Hierarchical Porous Polymer Beads Prepared by Polymerization-induced Phase Separation and Emulsion-template in a Microfluidic Device

Citation: Wei-cai Wang, Yan-xiong Pan, Kai Shi, Chao Peng, Xiang-ling Jia. Hierarchical Porous Polymer Beads Prepared by Polymerization-induced Phase Separation and Emulsion-template in a Microfluidic Device[J]. Chinese Journal of Polymer Science, 2014, 32(12): 1646-1654. doi: 10.1007/s10118-014-1547-1 shu

Hierarchical Porous Polymer Beads Prepared by Polymerization-induced Phase Separation and Emulsion-template in a Microfluidic Device

1.
1. State Key Laboratory of Polymer Physics and Chemistry, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun 130022, China
2.
2. University of Chinese Academy of Sciences, Changchun 130022, China
3.
4.
State Key Laboratory of Polymer Physics and Chemistry, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun 130022, China

摘要: Porous polymer beads (PPBs) containing hierarchical bimodal pore structure with gigapores and meso-macropores were prepared by polymerization-induced phase separation (PIPS) and emulsion-template technique in a glass capillary microfluidic device (GCMD). Fabrication procedure involved the preparation of water-in-oil emulsion by emulsifying aqueous solution into the monomer solution that contains porogen. The emulsion was added into the GCMD to fabricate the (water-in-oil)-in-water double emulsion droplets. The flow rate of the carrier continuous phase strongly influenced the formation mechanism and size of droplets. Formation mechanism transformed from dripping to jetting and size of droplets decreased from 550 m to 250 m with the increase in flow rate of the carrier continuous phase. The prepared droplets were initiated for polymerization by on-line UV-irradiation to form PPBs. The meso-macropores in these beads were generated by PIPS because of the presence of porogen and gigapores obtained from the emulsion-template. The pore morphology and pore size distribution of the PPBs were investigated extensively by scanning electron microscopy and mercury intrusion porosimetry (MIP). New pore morphology was formed at the edge of the beads different from traditional theory because of different osmolarities between the water phase of the emulsion and the carrier continuous phase. The morphology and proportion of bimodal pore structure can be tuned by changing the kind and amount of porogen.

关键词:

Porous polymer beads
/ Hierarchical
/ Polymerization-induced phase separation
/ Emulsion-template
/ Microfluidic device

English

Hierarchical Porous Polymer Beads Prepared by Polymerization-induced Phase Separation and Emulsion-template in a Microfluidic Device

1.
1. State Key Laboratory of Polymer Physics and Chemistry, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun 130022, China
2.
2. University of Chinese Academy of Sciences, Changchun 130022, China
3.
4.
State Key Laboratory of Polymer Physics and Chemistry, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun 130022, China
Received Date: 20 March 2014
Revised Date: 21 April 2014
Available Online: 05 December 2014

Abstract: Porous polymer beads (PPBs) containing hierarchical bimodal pore structure with gigapores and meso-macropores were prepared by polymerization-induced phase separation (PIPS) and emulsion-template technique in a glass capillary microfluidic device (GCMD). Fabrication procedure involved the preparation of water-in-oil emulsion by emulsifying aqueous solution into the monomer solution that contains porogen. The emulsion was added into the GCMD to fabricate the (water-in-oil)-in-water double emulsion droplets. The flow rate of the carrier continuous phase strongly influenced the formation mechanism and size of droplets. Formation mechanism transformed from dripping to jetting and size of droplets decreased from 550 m to 250 m with the increase in flow rate of the carrier continuous phase. The prepared droplets were initiated for polymerization by on-line UV-irradiation to form PPBs. The meso-macropores in these beads were generated by PIPS because of the presence of porogen and gigapores obtained from the emulsion-template. The pore morphology and pore size distribution of the PPBs were investigated extensively by scanning electron microscopy and mercury intrusion porosimetry (MIP). New pore morphology was formed at the edge of the beads different from traditional theory because of different osmolarities between the water phase of the emulsion and the carrier continuous phase. The morphology and proportion of bimodal pore structure can be tuned by changing the kind and amount of porogen.

Key words:

Porous polymer beads
/ Hierarchical
/ Polymerization-induced phase separation
/ Emulsion-template
/ Microfluidic device

