化学沉积Ni-P-Al2O3和Ni-P-SiC复合材料的微观组织与物理性能
English
Microstructure and Physical Property of Chemically Deposited NiPAl2O3 and NiP-SiC Composites
Abstract:
The title composites were obtained by chemical deposition method. It is found that the components are mechanically incorporated and the crystalization tendency of the composite coatings increases with increase of codeposited components and decrease of phosphorus content in alloy. Ni3P was observed in composite at higher aging temperatures.The composites have higher hardness and lower wear volume than the original alloy.
-
Key words:
- Ni-P alloy
- / SiC
- / Al2O3
- / chemical deposition
- / composite
- / physical property
- / microstructure
-
-