, H.; Hong, G.; Wu, X. A new type of highly efficient luminescent materials the system Al₂O₃-B₂O₃ containing Ce³⁺ and Tb³⁺ ions. Chem. Mater. 2003, 15, 2000-2004.(22) You, H.; Hong, G.; Wu, X. A new type of highly efficient luminescent materials the system Al₂O₃-B₂O₃ containing Ce³⁺ and Tb³⁺ ions. Chem. Mater. 2003, 15, 2000-2004.
23. [23]
  (23) Riwotzki, K.; Meyssamy, H.; Schnablegger, H.; Kornowski, A.; Haase, M. Liquid-phase synthesis of colloids and redispersible powders of strongly luminescing LaPO₄:Ce,Tb nanocrystals. Angew. Chem. Int. Ed. 2001, 40, 573-576.(23) Riwotzki, K.; Meyssamy, H.; Schnablegger, H.; Kornowski, A.; Haase, M. Liquid-phase synthesis of colloids and redispersible powders of strongly luminescing LaPO₄:Ce,Tb nanocrystals. Angew. Chem. Int. Ed. 2001, 40, 573-576.
24. [24]
  (24) Zhu, X. J.; Zhou, K. N.; Li, Y. M.; Wang, Z. L.; Feng, Q. C. Luminescent properties and energy transfer of Y₃Al₅O₁₂:Ce³⁺, Ln³⁺ (Ln = Tb, Pr) prepared by polymer-assisted sol-gel method. J. Lumin. 2012, 132, 3004-3009.(24) Zhu, X. J.; Zhou, K. N.; Li, Y. M.; Wang, Z. L.; Feng, Q. C. Luminescent properties and energy transfer of Y₃Al₅O₁₂:Ce³⁺, Ln³⁺ (Ln = Tb, Pr) prepared by polymer-assisted sol-gel method. J. Lumin. 2012, 132, 3004-3009.
25. [25]
  (25) Bachmann, V.; Ronda, C.; Meijerink, A. Temperature quenching of yellow Ce³⁺ luminescence in YAG:Ce. Chem. Mater. 2009, 21, 2077-2084.(25) Bachmann, V.; Ronda, C.; Meijerink, A. Temperature quenching of yellow Ce³⁺ luminescence in YAG:Ce. Chem. Mater. 2009, 21, 2077-2084.
26. [26]
  (26) Bhushan, S.; Chukichev, M. V. Temperature dependent studies of cathodoluminescence of green band of ZnO crystals. J. Mater. Sci. Lett. 1988, 7, 319-321.(26) Bhushan, S.; Chukichev, M. V. Temperature dependent studies of cathodoluminescence of green band of ZnO crystals. J. Mater. Sci. Lett. 1988, 7, 319-321.
27. [27]
  (27) Chen, Y.; Liu, B.; Shi, C.; Ren, G.; Zimmerer, G. The temperature effect of Lu₂SiO₅:Ce³⁺ luminescence. Nucl. Instrum. Meth. Phys. Res. A 2005, 537, 31-35.(27) Chen, Y.; Liu, B.; Shi, C.; Ren, G.; Zimmerer, G. The temperature effect of Lu₂SiO₅:Ce³⁺ luminescence. Nucl. Instrum. Meth. Phys. Res. A 2005, 537, 31-35.
28. [28]
  (28) Chiang, C. C.; Tsai, M. S.; Hon, M. H. Luminescent properties of cerium-activated garnet series phosphor: structure and temperature effects. J. Electrochem. Soc. 2008, 155, B517-B520.(28) Chiang, C. C.; Tsai, M. S.; Hon, M. H. Luminescent properties of cerium-activated garnet series phosphor: structure and temperature effects. J. Electrochem. Soc. 2008, 155, B517-B520.
29. [29]
  (29) Ueda, J.; Tanabe, S.; Nakanishi, T. Analysis of Ce³⁺ luminescence quenching in solid solutions between Y₃Al₅O₁₂ and Y₃Ga₅O₁₂ by temperature dependence of photoconductivity measurement. J. Appl. Phys. 2011, 110, 053102-1-6.(29) Ueda, J.; Tanabe, S.; Nakanishi, T. Analysis of Ce³⁺ luminescence quenching in solid solutions between Y₃Al₅O₁₂ and Y₃Ga₅O₁₂ by temperature dependence of photoconductivity measurement. J. Appl. Phys. 2011, 110, 053102-1-6.
30. [30]
  (30) Raukas, M.; Basun, S. A.; Schaik, W. V.; Yen, W.; Happek, M. U. Luminescence efficiency of cerium doped insulators: The role of electron transfer processes. Appl. Phys. Lett. 1996, 69, 3300-3302.(30) Raukas, M.; Basun, S. A.; Schaik, W. V.; Yen, W.; Happek, M. U. Luminescence efficiency of cerium doped insulators: The role of electron transfer processes. Appl. Phys. Lett. 1996, 69, 3300-3302.
31. [31]
  (31) Hamilton, D. S.; Gayen, S. K.; Pogatshnik, G. J.; Ghen, R. D.; Miniscalco, W. J. Optical-absorption and photoionization measurements from the excited states of Ce³⁺:Y₃Al₅O₁₂. Phys. Rev. B 1989, 39, 8807-8815.(31) Hamilton, D. S.; Gayen, S. K.; Pogatshnik, G. J.; Ghen, R. D.; Miniscalco, W. J. Optical-absorption and photoionization measurements from the excited states of Ce³⁺:Y₃Al₅O₁₂. Phys. Rev. B 1989, 39, 8807-8815.
32. [32]
  (32) Ivanovskikh, K. V.; Ogieglo, J. M.; Zych, A.; Ronda, C. R.; Meijerink, A. J. Solid. State. Sci. Technol. 2013, 2, R3148-R3152.(32) Ivanovskikh, K. V.; Ogieglo, J. M.; Zych, A.; Ronda, C. R.; Meijerink, A. J. Solid. State. Sci. Technol. 2013, 2, R3148-R3152.
33. [33]
  (33) Fang, Y. C.; Chu, S. Y.; Kao, P. C.; Chuang, Y. M.; Zeng, Z. L. Energy transfer and thermal quenching behaviors of CaLa₂ (MoO₄)₄: Sm^{3 +}, Eu^{3 +} red phosphors. J. Electrochem. Soc. 2011, 158, J1-J5.(33) Fang, Y. C.; Chu, S. Y.; Kao, P. C.; Chuang, Y. M.; Zeng, Z. L. Energy transfer and thermal quenching behaviors of CaLa₂ (MoO₄)₄: Sm^{3 +}, Eu^{3 +} red phosphors. J. Electrochem. Soc. 2011, 158, J1-J5.
34. [34]
  (34) Han, T.; Cao, S.; Peng, L.; Zhu, D.; Zhao, C.; Tu, M.; Zhang, J. Chemical substitution effects of elements on photoluminescence properties of YAG:Ce phosphors using orthogonal experimental design. Opt. Mater. 2012, 34, 1618-1621.(34) Han, T.; Cao, S.; Peng, L.; Zhu, D.; Zhao, C.; Tu, M.; Zhang, J. Chemical substitution effects of elements on photoluminescence properties of YAG:Ce phosphors using orthogonal experimental design. Opt. Mater. 2012, 34, 1618-1621.
35. [35]
  (35) Yadav, P. J.; Joshi, C. P.; Moharil, S. V. Two phosphor converted white LED with improved CRI. J. Lumin. 2013, 136, 1-4.(35) Yadav, P. J.; Joshi, C. P.; Moharil, S. V. Two phosphor converted white LED with improved CRI. J. Lumin. 2013, 136, 1-4.
36. [36]
  (36) Chung, W.; Yu, H. J.; Park, S. H.; Chun, B. H.; Kim, S. H. YAG and CdSe/ZnSe nanoparticles hybrid phosphor for white LED with high color rendering index. Mater. Chem. Phys. 2011, 126, 162-166.(36) Chung, W.; Yu, H. J.; Park, S. H.; Chun, B. H.; Kim, S. H. YAG and CdSe/ZnSe nanoparticles hybrid phosphor for white LED with high color rendering index. Mater. Chem. Phys. 2011, 126, 162-166.

