THE CONDUCTIVITY BEHAVIOR OF A POLYMER GEL ELECTROLYTE
摘要:
A new kind of polymer gel electrolyte which is composed of polytriethylene glycol dimethacrylate(PTREGD),propylene carbonate(PC) and LiPF6 has been prepared by thermal polymerization.The conductivity was measured as a function of temperature,and it was found that the Arrhenius equation was held very well through out the salt concentration studied.Maximum room temperature conductivity of 4.95×10-4S/cm,as well as a minimum activation energy value of 18.90 kJ/mol were obtained at the same salt concentration of 0.22 mol/L.
English
THE CONDUCTIVITY BEHAVIOR OF A POLYMER GEL ELECTROLYTE
Abstract:
A new kind of polymer gel electrolyte which is composed of polytriethylene glycol dimethacrylate(PTREGD),propylene carbonate(PC) and LiPF6 has been prepared by thermal polymerization.The conductivity was measured as a function of temperature,and it was found that the Arrhenius equation was held very well through out the salt concentration studied.Maximum room temperature conductivity of 4.95×10-4S/cm,as well as a minimum activation energy value of 18.90 kJ/mol were obtained at the same salt concentration of 0.22 mol/L.