1. [1]
  Smigol, V., Svec, F. and Frechet, J. M., Anal. Chem., 1994, 66(23): 4308
2. [2]
  Zhang, Y. and Riduan, S.N., Chem. Soc. Rev., 2012, 41(6): 2083
3. [3]
  Smigol, V., Svec, F. and Frechet, J.M., Macromolecules, 1993, 26(21): 5615
4. [4]
  Grzegorczyk, D.S. and Carta, G., Chem. Eng. Sci., 1996, 51(5): 807
5. [5]
  Galia, M., Svec, F. and Frechet, J.M., J. Polym. Sci. Part A: Polym. Chem., 1994, 32(11): 2169
6. [6]
  Christensen, B.E., Myhr, M.H., Aune, O., Hagen, S., Berge, A. and Ugelstad, J., Carbohydr. Polym., 1996, 29(3): 217
7. [7]
  Malik, D., Webb, C., Holdich, R., Ramsden, J.J., Warwick, G., Roche, I., Williams, D., Trochimczuk, A., Dale, J. and Hoenich, N., Sep. Purif. Technol., 2009, 66(3): 578
8. [8]
  Li, Y., Gao, F., Wei, W., Qu, J.B., Ma, G.H. and Zhou, W.Q., J. Mol. Catal. B: Enzym., 2010, 66(1): 182
9. [9]
  Skora, D., Svec, F. and Frchet, J.M., J. Chromatogr. A, 1999, 852(1): 297
10. [10]
  Petro, M., Svec, F., Gitsov, I. and Frchet, J.M., Anal. Chem., 1996, 68(2): 315
11. [11]
  Dubinsky, S., Petukhova, A., Gourevich, I. and Kumacheva, E., Chem. Commun., 2010, 46(15): 2578
12. [12]
  Svec, F. and Frechet, J.M., Science, 1996, 273(5272): 205
13. [13]
  Okay, O., Prog. Polym. Sci., 2000, 25(6): 711
14. [14]
  Menner, A., Haibach, K., Powell, R. and Bismarck, A., Polymer, 2006, 47(22): 7628
15. [15]
  Wu, R., Menner, A. and Bismarck, A., J. Polym. Sci. Part A: Polym. Chem., 2010, 48(9): 1979
16. [16]
  Cameron, N. and Sherrington, D., in Biopolymers Liquid Crystalline Polymers Phase Emulsion, Springer, 1996, p. 163
17. [17]
  Parlett, C.M., Wilson, K. and Lee, A.F., Chem. Soc. Rev., 2013, 42(9): 3876
18. [18]
  Sai, H., Tan, K.W., Hur, K., Asenath-Smith, E., Hovden, R., Jiang, Y., Riccio, M., Muller, D.A., Elser, V. and Estroff, L.A., Science, 2013, 341(6145): 530
19. [19]
  Schofield, W., Bain, C. and Badyal, J., Chem. Mater., 2012, 24(9): 1645
20. [20]
  Ning, Y., Yang, Y., Wang, C., Ngai, T. and Tong, Z., Chem. Commun., 2013, 49(78): 8761
21. [21]
  Utada, A.S., Lorenceau, E., Link, D.R., Kaplan, P.D., Stone, H.A. and Weitz, D.A., Science, 2005, 308(5721): 537
22. [22]
  Utada, A.S., Fernandez-Nieves, A., Stone, H.A. and Weitz, D.A., Phys. Rev. Lett., 2007, 99(9): 094502
23. [23]
  Dubinsky, S., Park, J.I., Gourevich, I., Chan, C., Deetz, M. and Kumacheva, E., Macromolecules, 2009, 42(6): 1990
24. [24]
  Gokmen, M.T., Van Camp, W., Colver, P.J., Bon, S.A.F. and Du Prez, F.E., Macromolecules, 2009, 42(23): 9289
25. [25]
  Giesche, H., Part. Part. Syst. Char., 2006, 23(1): 9

扫一扫看文章

计量

PDF下载量: 0
文章访问数: 2087
HTML全文浏览量: 71

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

Hierarchical Porous Polymer Beads Prepared by Polymerization-induced Phase Separation and Emulsion-template in a Microfluidic Device

English

Hierarchical Porous Polymer Beads Prepared by Polymerization-induced Phase Separation and Emulsion-template in a Microfluidic Device

CCS Chemistry：嵌段共聚物自组装成 “三明治”二维有机材料，实现纳米级压力传感功能

CCS Chemistry：颜徐州、鲍哲南：你的皮肤可能是一片SPMs

CCS Chemistry：工作高效不疲劳，只须让催化剂动起来

CCS Chemistry：静电组装导向聚合- 聚电解质纳米凝胶量化制备新策略

CCS Chemistry：金黄色葡萄球菌醛基脱氢酶是如何识别特异性底物的？

计量

通讯作者: 陈斌, bchen63@163.com

中国化学会秘书处

Hierarchical Porous Polymer Beads Prepared by Polymerization-induced Phase Separation and Emulsion-template in a Microfluidic Device

English

Hierarchical Porous Polymer Beads Prepared by Polymerization-induced Phase Separation and Emulsion-template in a Microfluidic Device

CCS Chemistry：嵌段共聚物自组装成 “三明治”二维有机材料，实现纳米级压力传感功能

CCS Chemistry：颜徐州、鲍哲南： 你的皮肤可能是一片SPMs

CCS Chemistry：工作高效不疲劳，只须让催化剂动起来

CCS Chemistry：静电组装导向聚合- 聚电解质纳米凝胶量化制备新策略

CCS Chemistry：金黄色葡萄球菌醛基脱氢酶是如何识别特异性底物的？

计量

文章相关

通讯作者: 陈斌, bchen63@163.com

中国化学会秘书处

CCS Chemistry：颜徐州、鲍哲南：你的皮肤可能是一片SPMs