扫一扫看文章

计量

PDF下载量: 0
文章访问数: 2069
HTML全文浏览量: 53

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

Spectral Property and Thermal Quenching Behavior of Tb³⁺-Doped YAG: Ce Phosphor

English

Spectral Property and Thermal Quenching Behavior of Tb³⁺-Doped YAG: Ce Phosphor

CCS Chemistry：嵌段共聚物自组装成 “三明治”二维有机材料，实现纳米级压力传感功能

CCS Chemistry：颜徐州、鲍哲南：你的皮肤可能是一片SPMs

CCS Chemistry：工作高效不疲劳，只须让催化剂动起来

CCS Chemistry：静电组装导向聚合- 聚电解质纳米凝胶量化制备新策略

CCS Chemistry：金黄色葡萄球菌醛基脱氢酶是如何识别特异性底物的？

计量

通讯作者: 陈斌, bchen63@163.com

中国化学会秘书处

Spectral Property and Thermal Quenching Behavior of Tb3+-Doped YAG: Ce Phosphor

English

Spectral Property and Thermal Quenching Behavior of Tb3+-Doped YAG: Ce Phosphor

CCS Chemistry：嵌段共聚物自组装成 “三明治”二维有机材料，实现纳米级压力传感功能

CCS Chemistry：颜徐州、鲍哲南： 你的皮肤可能是一片SPMs

CCS Chemistry：工作高效不疲劳，只须让催化剂动起来

CCS Chemistry：静电组装导向聚合- 聚电解质纳米凝胶量化制备新策略

CCS Chemistry：金黄色葡萄球菌醛基脱氢酶是如何识别特异性底物的？

计量

文章相关

通讯作者: 陈斌, bchen63@163.com

中国化学会秘书处

Spectral Property and Thermal Quenching Behavior of Tb³⁺-Doped YAG: Ce Phosphor

Spectral Property and Thermal Quenching Behavior of Tb³⁺-Doped YAG: Ce Phosphor

CCS Chemistry：颜徐州、鲍哲南：你的皮肤可能是一片SPMs