MULTIPLE MELTING AND CRYSTALLIZATION BEHAVIOR OF NYLON 1212
English
MULTIPLE MELTING AND CRYSTALLIZATION BEHAVIOR OF NYLON 1212
Abstract:
The wide-angle X-ray diffraction (WAXD) patterns of isothermally crystallized Nylon 1212 show that -form crystals form below 90℃ and the -form crystals can exist above 140℃. In the temperature range of 90140℃ the -form and -form crystals coexist. Variable-temperature WAXD exhibits that the nylon 1212 -form does not show crystal transition on heating, while -form isothermally crystallized at 160℃ exhibits Brill transition at a little higher than 180℃ on heating. The multiple melting behaviors of Nylon 1212 isothermally crystallized from melt come from a complex mechanism of different crystal structures, dual lamellar population and melting-recrystallization. In polarized optical microscope (POM) observations, Nylon 1212 isothermally crystallized at 175℃ shows the ringed banded spherulites. However, at temperatures below 160℃ the ringed banded image disappears, and cross-extinct spherulites are formed.
扫一扫看文章
计量
- PDF下载量: 0
- 文章访问数: 0
- HTML全文浏览量: 0
下载: